Nonleafing aluminum flake pigments

Claim 2

In a process for producing a substantially nonleafing aluminum flake by milling particulate aluminum to flake form in the presence of a milling agent, the improvement which comprises using a milling agent comprising isostearic acid.

Claim 3

A process according to claim 1 wherein said milling is performed in accordance with leaf-milling techniques.

Claim 4

A process according to claim 1, wherein the weight of isostearic acid present during milling is equal to between about 3% and about 7% of the weight of the aluminum present.

Claim 5

A process according to claim 1, wherein the milling agent further comprises an amount of another nonleafing milling agent effective to substantially eliminate residual leafing.

Claim 6

A process according to claim 4, wherein the weight of isostearic acid present during milling is equal to between about 3% and about 7% of the weight of aluminum present, and wherein the other nonleafing milling agent is an unsaturated fatty acid present during milling in a weight equal to between about 1.5% and about 3% of the weight of aluminum present.

Claim 7

A process according to claim 5, wherein the unsaturated fatty acid is oleic acid.

Claim 8

A process according to claim 2, wherein the leaf milling is performed in the presence of a liquid wet-milling vehicle.

Claim 9

A process according to claim 7, further including the step of removing the wet-milling vehicle from the flake pigment after leaf milling, to provide a dry powder pigment.

Claim 10

A process for producing a substantially nonleafing aluminum flake pigment from particulate aluminum comprising: milling the particulate aluminum to flake form in a ball mill in the presence of an amount of isostearic acid effective to act as a milling agent and an amount of an unsaturated fatty acid effective to substantially eliminate residual leafing and a liquid wet-milling vehicle for a time sufficient to provide aluminum flake pigment of desired particle size.

Claim 11

A process for producing a substantially nonleafing aluminum flake pigment from particulate aluminum comprising: milling the particulate aluminum to flake form in a ball mill in the presence of an amount of isostearic acid effective to act as a milling agent and an amount of an unsaturated fatty acid effective to substantially eliminate residual leafing and a liquid wet-milling vehicle for a time sufficient to provide aluminum flake pigment of desired particle size.

Claim 12

The process of claim 9 further comprising screening the aluminum flake pigment to recover a product of the desired particle size; and, removing the vehicle from the screened product to provide a dry powder pigment.

Claim 13

A process for producing a nonleafing aluminum pigment from particulate aluminum, comprising: wet-milling the particulate aluminum to flake form in the presence of a milling agent comprising about 3% to about 7% by weight of isostearic acid and about 1.5 to about 3% by weight of oleic acid, each based upon the aluminum content, and a liquid wet-milling vehicle to provide aluminum flake pigment; screening the flake pigment to recover a product of desired particle size; filtering the product to form a presscake; and adjusting the aluminum content of the presscake by adding mineral spirits until the aluminum content is within the range of about 60% to about 75% by weight of the presscake.

Claim 14

A process for producing a nonleafing aluminum pigment from particulate aluminum, comprising: wet-milling the particulate aluminum to flake form in the presence of a milling agent comprising about 3% to about 7% by weight of isostearic acid and about 1.5 to about 3% by weight of oleic acid, each based upon the aluminum content, and a liquid wet-milling vehicle to provide aluminum flake pigment; screening the flake pigment to recover a product of desired particle size; filtering the product to form a presscake; and adjusting the aluminum content of the presscake by adding mineral spirits until the aluminum content is within the range of about 60% to about 75% by weight of the presscake.

Claim 15

A substantially nonleafing aluminum flake pigment comprising aluminum flake particles having a surface layer comprising an isostearic acid milling agent residue.

Claim 16

A substantially nonleafing aluminum flake pigment comprising aluminum flake particles having a surface layer comprising an isostearic acid milling agent residue.

Claim 17

The pigment of claim 12, wherein said milling agent residue further comprises at least one other nonleafing milling agent residue in an amount effective to substantially eliminate residual leafing effects.

Claim 18

The pigment of claim 13, wherein said other milling agent residue is an oleic acid milling agent residue.

Claim 19

The pigment of claim 12, in the form of a dry powder.

Claim 20

The pigment of claim 12, in the form of a presscake containing a carrier liquid vehicle.

Claim 21

The pigment of claim 14, wherein said oleic acid milling agent residue is formed in the presence of a weight of oleic acid during milling which is not more than about 3% of the weight of aluminum present.

Claim 22

The pigment of claim 14 wherein said milling agent residue is formed in the presence of oleic acid and isostearic acid during milling in amounts respectively between about 1.5% and about 3% and between about 3% and about 7% of the weight of aluminum present.

Claim 23

A dry pigment powder produced by the process of claim 10.

Claim 24

A presscake produced by the process of claim 11.