Heat-resistant alloy for welded structures
Assignee: Nippon Steel Corp
•
Filing: 1978-03-15
•
Granted: 1980-10-14
•
Expires: 1998-03-15
Abstract
Abstract A heat-resistant alloy suitable for welded structures, particularly suitable for nuclear reactors, and free from the adverse effect of the cobalt used therein, which alloy has a basic composition comprising; 0.01-0.2% C, not more than 0.50% Si, not more than 0.50% Mn, 10 to 25% Cr, not more than 0.030% B, not more than 0.50% Zr, not more than 20% of (Mo+1/2W), 0.001 to 0.04% Y, not more than 2.0% Al, and not more than 1.0% Ti, with the balance being Ni and unavoidable impurities.
Inventors
- 👤 Yuzo Hosoi
- 👤 Noboru Shinoda
- 👤 Yutaka Tsuchida
- 👤 Shozo Sekino
- 👤 Mizuo Sakakihara
- 👤 Shoji Murota
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:25
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/03; C22C19/05; C22C19/051; C22C19/055
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
206 words
A heat-resistant alloy consisting of: C: 0.01-0.20% Si: not more than 0.50% Mn: not more than 0.50% Cr: 10 to 25% B: not more than 0.030% Zr: not more than 0.50% Mo+1/2W: 5 to 20% W: 10 to 20% when Mo is less than 10% Mo: 10 to 16% when W is 3 to 10% Y: 0.001 to 0.04% Al: not more than 2.0% Ti: not more than 1.0% one or more of Ce, La, Mg, Ca, Nb, Ta, V and Hf in the following amount: Ce, La, Mg, Ca: 0.001 to 0.050% for each and not more than 0.1% in total Nb, Ta, V, Hf: 0.001 to 3.0% for each and not more than 3.0% in total, with the balance being Ni and unavoidable impurities wherein Y E is defined in the equation Y.sub.E =(Y)%+1/5(Zr)%-1.85(S)-3.7(O)% wherein (Y), (Zr), (S) and (O) represent the amount of those respective elements present in the alloy on a weight basis, is in the range from about -0.01 to 0.02%, the alloy possesses a creep rupture strength of more than about 300 hours and wherein the amount of tungsten and molybdenum is within the area defined by the points a, b, c, d, e, and f of FIG. 3 hereof.
Claim 2
Dependent Claim
206 words
A heat-resistant alloy consisting of: C: 0.01-0.20% Si: not more than 0.50% Mn: not more than 0.50% Cr: 10 to 25% B: not more than 0.030% Zr: not more than 0.50% Mo+1/2W: 5 to 20% W: 10 to 20% when Mo is less than 10% Mo: 10 to 16% when W is 3 to 10% Y: 0.001 to 0.04% Al: not more than 2.0% Ti: not more than 1.0% one or more of Ce, La, Mg, Ca, Nb, Ta, V and Hf in the following amount: Ce, La, Mg, Ca: 0.001 to 0.050% for each and not more than 0.1% in total Nb, Ta, V, Hf: 0.001 to 3.0% for each and not more than 3.0% in total, with the balance being Ni and unavoidable impurities wherein Y E is defined in the equation Y.sub.E =(Y)%+1/5(Zr)%-1.85(S)-3.7(O)% wherein (Y), (Zr), (S) and (O) represent the amount of those respective elements present in the alloy on a weight basis, is in the range from about -0.01 to 0.02%, the alloy possesses a creep rupture strength of more than about 300 hours and wherein the amount of tungsten and molybdenum is within the area defined by the points a, b, c, d, e, and f of FIG. 3 hereof.
Claim 3
Dependent Claim
161 words
A heat-resistant alloy for welded structures consisting of: C: 0.01-0.20% Si: not more than 0.50% Mn: not more than 0.50% Cr: 10 to 25% B: not more than 0.030% Zr: not more than 0.50% Mo+1/2W: 5 to 20% W: 10 to 20% when Mo is less than 10% Mo: 10 to 16 % when W is 3 to 10% Y: 0.001 to 0.04% Al: not more than 2.0% Ti: not more than 1.0% with the balance being Ni and unavoidable impurities wherein Y E is defined in the equation Y.sub.E =[Y]%+1/5[Zr]%-1.85[S]%-3.7[O]% wherein [Y], [Zr], [S], and [O] represent the amount of those respective elements present in the alloy on a weight basis, is in the range from about -0.01 to 0.02%, the alloy possesses a creep rupture strength of more than about 300 hours and wherein the amount of tungsten and molybdenum is within the area defined by the points a, b, c, d, e, and f of FIG. 3 hereof.
Claim 4
Dependent Claim
161 words
A heat-resistant alloy for welded structures consisting of: C: 0.01-0.20% Si: not more than 0.50% Mn: not more than 0.50% Cr: 10 to 25% B: not more than 0.030% Zr: not more than 0.50% Mo+1/2W: 5 to 20% W: 10 to 20% when Mo is less than 10% Mo: 10 to 16 % when W is 3 to 10% Y: 0.001 to 0.04% Al: not more than 2.0% Ti: not more than 1.0% with the balance being Ni and unavoidable impurities wherein Y E is defined in the equation Y.sub.E =[Y]%+1/5[Zr]%-1.85[S]%-3.7[O]% wherein [Y], [Zr], [S], and [O] represent the amount of those respective elements present in the alloy on a weight basis, is in the range from about -0.01 to 0.02%, the alloy possesses a creep rupture strength of more than about 300 hours and wherein the amount of tungsten and molybdenum is within the area defined by the points a, b, c, d, e, and f of FIG. 3 hereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-14 | 1984-04-14 | 1984-10-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-14 | 1988-04-14 | 1988-10-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-14 | 1992-04-14 | 1992-10-14 | $7700.00 | Window Closed / Lapsed |