Electrically conductive resin composition
Assignee: Sony Corp
•
Filing: 1978-11-27
•
Granted: 1980-10-21
•
Expires: 1998-11-27
Abstract
Abstract A resin composition includes 20 to 70 parts by weight of unsaturated polyester being radically copolymerizable, having an average molecular weight between 500 and 5000, and having a degree of unsaturation between 150 and 190, 1 to 25 parts by weight of thermoplastic resin having an average molecular weight between 104 and 107, 30 to 70 parts by weight of ethylenically unsaturated compound being radically reactive with said unsaturated polyester resin and being able to dissolve said unsaturated polyester and said thermoplastic resin, on the basis of the total amount of said unsaturated polyester resin, said thermoplastic resin and said ethylenically unsaturated compound being 100 parts by weight, 0.05 to 1.0 parts by weight of fiber-like conductive material having a length between 1 and 10 millimeters and an aspect ratio between 2 and 103, and not more than 40 parts by weight of granular conductive material having a diameter between 10 and 300 microns, on the basis of the total amount of said unsaturated polyester resin, said thermoplastic resin and said ethylenically unsaturated compound being 100 weight parts.
Inventors
- 👤 Yoshimi Makino
- 👤 Hidetoshi Shimizu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:02
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/06; C08K; C08K3/00; C08K3/01; C08K3/02; C08K3/04; C08L33/00; C08L33/04; C08L33/06; C08L33/08
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
198 words
A resin composition comprising: (A) 20 to 70 parts by weight of an unsaturated polyester being radically copolymerizable, having an average molecular weight between 500 and 5000, and having a degree of unsaturation between 150 and 190, (B) 1 to 25 parts by weight of a thermoplastic resin having an average molecular weight between 1×10 4 and 1×10 7 , (C) 30 to 70 parts by weight of a liquid of at least one ethylenically unsaturated monomer being radically reactive with said unsaturated polyester and being able to dissolve said unsaturated polyester and said thermo-plastic resin, (D) 0.05 to 1.0 parts by weight of an electrically conductive fiber-like material having a length between 1 and 10 millimeters and an aspect ratio between 2 and 10 3 , on the basis of the total amount of said unsaturated polyester, said thermoplastic resin and said ethylenically unsaturated compound being 100 parts by weight; and (E) not more than 40 parts by weight of an electrically conductive powder material having a diameter between 10 and 300 microns, on the basis of the total amount of said unsaturated polyester, said thermo-plastic resin and said ethylenically unsaturated compound being 100 parts by weight.
Claim 2
Dependent Claim
198 words
A resin composition comprising: (A) 20 to 70 parts by weight of an unsaturated polyester being radically copolymerizable, having an average molecular weight between 500 and 5000, and having a degree of unsaturation between 150 and 190, (B) 1 to 25 parts by weight of a thermoplastic resin having an average molecular weight between 1×10 4 and 1×10 7 , (C) 30 to 70 parts by weight of a liquid of at least one ethylenically unsaturated monomer being radically reactive with said unsaturated polyester and being able to dissolve said unsaturated polyester and said thermo-plastic resin, (D) 0.05 to 1.0 parts by weight of an electrically conductive fiber-like material having a length between 1 and 10 millimeters and an aspect ratio between 2 and 10 3 , on the basis of the total amount of said unsaturated polyester, said thermoplastic resin and said ethylenically unsaturated compound being 100 parts by weight; and (E) not more than 40 parts by weight of an electrically conductive powder material having a diameter between 10 and 300 microns, on the basis of the total amount of said unsaturated polyester, said thermo-plastic resin and said ethylenically unsaturated compound being 100 parts by weight.
Claim 3
Dependent Claim
22 words
A resin composition according to claim 1, in which an average molecular weight of said unsaturated polyester is between 700 and 2000.
Claim 4
Dependent Claim
35 words
A resin composition according to claim 1, in which said conductive fiber-like material is the one or more selected from carbon fiber, glass fiber plated with metal, glass fiber coated with metal, and metal whisken.
Claim 5
Dependent Claim
27 words
A resin composition according to claim 1, in which said conductive powder material is the one or more selected from carbon powder, graphite powder and metal powder.
Claim 6
Dependent Claim
65 words
A resin composition according to claim 1, further comprising 0.1 to 3.0 parts by weight of an azo catalyst as a radical initiator, on the basis of the total amount of said unsaturated polyester, said thermoplastic resin and said ethylenically unsaturated compound being 100 parts by weight, and said azo catalyst being selected from the group consisting of 2,2'-azobis·isobutyl·carbonitrile, 2,2'-azobis-2,4-dimethylvaleronitrile, 2,2'-azobis-4-methoxy-2,4-dimethylvaleronitrile, 2-phenylazo-2,4-dimethyl-4-methoxyvaleronitrile, 2-cyano-2-propylazoformide, and 1,1'-azobiscyclohexane-1-carbonitrile.
Claim 7
Dependent Claim
59 words
A resin composition according to claim 1, in which said unsaturated polyester is produced by reaction of unsaturated dicarboxylic acid and polyhydric alcohol, said unsaturated dicarboxylic acid being selected from maleic anhydride, itaconic acid and citraconic acid, and said polyhydric alcohol being selected from ethylene glycol, diethylene glycol, propylene glycol, buthylene glycol, neopentyl glycol, trimethylolethane, trimethylolpropane, hexanetriol and pentaerythritol.
Claim 8
Dependent Claim
82 words
A resin composition according to claim 1, in which said unsaturated polyester is produced by reaction of unsaturated dicarboxylic acid, polyhydric alcohol and saturated dicarboxylic acid, said unsaturated dicarboxylic acid being selected from maleic anhydride, itaconic acid and citraconic acid, said polyhydric alcohol being selected from ethylene glycol, diethylene glycol, propylene glycol, buthylene glycol, neopentyl glycol, trimethylolethane, trimethylolpropane, hexanetriol and pentaerythritol, and said saturated carboxylic acid being selected from terephthalic acid, isophthalic acid, phthalic anhydride, tetrahydrophthalic anhydride, adipic acid and sebacic acid.
Claim 9
Dependent Claim
37 words
A resin composition according to claim 1, in which said ethylenically unsaturated monomer is selected from styrene, vinyltoluene, chlorostyrene, lower alcohol ester of methacrylic acid, 1,3-buttanediol dimetaacrylate, diacrylphthalate and a mixture of two or more of them.
Claim 10
Dependent Claim
81 words
A resin composition according to claim 1, in which said thermoplastic resin is selected from homopolymers of methylmethacrylate, ethylmethacrylate, buthylmethacrylate, methylacrylate and ethylacrylate, a coporymer of methylmethacrylate with lower alkyl ester of acrylic acid and/or methacrylic acid, copolymers of methylmethacrylate with a little of one or more kinds of laurylmethacrylate, isobornylmethacrylate, acryl amide, hydroxyethylmethacrylate, styrene, 2-ethyl-hexylacrylate, acrylonitrile, methacrylic acid, methacryl amide, methylol acryl amide, and cetyl stearyl methacrylate, styrene-acrylonitrile copolymer, vinyl chloride-vinyl acetate copolymer, cellulose acetate buthylate, and cellulose acetate propionate.
Claim 11
Dependent Claim
21 words
A resin composition according to claim 1, in which said resin composition has a resistivity of less than 10 8 ohms-cm.
Claim 12
Dependent Claim
49 words
A resin composition according to claim 1, in which the added amount of said conductive powder material is 10 to 40 parts by weight on the basis of the total amount of said unsaturated polyester resin, said thermoplastic resin and said ethylenically unsaturated compound being 100 parts by weight.
Claim 13
Dependent Claim
16 words
A resin composition according to claim 3, in which said conductive fiber-like material is carbon fiber.
Claim 14
Dependent Claim
15 words
A resin composition according to claim 4, in which said conductive powder material is graphite.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-21 | 1984-04-21 | 1984-10-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-21 | 1988-04-21 | 1988-10-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-21 | 1992-04-21 | 1992-10-21 | $7700.00 | Window Closed / Lapsed |