US4230660A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Epoxy-borax-coal tar composition for a radiation protective, burn resistant drum liner and centrifugal casting method
Assignee: United States Department of Energy
•
Filing: 1979-01-16
•
Granted: 1980-10-28
•
Expires: 1999-01-16
Abstract
Abstract A boron containing burn resistant, low level radiation protection material useful, for example, as a liner for radioactive waste disposal and storage, a component for neutron absorber, and a shield for a neutron source. The material is basically composed of Borax in the range of 25-50%, coal tar in the range of 25-37.5%, with the remainder being an epoxy resin mix. A preferred composition is 50% Borax, 25% coal tar and 25% epoxy resin. The material is not susceptible to burning and is about 1/5 the cost of existing radiation protection material utilized in similar applications.
Inventors
- 👤 Robert S. Taylor
- 👤 Norman W. Boyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 03:48
CPC Classifications
G; G21; G21C; G21C19/00; G21C19/40; A; A62; A62D; A62D5/00; G21F; G21F1/00; G21F1/02; G21F1/10; G21F1/103; Y; Y02; Y02E; Y02E30/00; Y02E30/30; Y10; Y10S; Y10S260/00; Y10S260/24
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
127 words
A method for producing a radiation protective, burn resistant material for drum liners used in radioactive waste storage, comprising the steps of: forming a mixture by mixing together substantially 10.8-16.2 weight percent of a first material consisting essentially of digycidyl ether of Bisphenol-A, substantially 4.6-6.9 weight percent of a second material consisting essentially of an aliphatic diepoxide, substantially 4.6-6.9weight percent of a third material consisting essentially of an aromatic amine, substantially 4.8-7.2 weight percent of a fourth material consisting essentially of an aliphatic amine, substantially 25-37.5 weight percent coal tar, and substantially 25-50 weight percent borax; and spinning the the mixture in a centrifugator for a time period of about 8-16 hours for forming the mixture into a liner and for curing of the thus formed liner.
Claim 2
Independent Claim
127 words
A method for producing a radiation protective, burn resistant material for drum liners used in radioactive waste storage, comprising the steps of: forming a mixture by mixing together substantially 10.8-16.2 weight percent of a first material consisting essentially of digycidyl ether of Bisphenol-A, substantially 4.6-6.9 weight percent of a second material consisting essentially of an aliphatic diepoxide, substantially 4.6-6.9weight percent of a third material consisting essentially of an aromatic amine, substantially 4.8-7.2 weight percent of a fourth material consisting essentially of an aliphatic amine, substantially 25-37.5 weight percent coal tar, and substantially 25-50 weight percent borax; and spinning the the mixture in a centrifugator for a time period of about 8-16 hours for forming the mixture into a liner and for curing of the thus formed liner.
Claim 3
Dependent Claim
68 words
A cured burn resistant radiation protective material produced from materials consisting essentially of about 25-50 weight percent borax, about 25-37.5 weight percent coal tar, and about 25-37.5 weight percent epoxy resin mix with said resin mix comprising a digycidyl ether of Bisphenol-A, an aliphatic diepoxide, an aromatic amine, and an aliphatic amine, and with the percentage of coal tar to epoxy resin mix being on a one-to-one ratio.
Claim 4
Dependent Claim
68 words
A cured burn resistant radiation protective material produced from materials consisting essentially of about 25-50 weight percent borax, about 25-37.5 weight percent coal tar, and about 25-37.5 weight percent epoxy resin mix with said resin mix comprising a digycidyl ether of Bisphenol-A, an aliphatic diepoxide, an aromatic amine, and an aliphatic amine, and with the percentage of coal tar to epoxy resin mix being on a one-to-one ratio.
Claim 5
Dependent Claim
54 words
The material defined in claim 2, wherein said epoxy resin mix consists of about 10.8-16.2 weight percent of the first material, about 4.65-6.9 weight percent of the second material, about 4.65-6.9 weight percent of the third material, and about 4.87-7.2 weight percent of the fourth material, the percentages being based on the total composition.
Claim 6
Dependent Claim
45 words
The material defined in claim 3, wherein the weight percentage of the first, second, third, Dow XD 7114, and fourth materials are respectively 10.822, 4.654, 4.654, and 4.870; and with the coal tar consisting of 25 weight percent and the borax being 50 weight percents.
Claim 7
Dependent Claim
20 words
A radiation protective, burn resistant drum liner for radioactive waste made in accordance with the method defined in claim 1.
Claim 8
Dependent Claim
29 words
The method defined in claim 1, wherein the step of spinning the mixture in the centrifugator is carried out at circumferential speeds of about 150-200 linear feet per minute.
Claim 9
Dependent Claim
39 words
The material defined in claim 2, wherein said epoxy resin mix comprises about 10.8-16.2 weight percent digycidyl ether of Bisphenol-A, about 4.65-6.9 weight percent aliphatic diepoxide, about 4.65-6.9 weight percent aromatic amine, and about 4.87-7.2 weight percent aliphatic amine.
Claim 10
Dependent Claim
49 words
The material defined in claim 7, wherein the weight percentage of the digycidyl ether Bisphenol-A, aliphatic diepoxide, aromatic amine, and aliphatic amine are respectively about 10.822, 4.654, 4.654, and 4.870; and with the coal tar consisting of about 25 weight percent, and the borax being about 50 weight percent.
References Cited (Backward Citations)
US2796411A
Cited
US2796529A
Cited
US2942116A
Cited
US3112530A
Cited
US2906720A
Cited
US3133887A
Cited
US3062771A
Cited
US3010153A
Cited
US3203906A
Cited
US3238148A
Cited
US3438903A
Cited
US4123392A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-28 | 1984-04-28 | 1984-10-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-28 | 1988-04-28 | 1988-10-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-28 | 1992-04-28 | 1992-10-28 | $7700.00 | Window Closed / Lapsed |