Fire-protecting polyester resins

Claim 2

In a fire-protecting moulding composition, the combination of: 35 to 50% by weight of an unsaturated polyester and 5 to 10% by weight of an unsaturated monomer copolymerisable therewith, together with a mixture of fire-protecting additives to render the moulding composition, when set, intumescent, said mixture consisting of: 5 to 20% by weight of a source of carbon having a high temperature of decomposition and containing many radicals capable of entering into an esterifying reaction with phosphoric acid, 20 to 40% by weight of a source of phosphoric acid having a decomposition temperature lower than that of said source of carbon whereby said esterifying reaction may take place at said decomposition temperature, and 5 to 20% by weight of a source of non-inflammable gases, said source providing said gases at temperatures above the decomposition temperature of said phosphoric acid source, all percentages being calculated on the combined weight of polyester and monomer fire-protecting additives.

Claim 3

A moulding composition comprising about 30% by weight of unsaturated polyester and about 8% by weight of unsaturated monomer is combined with a mixture of about 14% by weight of a source of carbon, about 22% by weight of a source of phosphoric acid, and about 18% by weight of a source of non-inflammable gases.

Claim 4

A moulding composition comprising about 30% by weight of unsaturated polyester and about 8% by weight of unsaturated monomer is combined with a mixture of about 14% by weight of a source of carbon, about 22% by weight of a source of phosphoric acid, and about 18% by weight of a source of non-inflammable gases.

Claim 5

The moulding composition as claimed in claim 1, wherein the carbon source is selected from the group consisting of mono- and di-pentaerythritol and mixtures thereof.

Claim 6

The moulding composition as claimed in claim 1, wherein the phosphoric acid source is selected from the group consisting of ammonium orthophosphate, polyphosphoryl phosphate and preferably ammonium polyphosphate.

Claim 7

The moulding composition as claimed in claim 1, wherein the source of non-inflammable gases comprises at least two substances having different decomposition temperatures, viz. at least one substance of relatively low decomposition temperature and at least one substance of relatively high decomposition temperature.

Claim 8

The moulding composition as claimed in claim 5, wherein the substance of relatively low decomposition temperature is selected from the group consisting of dicyanodiamide, urea, melamine, guanidine, melamineformaldehyde and other amines and amides.

Claim 9

The moulding composition as claimed in claim 5, wherein the substance of relatively high decomposition temperature is selected from the group consisting of chlorinated naphthalene and other chlorinated aromatics.

Claim 10

A moulding composition comprising 25 to 40% by weight of chlorendic acid-based polyester and 5 to 10% by weight of unsaturated monomer are combined with five to twenty percent of carbon source 20 to 40% by weight of a source of phosphoric acid. 5 to 20% by weight of a substance selected from the group consisting of amines and amides, and 0-10% by weight of chlorinated aromatics.

Claim 11

A moulding composition comprising 25 to 40% by weight of chlorendic acid-based polyester and 5 to 10% by weight of unsaturated monomer are combined with five to twenty percent of carbon source 20 to 40% by weight of a source of phosphoric acid. 5 to 20% by weight of a substance selected from the group consisting of amines and amides, and 0-10% by weight of chlorinated aromatics.

Claim 12

A molded, polyester resin article essentially comprising: a molded and cured copolymerisation product of 35 to 50% by weight of an unsaturated polyester and 5 to 10% by weight of an unsaturated monomer copolymerisable therewith, said polyester resin article containing a mixture of fire-protecting additives to render the cured product intumescent, said mixture consisting of 5 to 20% by weight of a source of carbon having a high temperature of decomposition and containing many radicals capable of entering into an esterifying reaction with phosphoric acid, 20 to 40% by weight of a source of phosphoric acid having a decomposition temperature lower than that of said source of carbon whereby said esterifying reaction may take place at said decomposition temperature, and 5 to 20% by weight of a source of non-inflammable gases, said source providing said gases at temperatures above the decomposition temperature of said phosphoric acid source, all percentages being calculated on the combined weight of polyester and monomer and fire-protecting additives.

Claim 13

A molded, polyester resin article essentially comprising: a molded and cured copolymerisation product of 35 to 50% by weight of an unsaturated polyester and 5 to 10% by weight of an unsaturated monomer copolymerisable therewith, said polyester resin article containing a mixture of fire-protecting additives to render the cured product intumescent, said mixture consisting of 5 to 20% by weight of a source of carbon having a high temperature of decomposition and containing many radicals capable of entering into an esterifying reaction with phosphoric acid, 20 to 40% by weight of a source of phosphoric acid having a decomposition temperature lower than that of said source of carbon whereby said esterifying reaction may take place at said decomposition temperature, and 5 to 20% by weight of a source of non-inflammable gases, said source providing said gases at temperatures above the decomposition temperature of said phosphoric acid source, all percentages being calculated on the combined weight of polyester and monomer and fire-protecting additives.

Claim 14

A molded, polyester resin article comprising about 30% by weight of unsaturated polyester and about 8% by weight of unsaturated monomer which is combined with a mixture of about 14% by weight of a source of carbon, about 22% by weight of a source of phosphoric acid, and about 18% by weight of a source of non-inflammable gases.

Claim 15

A molded, polyester resin article comprising about 30% by weight of unsaturated polyester and about 8% by weight of unsaturated monomer which is combined with a mixture of about 14% by weight of a source of carbon, about 22% by weight of a source of phosphoric acid, and about 18% by weight of a source of non-inflammable gases.

Claim 16

The molded, polyester resin article as claimed in claim 9, wherein the carbon source is selected from the group consisting of mono- and di-pentaerythritol and mixtures thereof.

Claim 17

The molded, polyester resin article as claimed in claim 9, wherein the phosphoric acid source is selected from the group consisting of ammonium orthophosphate, polyphosphoryl phosphate and preferably ammonium polyphosphate.

Claim 18

The molded, polyester resin article as claimed in claim 9, wherein the source of non-inflammable gases comprises at least two substances having different decomposition temperatures, viz. at least one substance of relatively low decomposition temperature and at least one substance of relatively high decomposition temperature.

Claim 19

The molded, polyester resin article as claimed in claim 13, wherein the substance of relatively low decomposition temperature is selected from the group consisting of dicyanodiamide, urea, melamine, guanidine, melamine-formaldehyde and other amines and amides.

Claim 20

The molded, polyester resin article as claimed in claim 13, wherein the substance of relatively high decomposition temperature is selected from the group consisting of chlorinated naphthalene and other chlorinated aromatics.

Claim 21

A molded, polyester resin article comprising 25 to 40% by weight of chlorendic acid-based polyester and 5 to 10% by weight of unsaturated monomer which are combined with five to twenty percent of carbon source, 20 to 40% by weight of a source of phosphoric acid, 5 to 20% by weight of a substance selected from the group consisting of amines and amides and 0 to 10% by weight of chlorinated aromatics.

Claim 22

A molded, polyester resin article comprising 25 to 40% by weight of chlorendic acid-based polyester and 5 to 10% by weight of unsaturated monomer which are combined with five to twenty percent of carbon source, 20 to 40% by weight of a source of phosphoric acid, 5 to 20% by weight of a substance selected from the group consisting of amines and amides and 0 to 10% by weight of chlorinated aromatics.

Claim 23

The molded, polyester resin article as claimed in claim 9, further comprising a glass fiber reinforcement.