Copper-boron carbide composite particle and method for its production

Claim 2

A process for encapsulating particulate boron carbide core materials within copper metal to produce discrete particles suitable for use in fabricating boron carbide core material-filled copper structures having a selected copper/boron carbide core material volume ratio, said process comprising the steps of: (A) placing the particulate boron carbide core material in a copper containing solution suitable for electroless copper plating and electrolessly plating an electrically conductive film of copper metal on said boron carbide core material to produce copper coated boron carbide particles; (B) electrolytically depositing additional copper onto said copper coated boron carbide particles; and (C) terminating the electrodeposition when particles of copper coated boron carbide having a selected copper/boron carbide core material volume ratio is achieved.

Claim 3

The process as set forth in claim 1 wherein the selected copper/boron carbide ratio is within the range of 0.3 to 4.

Claim 4

The process as set forth in claim 1 wherein the step (A) is effected by: placing the solution-boron carbide core particle mixture in a cylindrically shaped container having a longitudinal axis and a bottom surface describing at least a portion of a cone whose axis is coincident with said axis; orienting said container so that said axes define an acute angle with the vertical; and rotating said container about said axes.

Claim 5

A material for producing copper, boron carbidefilled, neutron abosrobing shield structures, said material comprising a multiplicity of particles suitable for being fused to form a unitary structure by rolling, pressing, or sintering, each said particle comprising: a core particle of boron carbide; a thin film of electroless copper bonded to said core particle; and a layer of electrodeposited copper metal bonded to said film and encapsulating said core particle, the copper/boron carbide volume ratio being within the range of 0.3 to 4.

Claim 6

A material for producing copper, boron carbidefilled, neutron abosrobing shield structures, said material comprising a multiplicity of particles suitable for being fused to form a unitary structure by rolling, pressing, or sintering, each said particle comprising: a core particle of boron carbide; a thin film of electroless copper bonded to said core particle; and a layer of electrodeposited copper metal bonded to said film and encapsulating said core particle, the copper/boron carbide volume ratio being within the range of 0.3 to 4.

Claim 7

A process for producing a neutron absorbing, shield structure, said process comprising the steps of: (A) placing a particulate boron carbide core material in a copper containing solution suitable for electroless copper plating and electrolessly plating an electrically conductive film of copper metal on said boron carbide core material to produce copper coated boron carbide particles; (B) electrolytically depositing additional copper onto said copper coated boron carbide particles; (C) terminating the electrodeposition when particles of copper coated boron carbide having a copper/boron carbide core material volume ratio between the range of 0.3 to 4 is achieved; and, (D) consolidating said particles of copper coated boron carbide to produce a structure having a thickness sufficient to provide a boron carbide particle intercepting all lines passing therethrough.

Claim 8

A process for producing a neutron absorbing, shield structure, said process comprising the steps of: (A) placing a particulate boron carbide core material in a copper containing solution suitable for electroless copper plating and electrolessly plating an electrically conductive film of copper metal on said boron carbide core material to produce copper coated boron carbide particles; (B) electrolytically depositing additional copper onto said copper coated boron carbide particles; (C) terminating the electrodeposition when particles of copper coated boron carbide having a copper/boron carbide core material volume ratio between the range of 0.3 to 4 is achieved; and, (D) consolidating said particles of copper coated boron carbide to produce a structure having a thickness sufficient to provide a boron carbide particle intercepting all lines passing therethrough.

Claim 9

The process as set forth in claim 5 wherein said consolidation step is effected by sintering.

Claim 10

The process as set forth in claim 5 wherein said consolidation step is effected by rolling.

Claim 11

The process as set forth in claim 5 wherein said consolidation step is effected by hot rolling.

Claim 12

The process as set forth in claim 5 wherein said consolidation step is effected by pressing.

Claim 13

The process as set forth in claim 5 wherein said consolidation step is effected by hot pressing.

Claim 14

The process as set forth in claim 5 wherein the boron carbide particle size is within the range of No. 8 and No. 50 grit.