Solid electrolyte oxygen sensor and method of making same
Assignee: Bank of Nova Scotia
•
Filing: 1979-07-09
•
Granted: 1980-10-21
•
Expires: 1999-07-09
Abstract
Abstract Oxygen sensor with a disc type solid electrolyte has the disc sealed in a shrinkable ceramic tube by the pressure which is developed and the surface glazing which takes place as the tube is fired. The tube is preferably formed of forsterite which can shrink about 25% during firing, thus causing the tube to become slightly bulged out in the region of the disc due to the interference fit produced by the shrinkage. The porous electrodes on the top and bottom surfaces of the disc are preferably omitted from a small region near one edge of the top and bottom surfaces but are continued as a stripe or band down the edge from a diametrically opposite portion of each surface, the stripes and unelectroded areas associated with the respective surfaces being spaced to prevent electrical shorting. The disc stripes are pressure bonded during firing of the tube to a pair of spaced lead stripes on the inside tube surface.
Inventors
- 👤 Edward P. Habdas
- 👤 Jon D. Aaron
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 06:43
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4075; C; C04; C04B; C04B35/00; C04B35/622; C04B35/653; C04B37/00; C04B37/003; C04B37/005; C04B37/02; C04B37/023; C04B37/025; G01N27/4071; C04B2235/00; C04B2235/65; C04B2235/656; C04B2237/00; C04B2237/02; C04B2237/10; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; C04B2237/345; C04B2237/348; C04B2237/40; C04B2237/408; C04B2237/50; C04B2237/76; C04B2237/78
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
297 words
A method of making an oxygen sensing device comprising the steps of: forming a sintered wafer of stabilized solid electrolyte ceramic; applying a first, porous, continuous electrode coating to the major portion of the sensing side of said wafer and to a narrow first band portion along the axial length of a first side edge portion of said wafer while leaving said sensing side of said wafer devoid of said electrode coating in the area thereof which is immediately adjacent a second side edge portion which is circumferentially spaced from said first band of coating; applying a second, porous, continuous electrode coating to the major portion of the reference side of said wafer and to a narrow second band portion along the axial length of said second side edge portion while leaving said reference side of said wafer devoid of said electrode coating in the area thereof which is immediately adjacent said first narrow band portion; applying first and second spaced conductive stripes internally along at least a portion of the length of an unfired ceramic tube having an inner diameter greater than the outer diameter of said wafer and a temperature coefficient of expansion which is compatible with said wafer after firing but will cause said tube to shrink into a hermetic sealing relationship with said wafer during firing, said stripes being applied at a circumferential spacing corresponding to the spacing between said first and second bands of coating; positioning said wafer internally of said unfired ceramic tube so that its first and second bands of coating are aligned with and overlie said first and second conductive stripes; and firing said tube and wafer assembly to shrink said tube onto said wafer and mechanically force said bands of coating into intimate contact with said conductive stripes.
Claim 2
Independent Claim
297 words
A method of making an oxygen sensing device comprising the steps of: forming a sintered wafer of stabilized solid electrolyte ceramic; applying a first, porous, continuous electrode coating to the major portion of the sensing side of said wafer and to a narrow first band portion along the axial length of a first side edge portion of said wafer while leaving said sensing side of said wafer devoid of said electrode coating in the area thereof which is immediately adjacent a second side edge portion which is circumferentially spaced from said first band of coating; applying a second, porous, continuous electrode coating to the major portion of the reference side of said wafer and to a narrow second band portion along the axial length of said second side edge portion while leaving said reference side of said wafer devoid of said electrode coating in the area thereof which is immediately adjacent said first narrow band portion; applying first and second spaced conductive stripes internally along at least a portion of the length of an unfired ceramic tube having an inner diameter greater than the outer diameter of said wafer and a temperature coefficient of expansion which is compatible with said wafer after firing but will cause said tube to shrink into a hermetic sealing relationship with said wafer during firing, said stripes being applied at a circumferential spacing corresponding to the spacing between said first and second bands of coating; positioning said wafer internally of said unfired ceramic tube so that its first and second bands of coating are aligned with and overlie said first and second conductive stripes; and firing said tube and wafer assembly to shrink said tube onto said wafer and mechanically force said bands of coating into intimate contact with said conductive stripes.
Claim 3
Dependent Claim
15 words
A method in accordance with claim 1 wherein said ceramic tube is formed by extrusion.
Claim 4
Dependent Claim
24 words
A method in accordance with claim 1 wherein said tube is formed of a material which will shrink about 25% when it is fired.
Claim 5
Dependent Claim
38 words
A method in accordance with claim 3 wherein said electrode coatings on said wafer and said conductive stripes on said tube are of the same material, said stripes extending internally of said tube to the reference end thereof.
Claim 6
Dependent Claim
25 words
A method in accordance with claim 4 wherein said tube is formed so that its walls have a substantially constant thickness cross-section throughout their length.
Claim 7
Dependent Claim
280 words
An oxygen sensing device comprising a ceramic tube having a relatively uniform wall thickness; a thin wafer of stabilized solid electrolyte material positioned intermediate the ends of said tube and transverse to the axis thereof, said wafer having a sensing side and a reference side, the outer diameter of said wafer being greater than the inner diameter of said tube in at least the spaced axial regions of said tube which are immediately adjacent the two sides of said wafer, and the outer diameter of said ceramic tube being greater in the plane of said wafer than in the transverse axial planes immediately adjacent thereto, said difference in diameters being sufficient to hermetically seal said wafer into said ceramic tube throughout a temperature range of at least about 500°-2000° F.; a first, continuous, porous electrode coating on the major portion of the sensing side of said wafer and along a first narrow band on the side edge of said wafer; a second, continuous porous electrode coating on the major portion of the reference side of said wafer and along a second, narrow band on the side edge of said wafer which is spaced circumferentially around said wafer from said first coating band, said sensing and reference sides being devoid of coating in the regions thereof which are immediately adjacent said second and first coating bands, respectively; first and second, axially extending, spaced conductive stripes positioned along the interior of said ceramic tube from the reference end thereof to at least the sensing edge of said wafer, said first and second conductive stripes being aligned with, and in intimate electrical and mechanical contact with said first and second coating bands, respectively.
Claim 8
Dependent Claim
280 words
An oxygen sensing device comprising a ceramic tube having a relatively uniform wall thickness; a thin wafer of stabilized solid electrolyte material positioned intermediate the ends of said tube and transverse to the axis thereof, said wafer having a sensing side and a reference side, the outer diameter of said wafer being greater than the inner diameter of said tube in at least the spaced axial regions of said tube which are immediately adjacent the two sides of said wafer, and the outer diameter of said ceramic tube being greater in the plane of said wafer than in the transverse axial planes immediately adjacent thereto, said difference in diameters being sufficient to hermetically seal said wafer into said ceramic tube throughout a temperature range of at least about 500°-2000° F.; a first, continuous, porous electrode coating on the major portion of the sensing side of said wafer and along a first narrow band on the side edge of said wafer; a second, continuous porous electrode coating on the major portion of the reference side of said wafer and along a second, narrow band on the side edge of said wafer which is spaced circumferentially around said wafer from said first coating band, said sensing and reference sides being devoid of coating in the regions thereof which are immediately adjacent said second and first coating bands, respectively; first and second, axially extending, spaced conductive stripes positioned along the interior of said ceramic tube from the reference end thereof to at least the sensing edge of said wafer, said first and second conductive stripes being aligned with, and in intimate electrical and mechanical contact with said first and second coating bands, respectively.
Claim 9
Dependent Claim
20 words
The oxygen sensing device of claim 6 wherein said electrode coatings and said conductive stripes are of the same material.
Claim 10
Dependent Claim
14 words
The oxygen sensing device of claim 7 wherein said tube is formed of forsterite.
References Cited (Backward Citations)
US4119513A
Cited
US4123344A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-21 | 1984-04-21 | 1984-10-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-21 | 1988-04-21 | 1988-10-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-21 | 1992-04-21 | 1992-10-21 | $7700.00 | Window Closed / Lapsed |