Method for the manufacture of thin-walled shaped articles of crystalline thermoplastic material
Assignee: Bellaplast Maschinenbau GmbH
•
Filing: 1978-09-27
•
Granted: 1980-11-18
•
Expires: 1998-09-27
Abstract
Abstract A method of manufacturing thin-walled articles by thermoforming from crystalline thermoplastic sheet or web material wherein the sheet or web is rapidly precooled from extrusion temperature, and the outer surface layers reheated prior to thermoforming.
Inventors
- 👤 Alfons W. Thiel
- 👤 Barbara Geppert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 01:06
CPC Classifications
B; B29; B29C; B29C51/00; B29C51/26; B29C51/42; B29C51/421; B29C51/422; B29C51/423; B29C48/00; B29C48/03; B29C48/07; B29C48/08; B29C48/25; B29C48/88; B29C48/885; B29C48/90; B29C48/908; B29C48/91; B29C48/911; B29C48/9135; B29C48/914; B29C48/919
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
236 words
A method for manufacturing thin-walled articles from crystalline thermoplastic material by thermoforming the articles in a web or sheet of said thermoplastic material and removing the shaped articles from said web or sheet, said thermoplastic material having a critical crystalline melting temperature range with a lower limit temperature T C and an upper limit temperature T M and said method further including temperature conditioning of said web or sheet for thermoforming, characterized in that said temperature conditioning involves at least two steps; namely: (a) developing by heating and/or cooling a preliminary temperature profile across the thickness of said web or sheet in which the core material of the web or sheet is at a temperature close to but lower than the critical crystalline melting temperature range of the said crystalline thermoplastic material and wherein said core is elastically deformable and the outer surface regions of the web or sheet are at lower temperatures than the core material and not thermally formable; and (b) developing a final temperature profile for the thermoforming step by reheating one or both of said outer surface regions of said web or sheet to a temperature within said critical crystalline melting range whereby the said crystalline thermoplastic material of the outer surface regions becomes elastically deformable, whereas the said core material is retained in an elastically deformable state at a temperature adjacent to but lower than said critical crystalline melting temperature range.
Claim 2
Independent Claim
236 words
A method for manufacturing thin-walled articles from crystalline thermoplastic material by thermoforming the articles in a web or sheet of said thermoplastic material and removing the shaped articles from said web or sheet, said thermoplastic material having a critical crystalline melting temperature range with a lower limit temperature T C and an upper limit temperature T M and said method further including temperature conditioning of said web or sheet for thermoforming, characterized in that said temperature conditioning involves at least two steps; namely: (a) developing by heating and/or cooling a preliminary temperature profile across the thickness of said web or sheet in which the core material of the web or sheet is at a temperature close to but lower than the critical crystalline melting temperature range of the said crystalline thermoplastic material and wherein said core is elastically deformable and the outer surface regions of the web or sheet are at lower temperatures than the core material and not thermally formable; and (b) developing a final temperature profile for the thermoforming step by reheating one or both of said outer surface regions of said web or sheet to a temperature within said critical crystalline melting range whereby the said crystalline thermoplastic material of the outer surface regions becomes elastically deformable, whereas the said core material is retained in an elastically deformable state at a temperature adjacent to but lower than said critical crystalline melting temperature range.
Claim 3
Dependent Claim
50 words
A method defined in claim 1, wherein at least one of the said outer surface regions of said web is reheated to a temperature adjacent to but lower than the crystalline melting point temperature T M at the upper limit of the critical crystalline melting range of the said material.
Claim 4
Dependent Claim
51 words
A method defined in claim 1, wherein at least one of said outer surface regions of said web is reheated to a temperature higher than the upper limit temperature T M of said crystalline melting point range to heat said outer surface regions of said web into a plastically deformable state.
Claim 5
Dependent Claim
116 words
The method as defined in claim 1, wherein developing the said preliminary temperature profile includes heating by external means a web or sheet of said crystalline thermoplastic material until the core material reaches a temperature close to but lower than said lower limit T C of said critical crystalline melting range, even though the outer surface regions of said web or sheet may reach temperatures within or higher than said critical melting temperature range; and then rapidly cooling said outer surface regions of said web or sheet down through said critical melting temperature range to a temperature lower than that of the inner core material while essentially controlling growth of crystals within said outer surface regions.
Claim 6
Dependent Claim
213 words
A method defined in claim 1, characterized by the substantially uninterrupted sequence of steps comprising: (a) extruding a web or said thermoplastic material at a temperature above the crystalline melting point temperature T M at the upper limit of the critical melting temperature range of said material; (b) substantially immediately rapidly precooling at the opposite surfaces of said web in a manner and so much that the core material of said web is cooled down to a temperature adjacent to but lower than the critical crystalline melting temperature range of the said crystalline thermoplastic material at a predetermined cooling rate to control growth of crystals in the material in said surface regions and in the said core material of the said web, said outer surface regions being cooled until they are not thermally formable; (c) allowing said outer surface regions of said web to be partially reheated by heat conducted thereto from the warmer core and adding sufficient external heat that said outer surface regions become at least elastically deformable at a temperature adjacent to but lower than said critical crystalline melting temperature range; and (d) then thermally forming and cooling said web to shape the desired article while continuing to essentially control growth of crystals within said material during said thermally forming.
Claim 7
Dependent Claim
35 words
The method defined in claim 5, wherein said rapid precooling at the opposite surfaces of said web is such that further growth of crystals in the outer surface regions of the web is essentially avoided.
Claim 8
Dependent Claim
43 words
The method defined in claim 5, wherein said rapid precooling at the opposite surfaces of said web is such that further growth of crystals in said outer surface regions and in the said inner core region material of said web is essentially avoided.
Claim 9
Dependent Claim
34 words
The method defined in claim 5, wherein said rapid precooling at the opposite surfaces of said web is produced by contact of said surfaces with a fluent cooling medium held at a predetermined temperature.
Claim 10
Dependent Claim
75 words
The method defined in claim 1, wherein a sheet or web is subjected to a forming tool operation for thermal forming, in which tool the said inner core layer is shaped by elastic deformation under stretching and stabilized by final cooling of the article wall, whereas the reheated outer layers are distributed and plastically deformed over said core in plasticized or fluid state so to produce outer layers of the articles free of crystal orientation.
Claim 11
Dependent Claim
90 words
The method defined in claim 1, wherein the said crystalline thermoplastic material is an isotactic polypropylene having a crystalline melting temperature range between 160° C. and 168° C., the web or sheet is formed initially by extrusion at an extrusion temperature within the range of 220° C. to 270° C., and the web or sheet entering the shaping tool operation has a core temperature in the range of 130° C. to 160° C. and a temperature at its outer surface regions in the range of 140° C. to 168° C.
Claim 12
Dependent Claim
117 words
The method defined in claim 1, wherein the said crystalline thermoplastic material is an isotactic polypropylene having a crystalline melting temperature range between 160° C. and 168° C., the web or sheet is formed initially by extrusion at an extrusion temperature within the range of 220° C. to 270° C., and the web entering the shaping tool operation has a core temperature in the range of 130° C. to 160° C. with one of the outer surface regions of said web or sheet having a temperature in the range of 140° C. to 168° C. and the other surface layer of the web or sheet having a temperature in the range of 168° F. to 270° C.
Claim 13
Dependent Claim
90 words
The method defined in claim 1, wherein said crystalline thermoplastic material is an isotactic polypropylene having a crystalline melting temperature range between 160° C. and 168° C., the said web or sheet is formed initially by extrusion at an extrusion temperature within the range of 220° C. to 270° C., and the web or sheet entering the shaping tool operation has a core temperature in the range of 130° C. to 160° C. and a temperature at its outer surface regions in the range of 168° C. to 270° C.
Claim 14
Dependent Claim
47 words
The method as defined in claim 1, wherein the said crystalline thermoplastic material is a low pressure produced oplyethylene having a density of 0,945 to 0,965 g/m 3 , a crystallinity of 75% to 95% and a crystalline melting temperature range between 130° C. to 135° C.
Claim 15
Dependent Claim
21 words
The method defined in claim 1, wherein the said crystalline thermoplastic material is a random copolymerisation product of ethylene and propylene.
Claim 16
Dependent Claim
21 words
The method defined in claim 1, wherein the said crystalline thermoplastic material is a block copolymerisation product of ethylene and propylene.
Claim 17
Dependent Claim
45 words
The method defined in claim 1, wherein one surface of the article wall is cooled during thermoforming by contact with a cooled thermoforming tool and at the other wall surface is cooled by a fluent cooling medium directed into contact with said other wall surface.
Claim 18
Dependent Claim
33 words
The method defined in claim 16, wherein said cooling of the other article wall during the said thermoforming is obtained by powdered dry ice blown into contact with the said outer wall surface.
Claim 19
Dependent Claim
38 words
A method for manufacturing thin-walled articles from thermoplastic sheet or web material according to claim 1, wherein the web or sheet after being developed to its final temperature profile and prior to thermoforming is subjected to biaxial stretching.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-18 | 1984-05-19 | 1984-11-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-18 | 1988-05-19 | 1988-11-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-18 | 1992-05-19 | 1992-11-18 | $7700.00 | Window Closed / Lapsed |