Method and apparatus for movement of heated thermoplastic elements for shear-fusion bonding of such thermoplastic elements
Assignee: Individual
•
Filing: 1978-10-26
•
Granted: 1980-12-16
•
Expires: 1998-10-26
Abstract
Abstract A shear-fusion bond method is provided to create a direct fusion joinder or bond over an extended interface between like thermoplastic elastomeric elements of a block copolymer having a rubber-like center or mid-block and styrene end blocks. Such material has a high melt viscosity and does not readily flow. The interface surfaces are coupled to a heat source and heated to a fusion bonding temperature, thereby softening the interface material so that it flows under pressure. The elements, with the surfaces in pressurized engagement, are rotated relative to each other about an axis which is normal to the interface. Rotation is through an angle of at least 10 degrees to subject the softened interface material to a high rate shear force movement substantially in the plane of the interface. This decreases the viscosity and causes the interface material to bondably flow. The interface surfaces are firmly held together while in the bondably flowing state to create a shear-fusion bond in which the interface disappears. The surfaces may be separately heated on a hot platen and then located in abutting engagement for rotation. The surfaces may also be provided with appropriate heat generating particles. The surfaces are inductively heated from a suitable field source to soften the interface, and then rotated.
Inventors
- 👤 Alfred F. Leatherman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:47
CPC Classifications
B; B29; B29C; B29C65/00; B29C65/02; B29C65/06; B29C65/0609; B29C65/0627; B29C65/18; B29C65/20; B29C65/2053; B29C65/2084; B29C65/34; B29C65/36; B29C65/3604; B29C65/3608; B29C65/3612; B29C65/3672; B29C65/3684; B29C66/00; B29C66/01; B29C66/02; B29C66/024; B29C66/0242; B29C66/05; B29C66/10; B29C66/13; B29C66/131; B29C66/1312; B29C66/32; B29C66/324; B29C66/341; B29C66/50; B29C66/51; B29C66/54; B29C66/70; B29C66/71; B29C66/712; B29C66/80; B29C66/81; B29C66/814; B29C66/8141; B29C66/81431; B29C66/82; B29C66/824; B29C66/8242; B29C66/83; B29C66/832; B29C66/8322; B29C65/0672; B29C65/3472; B29C65/3476; B29C65/3676; B29C65/368; B29C66/816; B29K; B29K2009/00; B29K2009/06; B29K2096/00; B29K2096/04; B29K2105/00; B29K2105/06; B29K2105/16
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
108 words
A method of fusion bonding plastic elements over extended interface surfaces, comprising heating the interface material to a fusion bonding temperature from a separate thermal energy source and thereby softening the interface material of said plastic elements independently of movement of said elements, subjecting the softened interface material to a high rate shear force movement in the plane of the interface to lower the viscosity of the interface material and cause said interface material to bondably flow, said shear force movement being insufficient to establish significant heating of said interface, and holding the interface surfaces while in the flowing state in firm engagement to create a fusion bond.
Claim 2
Independent Claim
108 words
A method of fusion bonding plastic elements over extended interface surfaces, comprising heating the interface material to a fusion bonding temperature from a separate thermal energy source and thereby softening the interface material of said plastic elements independently of movement of said elements, subjecting the softened interface material to a high rate shear force movement in the plane of the interface to lower the viscosity of the interface material and cause said interface material to bondably flow, said shear force movement being insufficient to establish significant heating of said interface, and holding the interface surfaces while in the flowing state in firm engagement to create a fusion bond.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein the step of subjecting the interface material to a shear force movement includes the step of rotating the elements relative to each other.
Claim 4
Dependent Claim
17 words
The method of claim 2 including rotating the element through an angle of at least 10 degrees.
Claim 5
Dependent Claim
19 words
The method of claim 2 including rotating the element through an angle of between 10 degrees and 120 degrees.
Claim 6
Dependent Claim
47 words
The method of claim 1, 2, 3, or 4 wherein the step of heating said interface surfaces includes separately heating of each surface and thereafter locating the surfaces in engagement and moving said elements for the subjecting of the softened interface material to the shear force movement.
Claim 7
Dependent Claim
21 words
The method of claim 1, 2, 3, or 4 wherein the interface surfaces are located in engagement during the heating step.
Claim 8
Dependent Claim
31 words
The method of claim 6 wherein the heating step includes the dispersion of heat generating particles throughout one of the elements and applying a high frequency energy field to said element.
Claim 9
Dependent Claim
26 words
The method of claim 7 wherein said particles are selected from the class consisting of gamma Fe 2 O 3 and Fe 3 O 4 .
Claim 10
Independent Claim
127 words
A method of fusion bonding like plastic elements having a high melt viscosity over extended interface surfaces, comprising heating the interface material to a fusion bonding temperature from a separate thermal energy source independently of the movement of said elements and thereby softening the interface material of said plastic elements, holding the interface surfaces while in the softened state in firm engagement, moving the elements relative to each other in the plane of the interface and thereby subjecting the softened interface material to a high rate shear force movement in the plane of the interface with the softened surfaces in engagement to lower the viscosity of the interface material and cause said interface material to bondably flow, and then cooling the interface to create a fusion bond.
Claim 11
Independent Claim
127 words
A method of fusion bonding like plastic elements having a high melt viscosity over extended interface surfaces, comprising heating the interface material to a fusion bonding temperature from a separate thermal energy source independently of the movement of said elements and thereby softening the interface material of said plastic elements, holding the interface surfaces while in the softened state in firm engagement, moving the elements relative to each other in the plane of the interface and thereby subjecting the softened interface material to a high rate shear force movement in the plane of the interface with the softened surfaces in engagement to lower the viscosity of the interface material and cause said interface material to bondably flow, and then cooling the interface to create a fusion bond.
Claim 12
Dependent Claim
46 words
The method of claim 9 wherein the interface material flows laterally of the interface and including the step of terminating the heating of the interface material in timed relationship to the lateral flow of the interface material to reduce the lateral flow of the interface material.
Claim 13
Dependent Claim
44 words
The method of claim 9 or 10 including the insertion of a bonding element of the same material as the plastic elements, said bonding element including particles responsive to an energy field to generate heat, said heating including the creation of said energy field.
Claim 14
Dependent Claim
12 words
The method of claim 11 wherein the particles are substantially uniformily dispersed.
Claim 15
Dependent Claim
27 words
The method of claim 11 wherein the energy field is removed in timed relationship to the step of subjecting the interface material to a shear force movement.
Claim 16
Dependent Claim
39 words
The method of claim 9 wherein said elements are formed of elastomeric polymer having a molecular structure creating a high viscosity at all temperatures below a charring temperature and thereby preventing gravity flow as the result of heating only.
Claim 17
Independent Claim
128 words
The method of fusion bonding thermoplastic elastomeric elements formed of block polymers having center blocks and end blocks, said elements having opposed interface surfaces, comprising applying heat to each of said interface surfaces to raise the temperature to a melt temperature and thereby softening the interface surfaces, mounting the elements with the softened surfaces in engagement, applying a clamping pressure across the softened interface surfaces, and rotating the heated elements relative to each other on an axis substantially perpendicular to the interface with said interface surfaces in said softened state at a sufficiently rapid rate with said clamping force applied to create shear force movement of the softened interface surfaces and thereby creating a bonding flow of the softened surfaces to create complete fusion of the interface surfaces.
Claim 18
Independent Claim
128 words
The method of fusion bonding thermoplastic elastomeric elements formed of block polymers having center blocks and end blocks, said elements having opposed interface surfaces, comprising applying heat to each of said interface surfaces to raise the temperature to a melt temperature and thereby softening the interface surfaces, mounting the elements with the softened surfaces in engagement, applying a clamping pressure across the softened interface surfaces, and rotating the heated elements relative to each other on an axis substantially perpendicular to the interface with said interface surfaces in said softened state at a sufficiently rapid rate with said clamping force applied to create shear force movement of the softened interface surfaces and thereby creating a bonding flow of the softened surfaces to create complete fusion of the interface surfaces.
Claim 19
Dependent Claim
50 words
The method of claim 15 wherein the interface surfaces are simultaneously heated for a period on the order of one second with the surfaces in fixed and abutting engagement, and said step of rotating the elements is provided after the start of the last one-half second of the heating period.
Claim 20
Dependent Claim
23 words
The method of claim 16 wherein said step of rotating the element is provided during the last one-half second of the heating period.
Claim 21
Dependent Claim
19 words
The method of claim 16 or 17 including rotating the element through an angle of at least 10 degrees.
Claim 22
Dependent Claim
19 words
The method of claim 18 including rotating the element through an angle of between 10 degrees and 120 degrees.
Claim 23
Dependent Claim
36 words
The method of claim 15 wherein the heating of the interface surfaces is separately and individually completed, and said mounting of the elements is carried out immediately upon completion of the heating of the interface surfaces.
Claim 24
Dependent Claim
25 words
The method of claim 20 wherein said heating step includes placing of the elements on a heating platen with the interface surfaces engaging the platen.
Claim 25
Independent Claim
86 words
The method of bonding plastic elements formed of molecular structure including olefin center blocks and styrene end blocks over extended planar interface bonding surfaces, comprising separately heating the bonding surfaces to soften the bonding surfaces independently of movement of said elements, locating the softened bonding surfaces into engagement under pressure, and rotating of the heated elements relative to each other on an axis essentially normal to the bonding surfaces to introduce shear forces into the softened bonding surfaces and thereby causing the softened material to flow.
Claim 26
Independent Claim
86 words
The method of bonding plastic elements formed of molecular structure including olefin center blocks and styrene end blocks over extended planar interface bonding surfaces, comprising separately heating the bonding surfaces to soften the bonding surfaces independently of movement of said elements, locating the softened bonding surfaces into engagement under pressure, and rotating of the heated elements relative to each other on an axis essentially normal to the bonding surfaces to introduce shear forces into the softened bonding surfaces and thereby causing the softened material to flow.
Claim 27
Dependent Claim
21 words
The method of claim 22 wherein the members are rotated through an angle at least on the order of ten degrees.
Claim 28
Dependent Claim
23 words
The method of claim 22 wherein the members are rotated through an angle of from ten degrees to one hundred and twenty degrees.
Claim 29
Dependent Claim
27 words
The method of claim 22 including the confining of the exposed end edges of the bonding surfaces to control the lateral movement of the softened bonding surfaces.
Claim 30
Independent Claim
76 words
The method of fusion bonding plastic elements comprising introducing susceptor particles at the interface of at least one of the plastic elements, subjecting the particles to high frequency magnetic field for generating heat in said particles and thereby softening the interface surfaces of said elements, and moving said plastic elements relative to each other with the interface surfaces softened for reducing the viscosity of the interface material and creating a fusion bond at the interface surfaces.
Claim 31
Independent Claim
76 words
The method of fusion bonding plastic elements comprising introducing susceptor particles at the interface of at least one of the plastic elements, subjecting the particles to high frequency magnetic field for generating heat in said particles and thereby softening the interface surfaces of said elements, and moving said plastic elements relative to each other with the interface surfaces softened for reducing the viscosity of the interface material and creating a fusion bond at the interface surfaces.
Claim 32
Dependent Claim
27 words
The method of claim 26 wherein said last named step is initiated only during a terminal portion of the subjecting of the particles to said magnetic field.
Claim 33
Dependent Claim
25 words
The method of claim 26 wherein said last named step is provided only after termination of the subjecting of the particles to said magnetic field.
Claim 34
Independent Claim
32 words
The method of anyone of the claims 26, 27 or 28 wherein said particles are selected from the group consisting of gamma Fe 2 O 3 and Fe 3 O 4 .
Claim 35
Independent Claim
139 words
A method of fusion bonding first and second self-supporting plastic elements aligned with common peripherial walls, said elements being bonded over an extended interface surface extending inwardly from the peripherial walls, comprising heating the interface material to a fusion bonding temperature from a separate thermal energy source independently of movement of said elements and thereby softening the interface material of said plastic elements, holding the interface surfaces while in the softened state in firm engagement, moving the self-supporting elements into increased compressive engagement over the complete bond interface and thereby subjecting the softened interface material to compression and thereby a high rate shear force movement with the separately softened surfaces in continuous engagement to lower the viscosity of the interface material and cause said interface material to bondably flow, and then cooling the interface to create a fusion bond.
Claim 36
Independent Claim
139 words
A method of fusion bonding first and second self-supporting plastic elements aligned with common peripherial walls, said elements being bonded over an extended interface surface extending inwardly from the peripherial walls, comprising heating the interface material to a fusion bonding temperature from a separate thermal energy source independently of movement of said elements and thereby softening the interface material of said plastic elements, holding the interface surfaces while in the softened state in firm engagement, moving the self-supporting elements into increased compressive engagement over the complete bond interface and thereby subjecting the softened interface material to compression and thereby a high rate shear force movement with the separately softened surfaces in continuous engagement to lower the viscosity of the interface material and cause said interface material to bondably flow, and then cooling the interface to create a fusion bond.
Claim 37
Dependent Claim
72 words
The method of claim 30 wherein said elements are formed of block polymers having center blocks and end blocks, said elements having particles responsive to a high frequency magnetic field to heat said elements and raise the temperature of the interface surfaces to a melt temperature, and including the step of applying a magnetic field to said elements before said moving of the elements to create the high rate shear force movement.
Claim 38
Dependent Claim
27 words
The method of claim 12 wherein the energy field is removed in timed relationship to the step of subjecting the interface material to a shear force movement.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-16 | 1984-06-16 | 1984-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-16 | 1988-06-16 | 1988-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-16 | 1992-06-16 | 1992-12-16 | $7700.00 | Window Closed / Lapsed |