Material separation
Assignee: ENCOMECH ENGINEERING DEVELOPMENTS Ltd
•
Filing: 1978-05-31
•
Granted: 1980-10-14
•
Expires: 1998-05-31
Abstract
Abstract A metal or alloy, present in material containing another metal or alloy having a higher melting point, can be recovered by heating the material in conditions preventing oxidation of the lower melting point metal or alloy, vaporizing this metal or alloy and depositing it on at least one collective surface. The initial heating may be performed in a controlled atmosphere at around atmospheric pressure, e.g. up to the melting point of the lower melting metal or alloy, whereafter the pressure can be reduced and heating continued to effect the vaporization. Apparatus for use in such a process comprises a heating chamber, means for heating the material in said chamber, means for producing higher and lower pressure conditions in said chamber, and condenser means in said chamber or arranged to be put into communication with the chamber in conjunction with the production of said lower pressure condition for the deposition of vaporized lower melting point metal or alloy on said condenser means. The invention may be applied to recovery of tin and lead from tin plate scrap, and more generally to recovery of lower melting point metals and alloys, e.g. zinc, lead or copper, from scrap and refuse.
Inventors
- 👤 William R. Laws
- 👤 Geoffrey R. Reed
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:30
CPC Classifications
C; C22; C22B; C22B7/00; C22B7/001; C22B7/004; C22B25/00; C22B25/06; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
90 words
A process for removing tin from scrap or waste tin plate comprising the steps of initially subjecting the tin plate to a first low temperature heating stage in a current of gas to remove moisture present, thereafter heating the tin plate under vacuum to a second and higher temperature heating stage above the melting point of the tin but below the melting point of the steel base of the tin plate for vaporisation of the tin, and thereafter recovering the vaporised metal by condensation on a cooled surface for collection.
Claim 2
Dependent Claim
90 words
A process for removing tin from scrap or waste tin plate comprising the steps of initially subjecting the tin plate to a first low temperature heating stage in a current of gas to remove moisture present, thereafter heating the tin plate under vacuum to a second and higher temperature heating stage above the melting point of the tin but below the melting point of the steel base of the tin plate for vaporisation of the tin, and thereafter recovering the vaporised metal by condensation on a cooled surface for collection.
Claim 3
Dependent Claim
17 words
A process according to claim 1 wherein the pressure is reduced to less than 10 -4 torr.
Claim 4
Dependent Claim
21 words
A process according to claim 1 wherein the pressure for said final stage is reduced at least to 10 -6 torr.
Claim 5
Dependent Claim
30 words
A process according to claim 1 wherein an electrostatic field is produced in the region of the collecting surface or surfaces for assisting the deposition of the vaporised metal thereon.
Claim 6
Dependent Claim
158 words
A process for recovering tin from tin plate by the application of heat while preventing oxidation of the tin coating, comprising the steps of initially drying the tin plate under ambient pressure by heating to a low temperature level not substantially greater than 180° C.; thereafter heating the dried tin plate to an intermediate temperature level between said low temperature and the temperature at the tin would melt, to break down non-metallic impurities present while simultaneously maintaining a vacuum about said tin plate sufficient to remove the vapour released thereby; subsequently increasing the temperature of said tin plate to a higher level above the melting point of the tin but below the melting point of the steel base of the tin plate while simultaneously maintaining a vacuum of at least 10 -4 torr on said tin plate for a time sufficient to vaporize the tin and collecting the vaporized tin by deposition on at least one collecting surface.
Claim 7
Dependent Claim
158 words
A process for recovering tin from tin plate by the application of heat while preventing oxidation of the tin coating, comprising the steps of initially drying the tin plate under ambient pressure by heating to a low temperature level not substantially greater than 180° C.; thereafter heating the dried tin plate to an intermediate temperature level between said low temperature and the temperature at the tin would melt, to break down non-metallic impurities present while simultaneously maintaining a vacuum about said tin plate sufficient to remove the vapour released thereby; subsequently increasing the temperature of said tin plate to a higher level above the melting point of the tin but below the melting point of the steel base of the tin plate while simultaneously maintaining a vacuum of at least 10 -4 torr on said tin plate for a time sufficient to vaporize the tin and collecting the vaporized tin by deposition on at least one collecting surface.
Claim 8
Dependent Claim
53 words
A process according to claim 5, wherein heating at said relatively low temperature level is within the range of from 150°-180° C., heating to said intermediate temperature level is within the range of from 500°-700° C., and heating above the melting point of the tin is within the range of from 800°-900° C.
Claim 9
Dependent Claim
15 words
A process according to claim 6 wherein the tin plate is agitated while being heated.
Claim 10
Dependent Claim
33 words
A process according to claim 6 wherein the tin plate is in the form of scrap tin cans having lead-containing soldered seams and the lead and tin are vaporised sequentially at different temperatures.
References Cited (Backward Citations)
US896245A
Cited
US1189830A
Cited
US2261406A
Cited
US2268484A
Cited
US3094395A
Cited
US3022161A
Cited
US3512958A
Cited
US3595484A
Cited
US3762911A
Cited
US3756804A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-14 | 1984-04-14 | 1984-10-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-14 | 1988-04-14 | 1988-10-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-14 | 1992-04-14 | 1992-10-14 | $7700.00 | Window Closed / Lapsed |