Assignee: Toray Industries Inc
•
Filing: 1979-12-11
•
Granted: 1980-12-02
•
Expires: 1999-12-11
Abstract
Abstract Provided is a process for producing a carbon fabric composed of carbon fibers having improved tensile strength and modulus of elasticity from a precursor fabric made of an acrylonitrile polymer fiber. The acrylonitrile polymer fiber used has a fusing temperature of at least 310° C., contains not more than 0.1 wt. % of a residual solvent, and is prepared by a process wherein an acrylonitrile polymer comprised of at least 94 wt. % of acrylonitrile and not more than 6 wt. % of another comonomer and having an intrinsic viscosity of 1.4-2.3 is spun into filaments and then the filaments are stretched at a total stretching ratio of at least 6. The fiber of the fabric woven therefrom is treated with a transition metal-containing compound. The precursor fabric exhibits a free areal shrinkage of not more than 50% and has a weight per unit area falling within the specified range. The precursor fabric is heated in an oxidizing gas atmosphere at 200°-400° C. under conditions such that the fabric is permitted to shrink by at least 80% of the free areal shrinkage, and then, carbonized at at least 700° C. in a non-oxidizing atmosphere.
Inventors
- 👤 Toru Hiramatsu
- 👤 Ken-ichi Morita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:59
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/20; D01F9/21; D01F9/22
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
353 words
An improvement in a process for producing a carbon fiber wherein a precursor fabric of an acrylonitrile polymer fiber is heated in an oxidizing gas atmosphere maintained at a temperature of from 200° to 400° C., said gas being selected from the group consisting of air, nitric oxide, ozone and sulfur dioxide; and then, the fabric is carbonized in a non-oxidizing gas atmosphere maintained at a temperature of at least 700° C.; said acrylonitrile polymer being polyacrylonitrile or a copolymer comprised of, based on the weight of the copolymer, at least 94% by weight of acrylonitrile and not more than 6% by weight of at least one other copolymerizable monoethylenically unsaturated monomer; the improvement comprising: using, as the precursor fabric, a fabric (i) exhibiting a free areal shrinkage of no more than 50%, (ii) containing at least one transition metal or transition metal-containing compound selected from the group consisting of manganese, chromium, a manganese-containing compound and a chromium-containing compound, and (iii) being comprised of an acrylonitrile polymer fiber, which (a) has an intrinsic viscosity of from 1.4 to 2.3, (b) contains not more than 0.1%, based on the weight of the dry fiber, of a residual solvent, (c) has been drawn at a total drawing ratio of at least 6 based on its original length and (d) has a fusing temperature of at least 310° C.; and said fabric (iv) having a weight per unit area, satisfying the formula: ##EQU6## wherein E is weight per unit area (g/m 2 ) of the fabric, C is weave factor, D is average fineness in deniers, divided by 1000, of the bundle of fibers, used as the weft and warp for the formation of the fabric, S is areal shrinkage of the fabric represented by the equation: S=(S.sub.1 -S.sub.2)/S.sub.1 where S 1 and S 2 are areas of the fabric as determined before and after the oxidation and carbonization, respectively, and Y is carbonization yield; said improvement further comprising carrying out said heating of the precursor fabric under conditions such that the fabric is permitted to shrink by at least 80% of the free areal shrinkage.
Claim 2
Dependent Claim
353 words
An improvement in a process for producing a carbon fiber wherein a precursor fabric of an acrylonitrile polymer fiber is heated in an oxidizing gas atmosphere maintained at a temperature of from 200° to 400° C., said gas being selected from the group consisting of air, nitric oxide, ozone and sulfur dioxide; and then, the fabric is carbonized in a non-oxidizing gas atmosphere maintained at a temperature of at least 700° C.; said acrylonitrile polymer being polyacrylonitrile or a copolymer comprised of, based on the weight of the copolymer, at least 94% by weight of acrylonitrile and not more than 6% by weight of at least one other copolymerizable monoethylenically unsaturated monomer; the improvement comprising: using, as the precursor fabric, a fabric (i) exhibiting a free areal shrinkage of no more than 50%, (ii) containing at least one transition metal or transition metal-containing compound selected from the group consisting of manganese, chromium, a manganese-containing compound and a chromium-containing compound, and (iii) being comprised of an acrylonitrile polymer fiber, which (a) has an intrinsic viscosity of from 1.4 to 2.3, (b) contains not more than 0.1%, based on the weight of the dry fiber, of a residual solvent, (c) has been drawn at a total drawing ratio of at least 6 based on its original length and (d) has a fusing temperature of at least 310° C.; and said fabric (iv) having a weight per unit area, satisfying the formula: ##EQU6## wherein E is weight per unit area (g/m 2 ) of the fabric, C is weave factor, D is average fineness in deniers, divided by 1000, of the bundle of fibers, used as the weft and warp for the formation of the fabric, S is areal shrinkage of the fabric represented by the equation: S=(S.sub.1 -S.sub.2)/S.sub.1 where S 1 and S 2 are areas of the fabric as determined before and after the oxidation and carbonization, respectively, and Y is carbonization yield; said improvement further comprising carrying out said heating of the precursor fabric under conditions such that the fabric is permitted to shrink by at least 80% of the free areal shrinkage.
Claim 3
Dependent Claim
42 words
A process according to claim 1 wherein said copolymer is comprised of, based on the weight of the copolymer, at least 97% by weight of acrylonitrile and not more than 3% by weight of at least one other copolymerizable monoethylenically unsaturated monomer.
Claim 4
Dependent Claim
48 words
A process according to claim 1 wherein the amount of the transition metal or transition metal-containing compound contained in the fabric is approximately 0.2% to 1.5% by weight expressed in terms of the weight of the transition metal atom and based on the weight of the dry fabric.
Claim 5
Dependent Claim
35 words
A process according to claim 1 wherein said fabric containing the transition metal or transition metal-containing compound is prepared by treating an acrylonitrile polymer fiber or a fabric made therefrom with the transition metal-containing compound.
Claim 6
Dependent Claim
18 words
A process according to claim 4 wheren the transition metal-containing compound used for the treatment is potassium permanganate.
Claim 7
Dependent Claim
56 words
A process according to claim 4 wherein the acrylonitrile polymer fiber or the fabric made therefrom is immersed in an aqueous solution containing 0.5% to 10% by weight of the transition metal-containing compound and maintained at a temperature of 20° to 98° C., and thereafter, the so treated fiber or fabric is washed and then dried.
Claim 8
Dependent Claim
21 words
A process according to claim 1 wherein said acrylonitrile polymer fiber has a fusing temperature of from 315° to 380° C.
Claim 9
Dependent Claim
21 words
A process according to claim 1 wherein said acrylonitrile polymer fiber has a fusing temperature of from 320° to 350° C.
Claim 10
Dependent Claim
20 words
A process according to claim 1 wherein said precursor fabric exhibits a free areal shrinkage of not more than 45%.
Claim 11
Dependent Claim
27 words
A process according to claim 1 wherein the precursor fabric is heated in the oxidizing gas atmosphere maintained at a temperature of from 200° to 350° C.
Claim 12
Dependent Claim
27 words
A process according to claim 1, wherein the resultaing carbon fabric is composed of carbon fibers having a tensile strength of at least 240 kg/mm 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-02 | 1984-06-02 | 1984-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-02 | 1988-06-02 | 1988-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-02 | 1992-06-02 | 1992-12-02 | $7700.00 | Window Closed / Lapsed |