Surface-treating agent adapted for intermediate products of a semiconductor device
Assignee: Toshiba Corp
•
Filing: 1978-07-21
•
Granted: 1980-12-16
•
Expires: 1998-07-21
Abstract
Abstract A surface-treating agent formed of an aqueous solution containing 0.01 to 20% by weight of trialkyl(hydroxyalkyl) ammonium hydroxide. The treating agent is adapted to be used for the effective removal of organic and inorganic contaminants deposited on the surface of intermediate semiconductor products obtained in the respective steps of manufacturing a semiconductor device and the efficient etching of a metal layer used as wiring. Further, it can be used for the elimination of those portions of a positive working photoresist film coated on the surface of the intermediate semiconductor products which are and are not exposed to a light by controlling its concentration.
Inventors
- 👤 Hisashi Muraoka
- 👤 Masafumi Asano
- 👤 Taizo Ohashi
- 👤 Yuzo Shimazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 05:31
CPC Classifications
H; H10; H10P; H10P70/00; H10P70/10; H10P70/15; C; C11; C11D; C11D3/00; C11D3/16; C11D3/26; C11D3/30; C23; C23G; C23G1/00; C23G1/14
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
110 words
A method for cleaning the surface of an intermediate product obtained in the manufacture of a semiconductor device which comprises bringing the surface of said intermediate product into contact with an aqueous solution at a temperature and for a time effective to clean the surface of said intermediate product, the aqueous solution containing an effective amount within the range of 0.01 to 20% by weight of at least one trialkyl(hydroxyalkyl) ammonium hydroxide expressed by the formula: ##STR4## where R 1 , R 2 , and R 3 are alkyl groups each having one to four carbon atoms, and R 4 is an alkylene group having two to four carbon atoms.
Claim 2
Independent Claim
110 words
A method for cleaning the surface of an intermediate product obtained in the manufacture of a semiconductor device which comprises bringing the surface of said intermediate product into contact with an aqueous solution at a temperature and for a time effective to clean the surface of said intermediate product, the aqueous solution containing an effective amount within the range of 0.01 to 20% by weight of at least one trialkyl(hydroxyalkyl) ammonium hydroxide expressed by the formula: ##STR4## where R 1 , R 2 , and R 3 are alkyl groups each having one to four carbon atoms, and R 4 is an alkylene group having two to four carbon atoms.
Claim 3
Dependent Claim
31 words
A method according to claim 1, wherein the trialkyl(hydroxyalkyl)ammonium hydroxide is trimethyl(2-hydroxyethyl)ammonium hydroxide, triethyl(2-hydroxyethyl)ammonium hydroxide, tripropyl(2-hydroxyethyl)ammonium hydroxide, tributyl(2-hydroxyethyl)ammonium hydroxide, dimethylethyl(2-hydroxyethyl)ammonium hydroxide, trimethyl(3-hydroxypropyl)ammonium hydroxide, trimethyl(3-hydroxybutyl)ammonium hydroxide, trimethyl(4-hydroxybutyl)ammonium hydroxide, or a mixture thereof.
Claim 4
Dependent Claim
22 words
A method according to claim 1, wherein the trialkyl(hydroxyalkyl)ammonium hydroxide is trimethyl(2-hydroxyethyl)ammonium hydroxide, triethyl(2-hydroxyethyl)ammonium hydroxide, trimethyl(3-hydroxypropyl) ammonium hydroxide, or a mixture thereof.
Claim 5
Dependent Claim
20 words
A method according to claim 1, wherein the aqueous solution contains 5 to 20% by weight of the trialkyl(hydroxyalkyl)ammonium hydroxide.
Claim 6
Dependent Claim
20 words
A method according to claim 1 wherein the trialkyl(hydroxyalkyl)ammonium hydroxide comprises 0.1 to 5% by weight of the aqueous solution.
Claim 7
Dependent Claim
20 words
A method according to claim 5 wherein the aqueous solution contains 1 to 3% by weight of the trialkyl(hydroxyalkyl)ammonium hydroxide.
Claim 8
Dependent Claim
42 words
A method according to claim 1, wherein the aqueous solution further comprises 0.01 to 10 parts by weight, based on 100 parts by weight of the aqueous solution, of at least one complexing agent capable of forming a water-soluble complex with metals.
Claim 9
Dependent Claim
30 words
A method according to claim 7, wherein the complexing agent is sodium cyanide, potassium cyanide, ammonium cyanide, ethylenediaminetetraacetic acid, sodium ethylenediaminetetraacetate, potassium etyhlenediaminetetraacetate, triethanolamine, ethylenediamine, cuproin, or a mixture thereof.
Claim 10
Dependent Claim
20 words
A method according to claim 8, wherein the amount of the complexing agent is 0.1 to 3 parts by weight.
Claim 11
Dependent Claim
34 words
A method according to claim 1, wherein the aqueous solution further comprises 0.001 to 5 parts by weight of at least one nonionic surfactant based on 100 parts by weight of the aqueous solution.
Claim 12
Dependent Claim
20 words
A method according to claim 10, wherein the amount of the nonionic surfactant is 0.01 to 2 parts by weight.
Claim 13
Dependent Claim
58 words
A method according to claim 10, wherein the nonionic surfactant is at least one polyoxyethylene type compound expressed by the formulae: ##STR5## where R and R" are alkyl groups each having 12 to 18 carbon atoms, R' is an alkyl group having 8 to 9 carbon atoms, m is 8 to 15, and n is 5 to 30.
Claim 14
Dependent Claim
14 words
A method according to claim 12, wherein the nonionic surfactant is polyoxyethylene nonylphenol ether.
Claim 15
Dependent Claim
31 words
A method according to claim 1, wherein the aqueous solution further comprises 0.003 to 30 parts by weight of hydrogen peroxide based on 100 parts by weight of the aqueous solution.
Claim 16
Dependent Claim
19 words
A method according to claim 14, wherein the amount of hydrogen peroxide is 0.06 to 3 parts by weight.
Claim 17
Dependent Claim
19 words
A method according to claim 14, wherein the amount of hydrogen peroxide is 0.06 to 1.5 parts by weight.
Claim 18
Independent Claim
105 words
A method for cleaning the surface of an intermediate product obtained in the manufacture of a semiconductor device which comprises immersing said intermediate product in an aqueous solution for 5 to 20 minutes, said solution being maintained at a temperature from 70° to 90° C., said solution containing an effective amount within the range of 0.01 to 20% by weight of at least one trialkyl(hydroxylakyl) ammonium hydroxide expressed by the formula: ##STR6## where R 1 , R 2 , and R 3 are alkyl groups each having one to four carbon atoms, and R 4 is an alkylene group having two to four carbon atoms.
Claim 19
Independent Claim
105 words
A method for cleaning the surface of an intermediate product obtained in the manufacture of a semiconductor device which comprises immersing said intermediate product in an aqueous solution for 5 to 20 minutes, said solution being maintained at a temperature from 70° to 90° C., said solution containing an effective amount within the range of 0.01 to 20% by weight of at least one trialkyl(hydroxylakyl) ammonium hydroxide expressed by the formula: ##STR6## where R 1 , R 2 , and R 3 are alkyl groups each having one to four carbon atoms, and R 4 is an alkylene group having two to four carbon atoms.
Claim 20
Independent Claim
34 words
A method according to claims 17, 45 or 46, wherein the aqueous solution further comprises 0.003 to 30 parts by weight of hydrogen peroxide based on 100 parts by weight of the aqueous solution.
Claim 21
Independent Claim
45 words
A method according to claims 17, 45 or 46, wherein the aqueous solution further comprises 0.01 to 10 parts by weight, based on 100 parts by weight of the aqueous solution, of at least one complexing agent capable of forming a water-soluble complex with metals.
Claim 22
Independent Claim
37 words
A method according to claims 17, 45 or 46, wherein the aqueous solution further comprises 0.001 to 5 parts by weight of at least one nonionic surfactant based on 100 parts by weight of the aqueous solution.
Claim 23
Independent Claim
137 words
A method for removing a photoresist film from the surface of an intermediate product obtained in the manufacture of a semiconductor device which comprises bringing the surface of an intermediate product obtained in the manufacture of a semiconductor device having a positive-working photoresist film thereon into contact with an aqueous solution at a temperature and for a time effective to remove at least a portion of the photoresist film from the surface of the intermediate product, the aqueous solution containing an effective amount within the range of 0.01 to 20% by weight of at least one trialkyl(hydroxyalkyl) ammonium hydroxide expressed by the formula: ##STR7## where R 1 , R 2 , and R 3 are alkyl groups each having one to four carbon atoms, and R 4 is an alkylene group having two to four carbon atoms.
Claim 24
Independent Claim
137 words
A method for removing a photoresist film from the surface of an intermediate product obtained in the manufacture of a semiconductor device which comprises bringing the surface of an intermediate product obtained in the manufacture of a semiconductor device having a positive-working photoresist film thereon into contact with an aqueous solution at a temperature and for a time effective to remove at least a portion of the photoresist film from the surface of the intermediate product, the aqueous solution containing an effective amount within the range of 0.01 to 20% by weight of at least one trialkyl(hydroxyalkyl) ammonium hydroxide expressed by the formula: ##STR7## where R 1 , R 2 , and R 3 are alkyl groups each having one to four carbon atoms, and R 4 is an alkylene group having two to four carbon atoms.
Claim 25
Dependent Claim
20 words
A method according to claim 21, wherein the aqueous solution contains 1 to 10% by weight of the trialkyl(hydroxyalkyl)ammonium hydroxide.
Claim 26
Dependent Claim
31 words
A method according to claim 21, wherein the trialkyl(hydroxyalkyl)ammonium hydroxide is trimethyl(2-hydroxyethyl)ammonium hydroxide, triethyl(2-hydroxyethyl)ammonium hydroxide, tripropyl(2-hydroxyethyl)ammonium hydroxide, tributyl(2-hydroxyethyl)ammonium hydroxide, dimethylethyl(2-hydroxyethyl)ammonium hydroixde, trimethyl(3-hydroxypropyl)ammonium hydroxide, trimethyl(3-hydroxybutyl)ammonium hydroxide, trimethyl(4hydroxybutyl)ammonium hydroxide, or a mixture thereof.
Claim 27
Dependent Claim
21 words
A method according to claim 21, wherein the trialkyl(hydroxyalkyl)ammonium hydroxide is trimethyl(2-hydroxyethyl)ammonium hydroxide, triethyl(2-hydroxyethyl)ammonium hydroxide, trimethyl(3-hydroxypropyl)ammonium hydroxide, or a mixture thereof.
Claim 28
Dependent Claim
23 words
A method according to claim 21, wherein the aqueous solution contains more than 10 up to 20% by weight of the trialkyl(hydroxyalkyl)ammonium hydroxide.
Claim 29
Dependent Claim
55 words
A method according to claim 21 wherein the trialkyl(hydroxyalkyl)ammonium hydroxide comprises 1 to 10% by weight of the aqueous solution where the photoresist film is exposed to light; and wherein the trialkyl(hydroxyalkyl)ammonium hydroxide comprises more than 10 up to 20% by weight of the aqueous solution where the photoresist film is not exposed to light.
Claim 30
Independent Claim
128 words
A method for etching a metal layer in the surface of an intermediate product obtained in the manufacture of a semiconductor device which comprises bringing the surface of an intermediate product obtained in the manufacture of a semiconductor device having a metal layer thereon into contact with an aqueous solution at a temperature and for a time effective to etch at least a portion of the metal layer, the aqueous solution containing an effective amount within the range of 0.01 to 20% by weight of at least one trialkyl(hydroxyalkyl)ammonium hydroxide expressed by the formula: ##STR8## where R 1 , R 2 , and R 3 are alkyl groups each having one to four carbon atoms, and R 4 is an alkylene group having two to four carbon atoms.
Claim 31
Independent Claim
128 words
A method for etching a metal layer in the surface of an intermediate product obtained in the manufacture of a semiconductor device which comprises bringing the surface of an intermediate product obtained in the manufacture of a semiconductor device having a metal layer thereon into contact with an aqueous solution at a temperature and for a time effective to etch at least a portion of the metal layer, the aqueous solution containing an effective amount within the range of 0.01 to 20% by weight of at least one trialkyl(hydroxyalkyl)ammonium hydroxide expressed by the formula: ##STR8## where R 1 , R 2 , and R 3 are alkyl groups each having one to four carbon atoms, and R 4 is an alkylene group having two to four carbon atoms.
Claim 32
Dependent Claim
29 words
A method according to claim 27, wherein the trialkyl(hydroxyalkyl)ammonium hydroxide is trimethyl(2-hydroxyethyl)ammonium hydroxide, triethyl(2-hydroxyethyl)ammonium hydroxide, tripropyl(2-hydroxyethyl)ammonium hydroxide, tributyl(2-hydroxyethyl)ammonium hydroxide, dimethylethyl(2-hydroxyethyl)ammonium hydroxide, trimthyl(3-hydroxypropyl)ammonium hydroxide, trimethyl(3-hydroxybutyl)ammonium hydroxide, or a mixture thereof.
Claim 33
Dependent Claim
21 words
A method according to claim 27, wherein the trialkyl(hydroxyalkyl)ammonium hydroxide is trimethyl(2-hydroxyethyl)ammonium hydroxide, triethyl(2-hydroxyethyl)ammonium hydroxide, trimethyl(3-hydroxypropyl)ammonium hydroxide, or a mixture thereof.
Claim 34
Dependent Claim
21 words
A surface-treating agent according to claim 27, wherein the aqueous solution contains 5 to 10% by weight of the trialkyl(hydroxyalkyl)ammonium hydroxide.
Claim 35
Dependent Claim
38 words
A method according to claim 27, wherein the intermediate product is immersed in the aqueous solution for a time effective to etch the metal layer, the aqueous solution being maintained at a temperature of 60° to 70° C.
Claim 36
Dependent Claim
40 words
A method according to claim 27 wherein the trialkyl(hydroxyalkyl)ammonium hydroxide comprises from 5 to 10% by weight of the aqueous solution, and the trialkyl(hydroxyalkyl)ammonium hydroxide is applied to said intermediate product by immersing said intermediate product in the aqueous solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-16 | 1984-06-16 | 1984-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-16 | 1988-06-16 | 1988-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-16 | 1992-06-16 | 1992-12-16 | $7700.00 | Window Closed / Lapsed |