Solventless silicone resins
Assignee: General Electric Co
•
Filing: 1978-11-24
•
Granted: 1980-12-16
•
Expires: 1998-11-24
Abstract
Abstract There is provided by the present invention a process for producing a solventless silicone resin having a viscosity at 100% varying from 200 to 5,000 centipoise at 25° C., comprising adding a mixture of water and alcohol to the desired organochlorosilanes taking the silicone alkoxylate and washing it repeatedly with alcohol until the acid content is at least below 1000 parts per million, adding an alkali metal hydroxide to reduce the acidity of the silicone alkoxylate such that it does not exceed 100 parts per million, and then adding sufficient water such that the amount of water that is added is between 0.2 to 0.8 moles of water per mole of hydrocarbonoxy radicals in such silicone hydrolyzate. The excess alcohol and water is stripped off to give the solventless silicone resin of the instant invention having an organo to Si ratio varying from 1.1 to 1.9, having a silanol content varying from 1 to 4% by weight and a hydrocarbonoxy content that varies from 7 to 14% by weight. A less preferred solventless system can be obtained by simply mixing in an organic solvent, a high alkoxy containing silicone resin produced by traditional procedures, and a high silanol silicone resin also produced by traditional procedure and stripping off the solvent.
Inventors
- 👤 George F. Roedel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:19
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/04; C08G77/14; C08G77/18
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
283 words
A silicone paint comprising a solventless silicone resin having an alkoxy content varying from 7 to 14% by weight and a viscosity at 100% solids varying from 200 to 5,000 centipoise at 25° C. comprising (a) adding to organo chlorosilanes of the formula, R.sub.a SiCl.sub.4-a where R is selected from the class consisting of alkyl radicals, cycloalkyl radicals, alkenyl radicals, aryl radicals and fluoroalkyl radicals all having up to 8 carbon atoms and mixtures thereof where a is 1 or 2, from 0.05 to 0.2 part of water and from 0.1 to 1 part of an aliphatic alcohol of up to 3 carbon atoms per part of organochlorosilane to form a silicone alkoxylate; (b) heating the alkoxylate to reflux (c) inserting additional amounts of said aliphatic alcohol to said alkoxylate and removing said alcohol until the acid-content of said alkoxylate is below 1000 parts per million; (d) adding an alkali metal hydroxide to said alkoxylate until its acid content does not exceed 100 parts per million (e) adding water to said alkoxylate such that the amount of water that is added from 0.2 to 0.8 moles of water per mole of hydrocarbonoxy radicals in said alkoxylate; and (f) heating said alkoylate so as to effect the hydrolysis reaction with the additional water to obtain the desired resin product wherein in said silicone paint there is present at 100% solids the silicone resin and from 0.05 to 4.0% by weight of the silicone resin of a curing catalysts selected from the class consisting of metal salts of carboxylic acids where the metal ion varies from manganese to zinc in the Periodic Table with the exception of iron and amine functional silanes and mixtures thereof.
Claim 2
Dependent Claim
283 words
A silicone paint comprising a solventless silicone resin having an alkoxy content varying from 7 to 14% by weight and a viscosity at 100% solids varying from 200 to 5,000 centipoise at 25° C. comprising (a) adding to organo chlorosilanes of the formula, R.sub.a SiCl.sub.4-a where R is selected from the class consisting of alkyl radicals, cycloalkyl radicals, alkenyl radicals, aryl radicals and fluoroalkyl radicals all having up to 8 carbon atoms and mixtures thereof where a is 1 or 2, from 0.05 to 0.2 part of water and from 0.1 to 1 part of an aliphatic alcohol of up to 3 carbon atoms per part of organochlorosilane to form a silicone alkoxylate; (b) heating the alkoxylate to reflux (c) inserting additional amounts of said aliphatic alcohol to said alkoxylate and removing said alcohol until the acid-content of said alkoxylate is below 1000 parts per million; (d) adding an alkali metal hydroxide to said alkoxylate until its acid content does not exceed 100 parts per million (e) adding water to said alkoxylate such that the amount of water that is added from 0.2 to 0.8 moles of water per mole of hydrocarbonoxy radicals in said alkoxylate; and (f) heating said alkoylate so as to effect the hydrolysis reaction with the additional water to obtain the desired resin product wherein in said silicone paint there is present at 100% solids the silicone resin and from 0.05 to 4.0% by weight of the silicone resin of a curing catalysts selected from the class consisting of metal salts of carboxylic acids where the metal ion varies from manganese to zinc in the Periodic Table with the exception of iron and amine functional silanes and mixtures thereof.
Claim 3
Dependent Claim
287 words
A silicone varnish comprising a solventless silicone resin having an alkoxy content varying from 7 to 14% by weight and having a viscosity at 100% solids varying from 200 to 5,000 centipoise at 25° C. comprising (a) adding to organo chlorosililanes of the formula, R.sub.a SiCl.sub.4-a where R is selected from the class consisting of alkyl radicals, cycloalkyl radicals, alkenyl radicals, aryl radicals and fluoroalkyl radicals all having up to 8 carbon atoms and mixtures thereof where a is 1 or 2, from 0.05 to 0.2 part of water and from 0.1 to 1 part of an aliphatic alcohol of up to 3 carbon atoms per part of organochlorosilane to form a silicone alkoxylate; (b) heating the alkoxylate to reflux (c) inserting additional amounts of said aliphatic alcohol to said alkoxylate and removing said alcohol until the acid-content of said alkoxylate is below 1000 parts per million; (d) adding an alkali metal hydroxide to said alkoxylate until its acid content does not exceed 100 parts per million (e) adding water to said alkoxylate such that the amount of water that is added from 0.2 to 0.8 moles of water per mole of hydrocarbonoxy radicals in said alkoxylate; and (f) heating said alkoxylate so as to effect the hydrolysis reaction with the additional water to obtain the desired resin product wherein in said silicone varnish there is present said silicone resin at a concentration of 100% solids and from 0.05 to 4.0% by weight of the silicone resin of a curing catalyst selected from the class consisting of metal salts of carboxylic acid where the metal ions vary from manganese to zinc in the Periodic Table with the exception of iron and amino functional silanes and mixtures thereof.
Claim 4
Dependent Claim
287 words
A silicone varnish comprising a solventless silicone resin having an alkoxy content varying from 7 to 14% by weight and having a viscosity at 100% solids varying from 200 to 5,000 centipoise at 25° C. comprising (a) adding to organo chlorosililanes of the formula, R.sub.a SiCl.sub.4-a where R is selected from the class consisting of alkyl radicals, cycloalkyl radicals, alkenyl radicals, aryl radicals and fluoroalkyl radicals all having up to 8 carbon atoms and mixtures thereof where a is 1 or 2, from 0.05 to 0.2 part of water and from 0.1 to 1 part of an aliphatic alcohol of up to 3 carbon atoms per part of organochlorosilane to form a silicone alkoxylate; (b) heating the alkoxylate to reflux (c) inserting additional amounts of said aliphatic alcohol to said alkoxylate and removing said alcohol until the acid-content of said alkoxylate is below 1000 parts per million; (d) adding an alkali metal hydroxide to said alkoxylate until its acid content does not exceed 100 parts per million (e) adding water to said alkoxylate such that the amount of water that is added from 0.2 to 0.8 moles of water per mole of hydrocarbonoxy radicals in said alkoxylate; and (f) heating said alkoxylate so as to effect the hydrolysis reaction with the additional water to obtain the desired resin product wherein in said silicone varnish there is present said silicone resin at a concentration of 100% solids and from 0.05 to 4.0% by weight of the silicone resin of a curing catalyst selected from the class consisting of metal salts of carboxylic acid where the metal ions vary from manganese to zinc in the Periodic Table with the exception of iron and amino functional silanes and mixtures thereof.
References Cited (Backward Citations)
US3725339A
Cited
US3786015A
Cited
US3978025A
Cited
US3846358A
Cited
US3948848A
Cited
US4085084A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-16 | 1984-06-16 | 1984-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-16 | 1988-06-16 | 1988-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-16 | 1992-06-16 | 1992-12-16 | $7700.00 | Window Closed / Lapsed |