Coating process and apparatus
Assignee: Cellophane SA France
•
Filing: 1979-02-21
•
Granted: 1980-12-09
•
Expires: 1999-02-21
Abstract
Abstract Films having widths of up to one meter or more can be coated at high coating speeds of up to 400 meters per minute or more with coating compositions having viscosities reaching up to 400 centipoises or more by arranging first and second guide rollers, a coating roller and rotating smoothing rod such that the path of travel of the film during the coating procedure is a substantially circular path whose diameter is preferably about one meter. During the coating procedure, the tension of the film by the first and second guide rollers is regulated independently of the speed at which the film travels. The apparatus and process have applicability to a wide range of films and coating compositions.
Inventors
- 👤 Jean-Pierre Pujol
- 👤 Jean Jugnet
- 👤 Claude Motta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 12:21
CPC Classifications
B; B05; B05D; B05D1/00; B05D1/28; B05C; B05C1/00; B05C1/04; B05C1/08; B05C1/12; D; D21; D21H; D21H23/00; D21H23/02; D21H23/22; D21H23/52; D21H23/56; D21H5/00; D21H5/0005; D21H5/0025; D21H5/003; B05D1/40; B05D2201/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
238 words
In a process for coating a flexible polyester film with a coating composition having a predetermined thickness, by the steps of: feeding the uncoated polyester film over a coating roller which deposits a layer of the coating compositions on a surface of the polyester film, the layer being thicker than the predetermined thickness, and feeding the coated polyester film over a rotating smoothing rod having a diameter less than the diameter of the coating roller to smooth out and reduce the thickness of the coating to the predetermined thickness, the improvement comprising feeding the polyester film, in at least its path of travel between the coating roller and rotating smoothing rod, over a substantially circular path of travel having a diameter between 0.5 and 1.5 meters, while maintaining the polyester film under tension during at least its travel in the substantially circular path, the tension being maintained independently of the speed of travel of the polyester film in the substantially circular path and passing the polyester film over the coating roller and over the rotating smoothing rod such that the angle that the polyester film makes with itself before and after passage over the coating roller and before and after passage over the rotating smoothing rod is between about 160° and about 163° with the proviso that the axes of the coating roller and rotating smoothing rod are in vertical planes which are at most 20 centimeters apart.
Claim 2
Dependent Claim
238 words
In a process for coating a flexible polyester film with a coating composition having a predetermined thickness, by the steps of: feeding the uncoated polyester film over a coating roller which deposits a layer of the coating compositions on a surface of the polyester film, the layer being thicker than the predetermined thickness, and feeding the coated polyester film over a rotating smoothing rod having a diameter less than the diameter of the coating roller to smooth out and reduce the thickness of the coating to the predetermined thickness, the improvement comprising feeding the polyester film, in at least its path of travel between the coating roller and rotating smoothing rod, over a substantially circular path of travel having a diameter between 0.5 and 1.5 meters, while maintaining the polyester film under tension during at least its travel in the substantially circular path, the tension being maintained independently of the speed of travel of the polyester film in the substantially circular path and passing the polyester film over the coating roller and over the rotating smoothing rod such that the angle that the polyester film makes with itself before and after passage over the coating roller and before and after passage over the rotating smoothing rod is between about 160° and about 163° with the proviso that the axes of the coating roller and rotating smoothing rod are in vertical planes which are at most 20 centimeters apart.
Claim 3
Dependent Claim
18 words
The process of claim 1 wherein the flexible polyester film has a width of at least 1 meter.
Claim 4
Dependent Claim
17 words
The process of claim 1 wherein the flexible polyester film has a width of about 2 meters.
Claim 5
Dependent Claim
31 words
The process of claim 1 wherein the speed of travel of the film in the substantially circular path ranges from about 10 meters per minute to about 400 meters per minute.
Claim 6
Dependent Claim
17 words
The process according to claim 4 wherein the speed of coating is about 300 meters per minute.
Claim 7
Dependent Claim
16 words
The process of claim 1 wherein the coating composition comprises an aqueous emulsion of polyvinylidene chloride.
References Cited (Backward Citations)
US1213728A
Cited
US1444217A
Cited
US2229620A
Cited
US2309090A
Cited
US2678284A
Cited
US3186861A
Cited
US3084663A
Cited
FR1475130A
Cited
US3338736A
Cited
US3844813A
Cited
US3751281A
Cited
US3941897A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-09 | 1984-06-09 | 1984-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-09 | 1988-06-09 | 1988-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-09 | 1992-06-09 | 1992-12-09 | $7700.00 | Window Closed / Lapsed |