Peroxy-free methacrylate lacquer and adhesive method employing same
Assignee: Pratt and Lambert Inc
•
Filing: 1979-03-07
•
Granted: 1980-10-28
•
Expires: 1999-03-07
Abstract
Abstract A peroxy catalyst activator is dissolved in a methyl methacrylate, ethyl methacrylate or styrene lacquer containing, in addition, an adhesion promotor, e.g., an acrylic or methacrylic compound such as the carboxylic acids, amides esters having in the ester moiety amino groups or epoxy groups. The lacquer comprises a copolymer of the monomers dissolved in a volatile liquid solvent such as a mixture of toluene and isopropanol. In use, the lacquer containing the activator is applied to at least one of two substrates and allowed to dry. Thereafter, an adhesive composition containing peroxy catalyst is applied to at least one substrate and both substrates are brought into contact and held until the adhesive bond is formed. The lacquer acts to seal porous substrates and permits the cure to take place rapidly without air inhibition. It forms a surface which retains its activity over a long time period, running into years. Thus, component parts may be coated with the lacquer and stored until needed.
Inventors
- 👤 Leon E. Wolinski
- 👤 Peter D. Berezuk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:53
CPC Classifications
C; C09; C09J; C09J5/00; C09J5/02; C09D; C09D133/00; C09D133/04; C09D133/06; C09D133/10; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/31935
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
175 words
A peroxy-free lacquer composition for coating a substrate and serving as a vehicle for a peroxy catalyst activator, the activator-containing coating on the substrate being adapted to be brought into contact with an adhesive containing a peroxy catalyst, the said lacquer composition comprising, in weight percent, copolymerizable monomers consisting of (A) 65 to 98% of a monomer selected from the group consisting of methyl methacrylate, ethyl methacrylate and styrene, (B) 2 to 35% of an adhesion promoter selected from the group consisting of ##STR2## (C) 0 to 33% of a softening monomer selected from the group consisting of butyl acrylate and 2-ethyl hexyl acrylate, at least one member of (A) and (B) respectively being present, the said lacquer composition consisting of copolymers and any unreacted monomers, (D) the said lacquer composition being dissolved in a volatile solvent to form a solution containing 20 to 40% lacquer composition, and (E) an tertiary amine activator for a peroxy free radical polymerization catalyst dissolved in said solution in a ratio of activator: lacquer composition of 5:95 to 95:5.
Claim 2
Dependent Claim
175 words
A peroxy-free lacquer composition for coating a substrate and serving as a vehicle for a peroxy catalyst activator, the activator-containing coating on the substrate being adapted to be brought into contact with an adhesive containing a peroxy catalyst, the said lacquer composition comprising, in weight percent, copolymerizable monomers consisting of (A) 65 to 98% of a monomer selected from the group consisting of methyl methacrylate, ethyl methacrylate and styrene, (B) 2 to 35% of an adhesion promoter selected from the group consisting of ##STR2## (C) 0 to 33% of a softening monomer selected from the group consisting of butyl acrylate and 2-ethyl hexyl acrylate, at least one member of (A) and (B) respectively being present, the said lacquer composition consisting of copolymers and any unreacted monomers, (D) the said lacquer composition being dissolved in a volatile solvent to form a solution containing 20 to 40% lacquer composition, and (E) an tertiary amine activator for a peroxy free radical polymerization catalyst dissolved in said solution in a ratio of activator: lacquer composition of 5:95 to 95:5.
Claim 3
Dependent Claim
34 words
The lacquer composition of claim 1 wherein the weight percent of (A) is 90 to 98, the weight percent of (B) is 2 to 10, the weight percent of (C) is 0 to 8.
Claim 4
Dependent Claim
29 words
The lacquer composition of claim 2 wherein the weight percent of (A) is 98, the weight percent of (B) is 2, and the weight percent of (C) is 0.
Claim 5
Dependent Claim
40 words
The lacquer composition of claim 1 wherein the solvent is a mixture in weight percent of 70 toluene and 30 isopropanol, the lacquer solution containing 20% of said lacquer composition, and the activator is 4,4'-methylene bis (N, N, -dimethyl aniline).
Claim 6
Dependent Claim
23 words
The lacquer composition of claim 4 wherein (A) is 98% methylmethacrylate, (B) is 2% acrylic acid, and the ratio of (B):(A) is 5:95.
Claim 7
Dependent Claim
23 words
The lacquer composition of claim 5 wherein (A) is 98% methylmethacrylate, (B) is 2% acrylic acid, and the ratio of (B):(A) is 30:70.
Claim 8
Dependent Claim
32 words
The lacquer composition of claim 4 wherein (A) is 65% methylmethacrylate, (B) is 6% acrylic acid, (C) is 29% butyl acrylate and the ratio of activator to the lacquer components is 30:70.
Claim 9
Dependent Claim
31 words
The lacquer composition of claim 4 wherein (A) is 98% methyl methacrylate, (B) is 2% glycidyl methacrylate, and the ratio of activator to the lacquer composition is from 30:70 to 95:5.
Claim 10
Dependent Claim
28 words
The lacquer composition of claim 4 wherein (A) is 98% methyl methacrylate, (B) is 20% aziridinal methacrylate, and the ratio of activator to the lacquer composition is 30:70.
Claim 11
Dependent Claim
128 words
In a structure having a first surface adapted to be adhesively joined to a second mating surface, the improvement comprising; having a coating on said first surface comprising a peroxy-free lacquer composition comprising in weight percent a copolymer of monomers consisting of (A) 65 to 98% of a monomer selected from the group consisting of methyl methacrylate, ethyl methacrylate and styrene, (B) 2 to 35% of an adhesion promoter selected from the group consisting of ##STR3## (C) 0 to 33% of a softening monomer selected from the group consisting of butyl acrylate and 2-ethyl hexyl acrylate, at least one member of (A) and (B) respectively being present, and (D) an activator for a peroxy free radical polymerization catalyst, the ratio of activator: lacquer composition being 5:95 to 95.5.
Claim 12
Dependent Claim
128 words
In a structure having a first surface adapted to be adhesively joined to a second mating surface, the improvement comprising; having a coating on said first surface comprising a peroxy-free lacquer composition comprising in weight percent a copolymer of monomers consisting of (A) 65 to 98% of a monomer selected from the group consisting of methyl methacrylate, ethyl methacrylate and styrene, (B) 2 to 35% of an adhesion promoter selected from the group consisting of ##STR3## (C) 0 to 33% of a softening monomer selected from the group consisting of butyl acrylate and 2-ethyl hexyl acrylate, at least one member of (A) and (B) respectively being present, and (D) an activator for a peroxy free radical polymerization catalyst, the ratio of activator: lacquer composition being 5:95 to 95.5.
Claim 13
Dependent Claim
25 words
The structure of claim 10 wherein the lacquer composition comprises 90-98% of (A), 2-10% (B), 0-8% of (C) and the activator is a tertiary amine.
Claim 14
Dependent Claim
15 words
The structure of claim 11 wherein (A) is 98% (B) is 2% (C) is 0.
Claim 15
Dependent Claim
13 words
The structure of claim 10 wherein the activator is 4,4'-methylene bis (N,N-dimethyl aniline).
Claim 16
Dependent Claim
26 words
The structure of claim 10 wherein (A) is 98% methyl methacrylate and (B) is 2% acrylic acid the ratio of activator to lacquer composition is 5:95.
Claim 17
Dependent Claim
26 words
The structure of claim 10 wherein (A) is 98% methyl methacrylate and (B) is 2% acrylic acid the ratio of activator to lacquer composition is 30:70.
Claim 18
Dependent Claim
22 words
The structure of claim 13 wherein (A) is 65% methyl methacrylate, (B) is 6% acrylic acid and (C) is 29% butyl acrylate.
Claim 19
Dependent Claim
30 words
The structure of claim 13 wherein (A) is 98% methyl methacrylate, (B) is 2% glycidyl methacrylate and the ratio of activator to the lacquer composition is from 30:70 to 95:5.
Claim 20
Dependent Claim
27 words
The structure of claim 13 wherein (A) is 98% methyl methacrylate, (B) is 2% azirindinal methacrylate and the ratio of activator to the lacquer composition is 30:70.
Claim 21
Dependent Claim
111 words
A method for adhesively joining a pair of mating surfaces comprising applying to at least one of said surfaces the lacquer composition solution of claim 1 containing an activator, allowing the solution to dry, applying to at least one of said surfaces an activatable curable adhesive comprising a non-reactive elastomer dissolved in a non-acid methacrylic or acrylic monomer and a methacrylic or acrylic acid monomer, the said adhesive containing an effective amount of an peroxy catalyst, the said adhesive being activatable by contact with a peroxy catalyst activator, joining the pair of mating surfaces in a contact relationship and maintaining the contact relationship until the said adhesive cares to a set.
Claim 22
Dependent Claim
12 words
The method of claim 19 wherein the activator is a tertiary amine.
Claim 23
Dependent Claim
13 words
The method of claim 19 wherein the activator is 4,4'-methylene bis (N,N-dimethyl aniline).
References Cited (Backward Citations)
US3290257A
Cited
USRE27093E
Cited
US4077926A
Cited
US3893960A
Cited
US3860563A
Cited
US4074004A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-28 | 1984-04-28 | 1984-10-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-28 | 1988-04-28 | 1988-10-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-28 | 1992-04-28 | 1992-10-28 | $7700.00 | Window Closed / Lapsed |