US4234550A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for treating a particulate nuclear fuel material
Assignee: General Electric Co
•
Filing: 1976-11-08
•
Granted: 1980-11-18
•
Expires: 1996-11-08
Abstract
Abstract A process for treating a particulate uranium oxide composition containing ammonium diuranate precursors such as uranyl fluoride and uranyl nitrate, along with possible impurities, is disclosed. The process comprises the steps of (a) contacting the composition with a sufficient amount of an ammonium hydroxide solution to convert the ammonium diuranate precursors to ammonium diuranate, and (b) heating the composition under a controlled atmosphere at a temperature sufficient to dry the composition, sublime any ammonium fluoride present, and convert the ammonium diuranate to uranium dioxide. In a first modification of the invention, there is practiced the additional step of moving the composition, preferably by mechanically agitating the composition, prior to the heating step, or during the heating step, or both prior to and during the heating step, for a sufficient time to produce rounded agglomerates in the form of a readily flowable powder. In another modification of the invention, there are practiced the additional steps of mechanically agitating the composition and screening the composition prior to heating. These additional steps produce rounded agglomerates of the composition in a desired size distribution.
Inventors
- 👤 William R. DeHollander
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 00:53
CPC Classifications
C; C01; C01G; C01G43/00; C01G43/01; C01G43/025; C01P; C01P2004/00; C01P2004/30; C01P2004/32; C01P2004/50; C01P2006/00; C01P2006/10
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
131 words
A method of treating a particulate uranium oxide composition containing from about 3 to about 15 percent by weight of an ammonium diuranate precursor, with or without fluoride impurities, comprising the steps of (a) contacting said composition with a sufficient amount of an ammonium hydroxide solution to convert said precursor to ammonium diuranate, convert any fluoride compounds to ammonium fluoride, and form a treated composition containing solid agglomerates, and (b) heating the treated composition under a controlled atmosphere at a temperature of from about 300° C. to about 700° C., said temperature being sufficient to dry the agglomerates, sublime any ammonium fluoride, and convert the ammonium diuranate to uranium dioxide yielding a particulate composition comprised substantially of uranium dioxide, said composition being capable of compaction into unsintered structures of increased strength.
Claim 2
Independent Claim
131 words
A method of treating a particulate uranium oxide composition containing from about 3 to about 15 percent by weight of an ammonium diuranate precursor, with or without fluoride impurities, comprising the steps of (a) contacting said composition with a sufficient amount of an ammonium hydroxide solution to convert said precursor to ammonium diuranate, convert any fluoride compounds to ammonium fluoride, and form a treated composition containing solid agglomerates, and (b) heating the treated composition under a controlled atmosphere at a temperature of from about 300° C. to about 700° C., said temperature being sufficient to dry the agglomerates, sublime any ammonium fluoride, and convert the ammonium diuranate to uranium dioxide yielding a particulate composition comprised substantially of uranium dioxide, said composition being capable of compaction into unsintered structures of increased strength.
Claim 3
Dependent Claim
35 words
A method according to claim 1 in combination with the step of mechanically agitating the agglomerates from step (a) for a sufficient period of time to produce rounding of the agglomerates and a flowable composition.
Claim 4
Dependent Claim
23 words
A method according to claim 2 in which the agitating step is accomplished by tumbling the agglomerates in a horizontal cylindrical mixing vessel.
Claim 5
Dependent Claim
17 words
A method according to claim 2 in which the agitating step is performed during the heating step.
Claim 6
Dependent Claim
20 words
A method according to claim 2 in which the agitating step is performed prior to and during the heating step.
Claim 7
Dependent Claim
18 words
A method according to claim 2 in which the agitating step is performed prior to the heating step.
Claim 8
Dependent Claim
52 words
A method according to claim 1 in combination with the steps of mechanically agitating the agglomerates of step (a) for a sufficient period of time to produce rounding of the agglomerates giving a flowable composition and screening the agglomerates to a size in the range of about -20 to about +100 mesh.
Claim 9
Dependent Claim
25 words
A method according to claim 1 in which the particulate uranium oxide composition is comprised of uranium dioxide and the precursor is a fluoride compound.
Claim 10
Dependent Claim
13 words
A method according to claim 8 in which the precursor is uranyl fluoride.
Claim 11
Dependent Claim
13 words
A method according to claim 1 in which the precursor is uranyl nitrate.
Claim 12
Dependent Claim
29 words
A method according to claim 1 in which the contacting step (a) is accomplished by adding the ammonium hydroxide to the uranium oxide composition during mixing of the composition.
Claim 13
Dependent Claim
20 words
A method according to claim 1 in which the heating step is conducted in an atmosphere comprised of wet hydrogen.
Claim 14
Dependent Claim
25 words
A method according to claim 1 in which the heating step is conducted in an atmosphere comprised of a mixture of hydrogen and carbon dioxide.
Claim 15
Dependent Claim
19 words
A method according to claim 1 in which the composition is added to the ammonium hydroxide solution during mixing.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-18 | 1984-05-19 | 1984-11-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-18 | 1988-05-19 | 1988-11-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-18 | 1992-05-19 | 1992-11-18 | $7700.00 | Window Closed / Lapsed |