Assignee: Stollberg Inc
•
Filing: 1979-04-04
•
Granted: 1980-11-25
•
Expires: 1999-04-04
Abstract
Abstract A particulate slagging composition for the extended optimum continuous casting of a steel which tends to evolve alumina into the molten protective layer of said composition maintained on the top of a pool of molten steel. Such particulate slagging composition is characterized by a R' ratio (the sum of the theoretical net oxide analysis values of CaO+MgO+BaO+SrO+MnO+FeO+F+B2O3 to the theoretical net oxide analysis value of SiO2) preselected for obtaining Opertional ADK values not substantially in excess of about 750 seconds after substantial absorption of alumina from the steel.
Inventors
- 👤 Joseph F. Uher
- 👤 Charles M. Loane, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:55
CPC Classifications
B; B22; B22D; B22D11/00; B22D11/10; B22D11/11
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
218 words
Particulate slagging composition for the continuous casting of steel, said steel tending to evolve alumina into said composition when said composition is in molten condition during its use in the continuous casting operation, said slagging composition being characterized by flowidity of about 4 to 16 inches, fusion range not substantially above 2300° F., a Start-up ADK value not exceeding 500 seconds, said composition further characterized by having theoretical net oxide analysis values within the following ranges wherein the percentages are weight percentages and are selected to total 100%: ______________________________________
Fluxing Ingredients Wt. %
______________________________________
CaO* 0-42
MgO* 0-20
BaO* 0-20
SrO* 0-20
MnO* 0-20
FeO* 0-18
F* (elemental component
of the fluorine-
providing materials) 4-16
B.sub.2 O.sub.3 * 0-15
Na.sub.2 O 1-25
K.sub.2 O 0-5
Li.sub.2 O 0-5
V.sub.2 O.sub.5 0-1
NiO 0-2
CuO 0-2
ZnO 0-1
TiO.sub.2 0-5
ZrO.sub.2 0-3
CoO 0-2
Cr.sub.2 O.sub.3 0-2
MoO.sub.3 0-1
Glass Network Formers
SiO.sub.2 20-40
Al.sub.2 O.sub.3 0-12
P.sub.2 O.sub.5 0-10
B.sub.2 O.sub.3 included above;
______________________________________ the ratio of the sum of the theoretical net oxide analysis values of the starred (*) fluxing ingredients to the theoretical net oxide analysis value of SiO 2 (this ratio being termed the R' ratio) being preselected between 1.5:1 and 3:1 for obtaining an Operational ADK value not substantially in excess of 750 seconds.
Claim 2
Dependent Claim
218 words
Particulate slagging composition for the continuous casting of steel, said steel tending to evolve alumina into said composition when said composition is in molten condition during its use in the continuous casting operation, said slagging composition being characterized by flowidity of about 4 to 16 inches, fusion range not substantially above 2300° F., a Start-up ADK value not exceeding 500 seconds, said composition further characterized by having theoretical net oxide analysis values within the following ranges wherein the percentages are weight percentages and are selected to total 100%: ______________________________________
Fluxing Ingredients Wt. %
______________________________________
CaO* 0-42
MgO* 0-20
BaO* 0-20
SrO* 0-20
MnO* 0-20
FeO* 0-18
F* (elemental component
of the fluorine-
providing materials) 4-16
B.sub.2 O.sub.3 * 0-15
Na.sub.2 O 1-25
K.sub.2 O 0-5
Li.sub.2 O 0-5
V.sub.2 O.sub.5 0-1
NiO 0-2
CuO 0-2
ZnO 0-1
TiO.sub.2 0-5
ZrO.sub.2 0-3
CoO 0-2
Cr.sub.2 O.sub.3 0-2
MoO.sub.3 0-1
Glass Network Formers
SiO.sub.2 20-40
Al.sub.2 O.sub.3 0-12
P.sub.2 O.sub.5 0-10
B.sub.2 O.sub.3 included above;
______________________________________ the ratio of the sum of the theoretical net oxide analysis values of the starred (*) fluxing ingredients to the theoretical net oxide analysis value of SiO 2 (this ratio being termed the R' ratio) being preselected between 1.5:1 and 3:1 for obtaining an Operational ADK value not substantially in excess of 750 seconds.
Claim 3
Dependent Claim
62 words
the particulate slagging composition of claim 1 wherein said ratio (R') is approximated by substituting therefor the ratio of the sum of the theoretical net oxide analysis values of the alkaline earth metal oxides plus FeO and MnO to the theoretical net oxide analysis value of silica (this ratio being termed the "R" ratio), said R ratio being between 0.8:1 and 2.5:1.
Claim 4
Dependent Claim
112 words
The composition of claim 1 wherein the theoretical net oxide analysis values are used to solve the equation below, the ratio of K 2 O to Na 2 O oxide analysis values is 1:8, the sum of Na 2 O and K 2 O oxide analysis values is represented in the equation as X 2 O, the solution of said equation substantially predicts the Start-up ADK value of said composition, and the F, B 2 O 3 , Cao, X 2 O, and SiO 2 oxide analysis values are selected to minimize said start-up ADK value in accordance with said equation, said equation being: ADK=1.894+(-76.16)(F)+(-15.58)(B.sub.2 O.sub.3)+(-12.77)(CaO)+(12.34)(SiO.sub.2)+(-2.562)(B.sub.2 O.sub.3)(X.sub.2 O)+(2.3335)(B.sub.2 O.sub.3).sup.2 +(-6.033)(F)(X.sub.2 O)+(4.073)(F)(B.sub.2 O.sub.3)+(7.872)(F).sup.2.
Claim 5
Dependent Claim
11 words
The particulate slagging composition of claim 1 which is a vitrifaction.
Claim 6
Dependent Claim
11 words
The particulate slagging composition of claim 1 which is partially vitreous.
Claim 7
Dependent Claim
36 words
The composition of claim 5 which contains fluorine, there being not more than about 5% fluorine in the vitreous portion of said composition and the remainder being in the form of unvitrified particles of fluorine-providing material.
Claim 8
Dependent Claim
22 words
The particulate slagging composition of claim 1 which has been intimately blended to form a mold powder, but has not been vitrified.
Claim 9
Dependent Claim
18 words
The particulate slagging composition of claim 1 wherein there is admixed about 1-10% of finely divided carbon particles.
Claim 10
Dependent Claim
36 words
The particulate slagging composition of claim 1 wherein after said addition of extra alumina has been dissolved into said composition, the flowidity value increases and the Operational ADK value is less than the Start-up ADK value.
Claim 11
Dependent Claim
10 words
The particulate slagging composition of claim 1 containing no alumina.
Claim 12
Dependent Claim
51 words
In a process for the continuous casting of steel wherein a pool of molten steel is maintained in the upper end of an open-ended continuous casting mold, the improvement which comprises establishing and maintaining on the top of said pool a protective layer of the particulate slagging composition of claim 1.
Claim 13
Dependent Claim
50 words
In a process for the continuous casting of a steel wherein a pool of molten steel is maintained in the upper end of an open-ended continuous casting mold, the improvement which comprises establishing and maintaining on the top of said pool a protective layer of the composition of claim 8.
Claim 14
Dependent Claim
57 words
The particulate slagging composition of claim 1 which has the following theoretical net oxide analysis values in weight percent: 6.0 Na 2 O, 35.1 CaO, 14.0 F (elemental component of the fluorine-providing materials), 21.4 SiO 2 , 8.2 Al 2 O 3 , 5.0 MgO, 1.6 K 2 O, 3.8 FeO, 4.7 B 2 O 3 .
Claim 15
Dependent Claim
45 words
The particulate slagging composition of claim 1 which has the following theoretical net oxide analysis values in weight percent: 1.7 Na 2 O, 41.6 CaO, 4.8 F (elemental component of the fluorine-providing materials), 37.7 SiO 2 , 9.9 FeO, 3.8 B 2 O 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-25 | 1984-05-26 | 1984-11-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-25 | 1988-05-26 | 1988-11-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-25 | 1992-05-26 | 1992-11-25 | $7700.00 | Window Closed / Lapsed |