Hard metal body
Assignee: Santrade Ltd
•
Filing: 1978-09-28
•
Granted: 1980-12-02
•
Expires: 1998-09-28
Abstract
Abstract A sintered hard metal body composed of at least one carbide as tungsten carbide and a binder phase consisting essentially of cobalt and/or nickel, the hard metal body being provided with a boronized surface zone having a thickness of 1-100 mu m characterized in that the hard metal contains small additions of up to about 5 percent by volume of the hard metal body of cubic carbides as VC, TiC, TaC, Mo2C, ZrC, NbC and/or Cr3C2, the content of binder phase is 6-40% of the volume of the body, and the mean grain size of the tungsten carbide is 0.2-1.5 mu m. The process of forming said body is also disclosed.
Inventors
- 👤 Leif S. Lindholm
- 👤 Jan N. Lindstrom
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:20
CPC Classifications
B; B23; B23B; B23B27/00; B23B27/14; B23B27/148; C; C23; C23C; C23C30/00; C23C30/005; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12056
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
106 words
A sintered hard metal body composed of at least one carbide as tungsten carbide and a binder phase consisting essentially of cobalt and/or nickel, the hard metal body being provided with a boronized surface zone having a thickness of 1-100 μm characterized in that the hard metal contains small additions of up to about 5 percent by volume of the hard metal body of cubic carbides as VC, TiC, TaC, Mo 2 C, ZrC, NbC and/or Cr 3 C 2 , the content of binder phase is 6-40% of the volume of the body, and the mean grain size of the tungsten carbide is 0.2-1.5 μm.
Claim 2
Dependent Claim
106 words
A sintered hard metal body composed of at least one carbide as tungsten carbide and a binder phase consisting essentially of cobalt and/or nickel, the hard metal body being provided with a boronized surface zone having a thickness of 1-100 μm characterized in that the hard metal contains small additions of up to about 5 percent by volume of the hard metal body of cubic carbides as VC, TiC, TaC, Mo 2 C, ZrC, NbC and/or Cr 3 C 2 , the content of binder phase is 6-40% of the volume of the body, and the mean grain size of the tungsten carbide is 0.2-1.5 μm.
Claim 3
Dependent Claim
25 words
The hard metal body of claim 1, wherein the content of the binder phase is from 8 to 20% of the volume of the body.
Claim 4
Dependent Claim
20 words
The hard metal body of claim 1, wherein the content of the binder phase is less than 15% by volume.
Claim 5
Dependent Claim
22 words
The hard metal body of claim 1, wherein the mean grain size of the tungsten carbide is from 0.2 to 1 μm.
Claim 6
Dependent Claim
22 words
The hard metal body of claim 4, wherein the mean grain size of the tungsten carbide is at the most 0.8 μm.
Claim 7
Dependent Claim
26 words
The hard metal body of claim 1, wherein the additional carbide is present in an amount of at least 0.1% of the volume of the body.
Claim 8
Dependent Claim
20 words
The hard metal body of claim 6, wherein the additional carbide is present in an amount of at least 0.2%.
Claim 9
Dependent Claim
26 words
The hard metal body of claim 1, wherein the additional carbide is present in an amount of at the most 1/4 of the binder phase content.
Claim 10
Dependent Claim
29 words
The hard metal body of claim 8, wherein the additional carbides are present in an amount of from about 0.3 to 5.0% by volume of the hard metal body.
Claim 11
Dependent Claim
159 words
A process for boronizing the surface of a cemented carbide body, the said body containing at least one carbide as tungsten carbide, from 6 to 40% by volume of the body of a binder phase consisting essentially of cobalt and/or nickel, and small additions of up to about 5 percent by volume of the hard metal body of cubic carbides as VC, TiC, TaC, Mo 2 C, ZrC, NbC and/or Cr 3 C 2 , the mean grain size of the tungsten carbide being 0.2 to 1.5 μm, comprising contacting the said cemented carbide body at a temperature of from about 750° to 1000° C. with a first gaseous mixture of a boron trihalide and a hydrogen halide, to form a thin boronized layer on said body and thereafter increasing the amount of the hydrogen halide to form a second gaseous mixture to complete boronizing of said hard metal body to a thickness of from 1 to 100 μm.
Claim 12
Dependent Claim
159 words
A process for boronizing the surface of a cemented carbide body, the said body containing at least one carbide as tungsten carbide, from 6 to 40% by volume of the body of a binder phase consisting essentially of cobalt and/or nickel, and small additions of up to about 5 percent by volume of the hard metal body of cubic carbides as VC, TiC, TaC, Mo 2 C, ZrC, NbC and/or Cr 3 C 2 , the mean grain size of the tungsten carbide being 0.2 to 1.5 μm, comprising contacting the said cemented carbide body at a temperature of from about 750° to 1000° C. with a first gaseous mixture of a boron trihalide and a hydrogen halide, to form a thin boronized layer on said body and thereafter increasing the amount of the hydrogen halide to form a second gaseous mixture to complete boronizing of said hard metal body to a thickness of from 1 to 100 μm.
Claim 13
Dependent Claim
28 words
The process of claim 10, wherein the first mixture contains from 1/2 to 2 percent hydrogen halide and the second mixture contains 2 to 5 percent hydrogen halide.
Claim 14
Dependent Claim
14 words
The process of claim 10, wherein the temperature is from 850° to 925° C.
References Cited (Backward Citations)
US3647576A
Cited
US3999954A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-02 | 1984-06-02 | 1984-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-02 | 1988-06-02 | 1988-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-02 | 1992-06-02 | 1992-12-02 | $7700.00 | Window Closed / Lapsed |