Production of extreme purity aluminum

Claim 2

An improved process for purifying aluminum containing impurities comprising: (a) providing an electrolytic cell for the purification of aluminum, the cell of the type having a bottom layer of molten aluminum constituting an anode layer and having a top layer of molten aluminum constituting a cathode layer, the anode layer separated from the cathode layer by an electrolyte layer, the cell having a floor of carbonaceous material and walls comprised of (i) an outer insulating refractory layer; and (ii) an inner refractory liner fabricated from high purity bricks containing at least 90 wt.% alumina, the bricks bonded together with a high purity cement resistant to attack by molten aluminum and molten salt. (b) introducing aluminum to the cell; (c) electrolytically transporting aluminum from said anode layer through said electrolyte layer to said cathode layer while leaving said impurities in said anode layer thereby partially purifying said aluminum; (d) thereafter, removing a portion of said partially purified molten aluminum from said cathode layer; (e) fractionally crystallizing said molten aluminum portion in a crystallization cell to remove eutectic impurities therefrom by solidifying a fraction of said molten aluminum, said solid fraction having a higher purity than the constituting the remaining molten aluminum fraction, thereby concentrating said eutectic impurites in said molten fraction; and (f) separating said molten fraction from said solid fraction to provide said purified aluminum.

Claim 3

The method in accordance with claim 1 wherein alumina bricks contain 92 to 99 wt.% alumina.

Claim 4

The method in accordance with claim 1 wherein the cement contains 43 to 89 wt.% alumina, 10 to 45 wt.% calcium aluminate, 0.5 to 10 wt.% zinc borosilicate and 0.1 to 1.5 wt.% boric acid.

Claim 5

An improved process for purifying aluminum containing impurities comprising: (a) providing an electrolytic cell for the purification of aluminum, the cell of the type having a bottom layer of molten aluminum constituting said anode layer and having a top layer of molten aluminum constituting a cathode layer, said anode layer separated from said cathode layer by an electrolyte layer, the cell having a flow of carbonaceous material and walls comprised of (i) an outer insulating refractory layer; and (ii) an inner refractory liner fabricated from high purity bricks containing at least 90 wt.% alumina, the bricks bonded together with a high purity cement resistant to attack by molten aluminum and molten salt. (b) introducing aluminum to the cell; (c) electrolytically transporting aluminum from said anode layer through said electrolyte layer to said cathode layer while leaving said impurities in said anode layer thereby partially purifying said aluminum, said transporting being capable of recovering aluminum at the cathode consisting essentially of 99.993 wt.% aluminum; (d) thereafter, removing a portion of said partially purified molten aluminum from said cathode layer; (e) fractionally crystallizing said molten aluminum portion in a crystallization cell to remove eutectic impurities therefrom by solidifying a fraction of said molten aluminum, said solid fraction having a higher purity than that constituting the remaining molten aluminum fraction, thereby concentrating said eutectic impurities in said molten fraction, said crystallizing adapted to recover aluminum product consisting essentially of 99.999 wt.% aluminum when the feed to the process is about 99.993 wt.%; and (f) separating said molten fraction from said solid fraction to provide said purified aluminum, said improved process suited to recover 50 wt.% of the feed to the process.

Claim 6

An improved process for purifying aluminum containing impurities comprising: (a) providing an electrolytic cell for the purification of aluminum, the cell of the type having a bottom layer of molten aluminum constituting said anode layer and having a top layer of molten aluminum constituting a cathode layer, said anode layer separated from said cathode layer by an electrolyte layer, the cell having a flow of carbonaceous material and walls comprised of (i) an outer insulating refractory layer; and (ii) an inner refractory liner fabricated from high purity bricks containing at least 90 wt.% alumina, the bricks bonded together with a high purity cement resistant to attack by molten aluminum and molten salt. (b) introducing aluminum to the cell; (c) electrolytically transporting aluminum from said anode layer through said electrolyte layer to said cathode layer while leaving said impurities in said anode layer thereby partially purifying said aluminum, said transporting being capable of recovering aluminum at the cathode consisting essentially of 99.993 wt.% aluminum; (d) thereafter, removing a portion of said partially purified molten aluminum from said cathode layer; (e) fractionally crystallizing said molten aluminum portion in a crystallization cell to remove eutectic impurities therefrom by solidifying a fraction of said molten aluminum, said solid fraction having a higher purity than that constituting the remaining molten aluminum fraction, thereby concentrating said eutectic impurities in said molten fraction, said crystallizing adapted to recover aluminum product consisting essentially of 99.999 wt.% aluminum when the feed to the process is about 99.993 wt.%; and (f) separating said molten fraction from said solid fraction to provide said purified aluminum, said improved process suited to recover 50 wt.% of the feed to the process.