Electrodialysis membranes of high interstitial molality based upon methacrylate ester derivatives
Assignee: Veolia WTS Systems USA Inc
•
Filing: 1979-03-02
•
Granted: 1980-11-04
•
Expires: 1999-03-02
Abstract
Abstract This invention relates to cross-linked copolymers of methacrylate esters containing ionogenic functional groups capable of being converted into high efficiency electro-dialysis membranes. Such totally aliphatic polymer membranes have been found to give electrical resistances which can be as low as one half that of membranes previously synthesized as well as higher interstitial molality. This reduced resistance, in concert with a high degree of chemical and physical stability enables water desalination by electrodialysis to be performed over longer periods of useful membrane life and at a lower expenditure of electrical energy per thousand gallons of water desalted.
Inventors
- 👤 Russell B. Hodgdon
- 👤 Samuel S. Alexander
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:59
CPC Classifications
B; B01; B01D; B01D61/00; B01D61/42; B01D61/44; B01D61/46; B01D61/48; B01D71/00; B01D71/06; B01D71/48; B01D71/52; B01D71/521; B01D71/5211; C; C08; C08J; C08J5/00; C08J5/20; C08J5/22; C08J5/2206; C08J5/2218; C08J5/2231; C08J2333/00; C08J2333/04; C08J2333/06; C08J2333/10; C08J2333/12; Y; Y02; Y02A; Y02A20/00; Y02A20/124
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
141 words
An ion exchange resin membrane consisting of a copolymer of about 35 to about 50 mol percent of at least one compound selected from the group consisting of ethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, polyethylene glycol dimethacrylate, trimethylol propane trimethacrylate, bis-phenol A dimethacrylate, pentaerythritol trimethacrylate and pentaerythritol tetramethacrylate with about 65 to about 50 mol percent respectively of a methacrylate ester salt having the chemical formula: ##STR6## where R is an ion exchange moeity selected from the group consisting of quaternary ammonium salts and sulfonic acid salts, said copolymer having an interstitial ion exchange molality of at least about 2.2 gram equivalents of ion exchange capacity per kilogram of water content, said membrane having a resistivity as measured at 1000 Hertz in equilibrium with 0.01 N sodium chloride solution at room temperature of less than about 30 ohm cm. 2 .
Claim 2
Dependent Claim
141 words
An ion exchange resin membrane consisting of a copolymer of about 35 to about 50 mol percent of at least one compound selected from the group consisting of ethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, polyethylene glycol dimethacrylate, trimethylol propane trimethacrylate, bis-phenol A dimethacrylate, pentaerythritol trimethacrylate and pentaerythritol tetramethacrylate with about 65 to about 50 mol percent respectively of a methacrylate ester salt having the chemical formula: ##STR6## where R is an ion exchange moeity selected from the group consisting of quaternary ammonium salts and sulfonic acid salts, said copolymer having an interstitial ion exchange molality of at least about 2.2 gram equivalents of ion exchange capacity per kilogram of water content, said membrane having a resistivity as measured at 1000 Hertz in equilibrium with 0.01 N sodium chloride solution at room temperature of less than about 30 ohm cm. 2 .
Claim 3
Dependent Claim
147 words
An electrodialysis apparatus comprising at least one ion exchange resin membrane consisting of a copolymer of about 35 to about 50 mol percent of at least one compound selected from the group consisting of ethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, polyethylene glycol dimethacrylate, trimethylol propane trimethacrylate, bis-phenol A dimethacrylate, pentaerythritol trimethacrylate and pentaerythritol tetramethacrylate with about 65 to about 50 mol percent respectively of a methacrylate ester salt having the chemical formula: ##STR7## where R is an ion exchange moeity selected from the group consisting of quaternary ammonium salts and sulfonic acid salts, said copolymer having an interstitial ion exchange molality of at least about 2.2 gram equivalents of ion exchange capacity per kilogram of water content, said membrane having a resistivity as measured at 1000 Hertz in equilibrium with 0.01 N aqueous sodium chloride solution at room temperature of less than about 30 ohm-cm. 2 .
Claim 4
Dependent Claim
147 words
An electrodialysis apparatus comprising at least one ion exchange resin membrane consisting of a copolymer of about 35 to about 50 mol percent of at least one compound selected from the group consisting of ethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, polyethylene glycol dimethacrylate, trimethylol propane trimethacrylate, bis-phenol A dimethacrylate, pentaerythritol trimethacrylate and pentaerythritol tetramethacrylate with about 65 to about 50 mol percent respectively of a methacrylate ester salt having the chemical formula: ##STR7## where R is an ion exchange moeity selected from the group consisting of quaternary ammonium salts and sulfonic acid salts, said copolymer having an interstitial ion exchange molality of at least about 2.2 gram equivalents of ion exchange capacity per kilogram of water content, said membrane having a resistivity as measured at 1000 Hertz in equilibrium with 0.01 N aqueous sodium chloride solution at room temperature of less than about 30 ohm-cm. 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-04 | 1984-05-05 | 1984-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-04 | 1988-05-05 | 1988-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-04 | 1992-05-05 | 1992-11-04 | $7700.00 | Window Closed / Lapsed |