High strength modified asphalt paving composition
Assignee: CHEMKRETE TECHNOLOGIES Inc
•
Filing: 1978-11-24
•
Granted: 1980-11-18
•
Expires: 1998-11-24
Abstract
Abstract A paving composition formed of aggregate mixed with substantially unblown asphalt cement (neither emulsified nor cut-back) including a soluble organic-manganese compound either alone or in combination with organic-cobalt or organic-copper compounds for improved strength. The composition is employed for paving roads by conventional techniques.
Inventors
- 👤 Laurence Latta, Jr.
- 👤 John B. Leonard, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:09
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/09; C08K5/098; Y; Y02; Y02A; Y02A30/00; Y02A30/30
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
110 words
A paving composition comprising at least 85 percent by weight aggregate, substantially unblown and unoxidized asphalt cement which is neither cut-back nor emulsified and which has bitumens as its predominant constitutent, and a strength improving agent comprising an organic manganese compound, either alone or in combination with organic-cobalt or organic-copper compounds, said strength improving agent being present in a form sufficient to make it substantially soluble in said asphalt cement and in an amount sufficient to provide manganese, manganese and cobalt or manganese and copper ion concentrations, based upon the total weight of said ions, in the range of about 0.01 to 0.50 percent by weight of said asphalt cement.
Claim 2
Dependent Claim
110 words
A paving composition comprising at least 85 percent by weight aggregate, substantially unblown and unoxidized asphalt cement which is neither cut-back nor emulsified and which has bitumens as its predominant constitutent, and a strength improving agent comprising an organic manganese compound, either alone or in combination with organic-cobalt or organic-copper compounds, said strength improving agent being present in a form sufficient to make it substantially soluble in said asphalt cement and in an amount sufficient to provide manganese, manganese and cobalt or manganese and copper ion concentrations, based upon the total weight of said ions, in the range of about 0.01 to 0.50 percent by weight of said asphalt cement.
Claim 3
Dependent Claim
38 words
The paving composition of claim 1 in which said asphalt cement is further characterized by a penetration of less than about 400 measured at 25° C. and a viscosity at 60° C. of more than about 65 poise.
Claim 4
Dependent Claim
25 words
The paving composition of claim 1 in which the concentration of aggregate is between about 90 and 98 percent by weight of said paving composition.
Claim 5
Dependent Claim
56 words
The paving composition of claim 1 in which said strength improving agent is an organic-manganese compound present in a form capable of providing substantially soluble manganese ions in said asphalt cement and in an amount sufficient to provide manganese ion concentrations in the range of about 0.01 to 0.50 percent by weight of said asphalt cement.
Claim 6
Dependent Claim
26 words
The paving composition of claim 4 in which the concentration of manganese ions is between about 0.05 and 0.20 percent by weight of said asphalt cement.
Claim 7
Dependent Claim
17 words
The paving composition of claim 4 in which said strength improving agent also includes an organic-cobalt compound.
Claim 8
Dependent Claim
28 words
The paving composition of claim 6 in which said organic-cobalt compound is present in the amount of about 0.001 to 0.2 percent by weight of said asphalt cement.
Claim 9
Dependent Claim
35 words
The paving composition of claim 1 in which the anion for the organic-manganese, organic-cobalt and organic-copper compounds are derived from an organic compound selected from the group consisting of carboxylic acids, ketones, sulfonates and phosphates.
Claim 10
Dependent Claim
16 words
The paving composition of claim 8 in which said anion is derived from a carboxylic acid.
Claim 11
Dependent Claim
24 words
The paving composition of claim 9 in which said anion is derived from a carboxylic acid having between about 1 and 30 carbon atoms.
Claim 12
Dependent Claim
79 words
A strength improving agent for a paving composition that includes at least 85 percent by weight aggregate and substantially unblown asphalt cement which is neither cut-back nor emulsified, said agent comprising organic-manganese either alone or in combination with an organic-cobalt compound, uniformly dissolved in said asphalt cement and present in an amount sufficient to provide a concentration of manganese or manganese and cobalt ions in the range of about 0.01 and 0.5 percent by weight of said asphalt cement.
Claim 13
Dependent Claim
79 words
A strength improving agent for a paving composition that includes at least 85 percent by weight aggregate and substantially unblown asphalt cement which is neither cut-back nor emulsified, said agent comprising organic-manganese either alone or in combination with an organic-cobalt compound, uniformly dissolved in said asphalt cement and present in an amount sufficient to provide a concentration of manganese or manganese and cobalt ions in the range of about 0.01 and 0.5 percent by weight of said asphalt cement.
Claim 14
Dependent Claim
49 words
The strength improving agent of claim 11 wherein said organic-manganese compound is present in the amount of about 0.08 to 0.12 percent by weight of said asphalt cement and said organic-cobalt compound is present in the amount of about 0.001 to 0.2 percent by weight of said asphalt cement.
Claim 15
Dependent Claim
36 words
The strength improving agent of claim 12 in which said organic-manganese compound is selected from the group consisting of manganese napthenate, manganese acetate, manganese acetyl acetonate, and manganese octoate, and said organic-cobalt compound is cobalt naphthenate.
Claim 16
Independent Claim
121 words
A method of forming a paving composition comprising the steps of: (a) dissolving at an elevated temperature a paving composition strength improving agent in substantially unblown fluid asphalt cement which is neither emulsified nor cut-back, said strength improving agent comprising an organic-manganese compound either alone or in combination with organic-cobalt or organic-copper compounds, said agent being present in a form soluble in the asphalt cement, the combined concentrations of said manganese, manganese and cobalt and manganese and copper ions comprising about 0.01 to 0.5 percent weight of said asphalt cement, and (b) mixing said manganese, manganese and cobalt or manganese and copper ion-containing asphalt with at least 85 weight percent of aggregate at an elevated temperature to form a paving composition.
Claim 17
Independent Claim
121 words
A method of forming a paving composition comprising the steps of: (a) dissolving at an elevated temperature a paving composition strength improving agent in substantially unblown fluid asphalt cement which is neither emulsified nor cut-back, said strength improving agent comprising an organic-manganese compound either alone or in combination with organic-cobalt or organic-copper compounds, said agent being present in a form soluble in the asphalt cement, the combined concentrations of said manganese, manganese and cobalt and manganese and copper ions comprising about 0.01 to 0.5 percent weight of said asphalt cement, and (b) mixing said manganese, manganese and cobalt or manganese and copper ion-containing asphalt with at least 85 weight percent of aggregate at an elevated temperature to form a paving composition.
Claim 18
Dependent Claim
18 words
The method of claim 14 in which said elevated temperature of step (b) is at least 100° C.
Claim 19
Dependent Claim
27 words
The method of claim 14 in which the anion is derived from an organic compound selected from the group consisting of carboxylic acids, ketones, sulfonates and phosphates.
Claim 20
Dependent Claim
18 words
The method of claim 14 in which the anion of said organic-metal compound is derived from carboxylic acid.
Claim 21
Dependent Claim
36 words
The method of claim 14 in which said asphalt cement is characterized by a penetration of less than about 400 measured at 25° C. and a viscosity at 60° C. of more than about 65 poise.
Claim 22
Dependent Claim
59 words
The method of claim 14 in which said strength improving agent is the combination of organic-manganese and organic-cobalt compounds, wherein the concentration of said organic-cobalt compound is between about 0.001 and 0.2 percent by weight of said asphalt cement, and the concentration of said organic-manganese compound is between about 0.05 and 0.20 percent by weight of said asphalt cement.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-18 | 1984-05-19 | 1984-11-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-18 | 1988-05-19 | 1988-11-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-18 | 1992-05-19 | 1992-11-18 | $7700.00 | Window Closed / Lapsed |