Rheological control of polyester-styrene resin compositions
Assignee: Georgia Kaolin Co
•
Filing: 1975-12-23
•
Granted: 1980-12-23
•
Expires: 1995-12-23
Abstract
Abstract A method and composition for control of rheological properties of polyester-styrene resin compositions is provided in which a smectite is reacted with a quaternary ammonium salt to provide a desired level of quaternary ammonium salt thereon and the treated smectite is added to a polyester-styrene resin mixture to produce a desired level of viscosity.
Inventors
- 👤 William F. Moll, Jr.
- 👤 Thomas D. Thompson, III
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:19
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34; C08K3/346; C08K5/00; C08K5/16; C08K5/17; C08K9/00; C08K9/04
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
122 words
The method of controlling the rheological properties of polyester-styrene resin compositions comprising the steps of: (a) reacting dimethyl benzylhydrogenated tallow amine in varying amounts with a smectite in a water system to determine an optimum level of amine on said smectite to provide a desired viscosity in said polyester-styrene resin system and a thixotropic index above about 2.5, without regard to the ion exchange capacity of the smectite, (b) reacting the amine in the determined optimum with said smectite to provide a desired optimum level of dimethyl benzylhydrogenated tallow amine on said smectite, (c) recovering the resulting reaction product from the water system, and (d) adding the recovered reaction product to a polyester-styrene resin mixture to produce a desired level of viscosity.
Claim 2
Independent Claim
122 words
The method of controlling the rheological properties of polyester-styrene resin compositions comprising the steps of: (a) reacting dimethyl benzylhydrogenated tallow amine in varying amounts with a smectite in a water system to determine an optimum level of amine on said smectite to provide a desired viscosity in said polyester-styrene resin system and a thixotropic index above about 2.5, without regard to the ion exchange capacity of the smectite, (b) reacting the amine in the determined optimum with said smectite to provide a desired optimum level of dimethyl benzylhydrogenated tallow amine on said smectite, (c) recovering the resulting reaction product from the water system, and (d) adding the recovered reaction product to a polyester-styrene resin mixture to produce a desired level of viscosity.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein the level of quaternary ammonium salt is measured as loss on ignition.
Claim 4
Dependent Claim
18 words
The method as claimed in claim 1 wherein the reaction product is added directly to the polyester-styrene composition.
Claim 5
Dependent Claim
33 words
The method as claimed in claim 1 wherein the reaction product is first added to a small amount of styrene to form a pregel and the pregel is added to the polyester-styrene composition.
Claim 6
Dependent Claim
31 words
The method as claimed in claim 1 wherein the reaction product is added to the styrene component of the polyester-styrene composition to form a pregel prior to addition to the polyester.
Claim 7
Dependent Claim
52 words
The method as claimed in claim 1 wherein the optimum level of treatment for the clay is determined by varying the amount of quaternary ammonium salt on the smectite to determine the optimum level of viscosity and the clay is then treated to said optimum level to provide the desired reaction product.
Claim 8
Dependent Claim
32 words
A method as claimed in claim 1 wherein the quaternary ammonium salt is a member selected from the group consisting of dimethyldialkyl ammonium halides and methylsulfates and dimethylbenzylalkyl ammonium halides and methylsulfates.
Claim 9
Dependent Claim
17 words
A method as claimed in claim 7 wherein the alkyl group contains at least 10 carbon atoms.
Claim 10
Dependent Claim
47 words
A material adapted to control the rheological properties of polyester-styrene resin systems consisting of a reaction product of smectite and dimethyl benzylhydrogenated tallow amine, selected to produce a desired viscosity and a thixotropic index above about 2.5, without regard to the ion exchange capacity of the smectite.
Claim 11
Dependent Claim
47 words
A material adapted to control the rheological properties of polyester-styrene resin systems consisting of a reaction product of smectite and dimethyl benzylhydrogenated tallow amine, selected to produce a desired viscosity and a thixotropic index above about 2.5, without regard to the ion exchange capacity of the smectite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-23 | 1984-06-23 | 1984-12-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-23 | 1988-06-23 | 1988-12-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-23 | 1992-06-23 | 1992-12-23 | $7700.00 | Window Closed / Lapsed |