Delamination resistant multilayer metal/polymer composites
Assignee: Dow Chemical Co
•
Filing: 1978-12-15
•
Granted: 1980-12-23
•
Expires: 1998-12-15
Abstract
Abstract A multilayer, metal/organic polymer composite exhibiting excellent resistance to delamination after thermoforming is provided by metallizing a substrate layer of thermoplastic organic polymer such as polystyrene or polycarbonate film and bonding the exposed metal surface to a structural plastic with a soft adhesive layer. Subsequently, the multilayer composite or at least a portion thereof can be shaped into an article which may be structurally reinforced by casting an elastomeric or rigid foamed polymer such as polyurethane foam into a cavity defined by the composite. The multilayer composites are useful in the manufacture of reflective and decorative parts for automobiles and other vehicles of transportation, as well as high barrier packages for foods and electroconductive elements.
Inventors
- 👤 Henry J. Marton
- 👤 Virgil B. Kurfman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 07:59
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/04; B32B15/08; B32B7/00; B32B7/04; B32B7/06; B32B7/12; B32B2305/00; B32B2305/08; B32B2307/00; B32B2307/70; B32B2307/748; B32B2309/00; B32B2309/08; B32B2309/10; B32B2309/105; B32B2355/00; B32B2355/02; B32B2375/00; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/28; Y10T428/2804; Y10T428/2813; Y10T428/2817; Y10T428/2826; Y10T428/2852; Y10T428/2878; Y10T428/2883; Y10T428/2896; Y10T428/31504; Y10T428/31507; Y10T428/31551; Y10T428/31554; Y10T428/31605; Y10T428/31678; Y10T428/31681; Y10T428/31692; Y10T428/31696; Y10T428/31699
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
116 words
A metal/organic polymer composite comprising (1) a normally solid thermoplastic, substrate polymer layer; (2) a normally solid, metal layer having two major surfaces wherein the first of said surfaces is adhered to one surface of the substrate polymer layer, said metal layer having a thickness sufficient to form a substantially continuous layer and less than that which inherently delaminates from the substrate polymer layer; and (3) a layer of a soft adhesive polymer adhered to the second surface of the metal layer, said soft adhesive polymer having toughness and modulus such that upon adhering the composite to a rigid substrate the tendency of the metal layer to separate from the substrate polymer layer is measurably reduced.
Claim 2
Dependent Claim
116 words
A metal/organic polymer composite comprising (1) a normally solid thermoplastic, substrate polymer layer; (2) a normally solid, metal layer having two major surfaces wherein the first of said surfaces is adhered to one surface of the substrate polymer layer, said metal layer having a thickness sufficient to form a substantially continuous layer and less than that which inherently delaminates from the substrate polymer layer; and (3) a layer of a soft adhesive polymer adhered to the second surface of the metal layer, said soft adhesive polymer having toughness and modulus such that upon adhering the composite to a rigid substrate the tendency of the metal layer to separate from the substrate polymer layer is measurably reduced.
Claim 3
Dependent Claim
32 words
The composite of claim 1 wherein the soft adhesive polymer has a Young's Modulus less than 1500 psi, an elongation greater than 50 percent and a tensile strength greater than 10 psi.
Claim 4
Dependent Claim
83 words
The composite of claim 2 wherein the metal is indium or an alloy of at least two of cadmium, indium, tin, antimony, lead, bismuth, magnesium, aluminum, zinc, copper or silver; the substrate polymer is polycarbonate, thermoplastic polyester, acrylic resin, monovinylidene aromatic polymer, a polymer of vinyl chloride or vinylidene chloride, or acetal resin; and the soft adhesive polymer is a diene rubber, a block copolymer having (1) polystyrene blocks and (2) blocks of polybutadiene or polyisoprene, flexible polyurethanes and other thermoplastic rubber polymers.
Claim 5
Dependent Claim
147 words
The composite of claim 2 wherein the substrate polymer is a polycarbonate, a thermoplastic polyester, or a monovinylidene aromatic polymer; the soft adhesive polymer is a flexible polyurethane or a block copolymer of polystyrene and polybutadiene; and the metal is indium, an alloy of about 55 percent tin, about 35 percent bismuth, and about 10 percent silver; an alloy of about 50 percent zinc and about 50 percent cadmium, an alloy of about 80 percent tin, about 15 percent bismuth and about 5 percent copper; an alloy of about 75 percent tin, about 20 percent bismuth and about 5 percent silver; an alloy of about 75 percent tin and about 25 percent silver; an alloy of about 75 percent tin and about 25 percent lead; and an alloy of about 50 percent tin, about 30 percent bismuth and about 20 percent copper, said percentage being by weight.
Claim 6
Dependent Claim
79 words
A formed metal/organic polymer composite made from the composite of claim 1 wherein during forming, at least a portion of the composite undergoes a cumulative surface dimensional change of at least 20 percent, said metal being a metal or a metal alloy of two or more metals that melts at a temperature or over a range of temperatures that is from about 80 to about 135 percent of the temperature used in the forming, said temperatures being in °K.
Claim 7
Dependent Claim
42 words
The composite of claim 1 wherein the liquidus temperature and the solidus temperature of the metal are within the range from about 0.8 T f to about 1.35 T f , wherein T f is the temperature used in forming the composite.
Claim 8
Dependent Claim
36 words
The composite of claim 3 wherein the thickness of the metal layer is from about 0.002 to about 1 micrometer and the thickness of the soft adhesive layer is from about 25 to about 250 micrometers.
Claim 9
Dependent Claim
29 words
The composite of claim 1 which also comprises a polymeric material adherent to an exposed major surface of the soft adhesive polymer layer, said polymeric material reinforcing the composite.
Claim 10
Dependent Claim
13 words
The composite of claim 8 wherein the reinforcing polymeric material is a polyurethane.
Claim 11
Dependent Claim
14 words
The composite of claim 8 wherein the reinforcing polymeric material is an ABS resin.
Claim 12
Dependent Claim
18 words
The composite of claim 1 wherein the thickness of the metal layer is less than about 1 micrometer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-23 | 1984-06-23 | 1984-12-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-23 | 1988-06-23 | 1988-12-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-23 | 1992-06-23 | 1992-12-23 | $7700.00 | Window Closed / Lapsed |