Earthen cement compositions for building materials and process
Assignee: Individual
•
Filing: 1978-07-28
•
Granted: 1980-10-21
•
Expires: 1998-07-28
Abstract
Abstract Soil compositions suitable for use as building materials and having significantly improved properties of thermal or energy conductants and energy resistance as well as improved stress, compression, bearing, sound absorbing and structural integrity characteristics comprise a soil combined with cellulose, sodium silicate, and potassium or sodium hydroxide in specific proportions. The composition may also include clay and mineral fillers, depending on the characteristics of the soil.
Inventors
- 👤 Gordon L. Schneider
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:28
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/24; C04B28/26; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/91; Y10; Y10S; Y10S106/00; Y10S106/90; Y10S52/00; Y10S52/09
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
88 words
A process for producing an improved earthen composition comprising: (a) preparing an aqueous hydroxide solution selected from the group consisting of sodium hydroxide, potassium hydroxide, and mixtures thereof, (b) adding cellulose to said aqueous hydroxide solution and agitating the mixture to separate cellulose fibers throughout the mixture, (c) blending the product of (b) with soil until a substantially homogeneous mixture is achieved having a pH of between about 12.5 and 13.5, (d) adding and mixing sodium silicate to said mixture of (c), and (e) drying the resulting composition.
Claim 2
Dependent Claim
88 words
A process for producing an improved earthen composition comprising: (a) preparing an aqueous hydroxide solution selected from the group consisting of sodium hydroxide, potassium hydroxide, and mixtures thereof, (b) adding cellulose to said aqueous hydroxide solution and agitating the mixture to separate cellulose fibers throughout the mixture, (c) blending the product of (b) with soil until a substantially homogeneous mixture is achieved having a pH of between about 12.5 and 13.5, (d) adding and mixing sodium silicate to said mixture of (c), and (e) drying the resulting composition.
Claim 3
Dependent Claim
21 words
The process of claim 1 wherein said sodium silicate comprises between about 1% and about 20% by weight of the composition.
Claim 4
Dependent Claim
20 words
The process of claim 1 wherein said cellulose comprises between about 0.5% and about 20%, by weight of the composition.
Claim 5
Dependent Claim
22 words
The process of claim 1 wherein the amount of hydroxide is between about 0.05% and about 2% by weight of the composition.
Claim 6
Dependent Claim
22 words
The process of claim 1 wherein said soil is selected from the group consisting of clay, silt, caliche, loam, gravel and sand.
Claim 7
Dependent Claim
23 words
The process of claim 1 wherein said soil comprises sand and said composition includes between about 5 and about 20% by weight clay.
Claim 8
Dependent Claim
12 words
The process of claim 6 wherein said clay comprises kaolin or kaolinite.
Claim 9
Dependent Claim
14 words
The process of claim 1 including adding up to 40%, by weight, mineral filler.
Claim 10
Dependent Claim
14 words
The process of claim 1 including adding sufficient water to provide a pourable composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-21 | 1984-04-21 | 1984-10-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-21 | 1988-04-21 | 1988-10-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-21 | 1992-04-21 | 1992-10-21 | $7700.00 | Window Closed / Lapsed |