Spherical activated carbon having low dusting property and high physical strength and process for producing the same

Claim 2

A process for producing spherical particles of activated carbon having a low susceptibility to dusting, comprising the steps of: heating while continuously stirring a mixture of a pitch having a softening point of 50° to 350° C., a carbon content of 80 to 97%, an atomic ratio of hydrogen to carbon of 0.3 to 2.0, and a content of nitrobenzene insoluble matter of below 60%, at least one aromatic compound miscible with said pitch and 0.1 to 10% by weight based on the amount of said pitch of at least one polymer or one copolymer having the chain hydrocarbon moiety as a major component thereof, thereby liquefying homogeneously said mixture; dispersing said liquefied mixture into an aqueous solution containing a suspending agent, thereby obtaining microspheres of said mixture dispersed in said solution; and subjecting the thus obtained microspheres to a series of treatments of removal of said aromatic compound, infusibilization, carbonization and activation.

Claim 3

The process of claim 1, wherein said heating of said mixture is carried out at a temperature of 150° to 200° C.

Claim 4

The process of claim 1, wherein said dispersing is carried out in said aqueous solution at a temperature of 50° to 200° C.

Claim 5

The process of claim 1, wherein said polymer or copolymer has a molecular weight less than about 500,000.

Claim 6

The process of claim 1, wherein said mixture contains 0.5 to 8% by weight of said polymer or copolymer based on the amount of said pitch.

Claim 7

The process of claim 1, wherein said polymer or copolymer is selected from the group consisting of polyethylene, polypropylene, polybutadiene, polystyrene, copolymers of ethylene and vinylacetate and their derivatives.

Claim 8

The process of claim 1, wherein said mixture contains 5 to 50% by weight of said aromatic compound based on the amount of said pitch.

Claim 9

The process of claim 1, wherein said aromatic compound miscible with said pitch is selected from the group consisting of benzene, toluene, xylene, naphthalene, methylnaphthalene, dimethylnapththalene, anthracene, phenanthrene, triphenylene, diphenyl, diphenylmethane, diphenyl ether and their alkyl derivatives.

Claim 10

The spherical particles of activated carbon produced by the process of claim 1, having the following properties:

Claim 11

1 to 1.5 mm in diameter; 0.5 to 1.5 g/ml of density of individual particles; 800 to 1600 m 2 /g of specific surface area; about 0.3 ml/g, as measured in the range of micropore radius of below 100 A, of micropore volume and also 0.5 ml/g, as measured in the range of micropore radius between 100 and 100,000 A; and below 0.5% by weight of ash content.

Claim 12

1 to 1.5 mm in diameter; 0.5 to 1.5 g/ml of density of individual particles; 800 to 1600 m 2 /g of specific surface area; about 0.3 ml/g, as measured in the range of micropore radius of below 100 A, of micropore volume and also 0.5 ml/g, as measured in the range of micropore radius between 100 and 100,000 A; and below 0.5% by weight of ash content.

Claim 13

The spherical particles of activated carbon having a low susceptibility to dusting and prepared by the process comprising the steps of: heating while continuously stirring a mixture of a pitch having a softening point of 50° to 350° C., a carbon content of 80 to 97% by weight, an atomic ratio of hydrogen to carbon of 0.3 to 2.0, and a content of nitrobenzene-insoluble matter of below 60% by weight, at least one aromatic compound miscible with said pitch and 0.1 to 10% by weight based on the amount of said pitch of at least one polymer or one copolymer having the chain hydrocarbon moiety as a major component thereof, thereby liquefying homogeneously said mixture; dispersing said liquefied mixture into an aqueous solution containing a suspending agent, thereby obtaining microspheres of said mixture dispersed in said solution; and subjecting the thus-obtained microspheres to a series of treatments of removal of said aromatic compound, infusibilization, carbonization and activation.

Claim 14

The spherical particles of activated carbon having a low susceptibility to dusting and prepared by the process comprising the steps of: heating while continuously stirring a mixture of a pitch having a softening point of 50° to 350° C., a carbon content of 80 to 97% by weight, an atomic ratio of hydrogen to carbon of 0.3 to 2.0, and a content of nitrobenzene-insoluble matter of below 60% by weight, at least one aromatic compound miscible with said pitch and 0.1 to 10% by weight based on the amount of said pitch of at least one polymer or one copolymer having the chain hydrocarbon moiety as a major component thereof, thereby liquefying homogeneously said mixture; dispersing said liquefied mixture into an aqueous solution containing a suspending agent, thereby obtaining microspheres of said mixture dispersed in said solution; and subjecting the thus-obtained microspheres to a series of treatments of removal of said aromatic compound, infusibilization, carbonization and activation.

Claim 15

The spherical activated carbon of claim 10 which has the following physical characteristics: spheres of 0.1-1.5 mm in diameter; particle density of 0.5-1.5 g/ml specific surface area of 800-1600 m 2 /g; a micro-pore volume of above 0.3 ml/g as measured in the range of micro-pore radius of below 100 A, and also of below 0.5 ml/g as measured in the range of micro-pore radius between 100 A and 100,000 A; and the ash content of below 0.5% by weight.