Process and apparatus for production of spherical grain ferrite powder
Assignee: Dowa Holdings Co Ltd
•
Filing: 1979-03-30
•
Granted: 1980-10-07
•
Expires: 1999-03-30
Abstract
Abstract There is disclosed a novel type of spherical grain-ferrite powder as well as a process and apparatus for the production thereof. A slurry of ferrite-forming powdered raw materials in alcohol is sprayed under applied pressure through a spray nozzle into a high temperature atmosphere of between 700°-1500° C. to allow the combustion of sprayed alcohol therein thereby instantaneously producing spherical grain-ferrite powder.
Inventors
- 👤 Yasuo Watanabe
- 👤 Seizi Isoyama
- 👤 Yoshikazu Yamamichi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:52
CPC Classifications
C; C01; C01G; C01G49/00; C01G49/0018; C01G49/0036; C01G49/0063; C01G49/0072; G; G03; G03G; G03G9/00; G03G9/08; G03G9/10; G03G9/107; G03G9/1075; G03G9/108; G03G9/1085; C01P; C01P2002/00; C01P2002/30; C01P2002/32; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/30; C01P2004/32; C01P2004/60; C01P2004/61; C01P2006/00; C01P2006/10; C01P2006/42
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
167 words
A process for the production of spherical grain ferrite powder which comprises the steps of: suspending impalpable powder of (1) pre-formed ferrite powder or (2) ferrite-forming material, in methyl alcohol to form a suspension consisting of said impalpable powder in said alcohol, said ferrite-forming material being selected from the group consisting of the oxides, hydroxides and carbonates of (i) iron and (ii) at least one ferrite-forming metal element M selected from the group consisting of Mn, Ni, Zn, Co, Mg, Cu, Ba and Sr, and wherein said pre-formed ferrite powders have the formula MO.Fe 2 O 3 ; spraying said suspension into a high temperature zone at a temperature of from about 1200° to about 1300° C.; whereby granulation, and ferrite formation when said impalpable powder is said ferrite-forming material, and sintering of said impalpable powder occurs while they are in said high temperature zone to form spherical ferrite particles with at least 80% of said spherical particles being of a size between 30 and 250 microns.
Claim 2
Dependent Claim
167 words
A process for the production of spherical grain ferrite powder which comprises the steps of: suspending impalpable powder of (1) pre-formed ferrite powder or (2) ferrite-forming material, in methyl alcohol to form a suspension consisting of said impalpable powder in said alcohol, said ferrite-forming material being selected from the group consisting of the oxides, hydroxides and carbonates of (i) iron and (ii) at least one ferrite-forming metal element M selected from the group consisting of Mn, Ni, Zn, Co, Mg, Cu, Ba and Sr, and wherein said pre-formed ferrite powders have the formula MO.Fe 2 O 3 ; spraying said suspension into a high temperature zone at a temperature of from about 1200° to about 1300° C.; whereby granulation, and ferrite formation when said impalpable powder is said ferrite-forming material, and sintering of said impalpable powder occurs while they are in said high temperature zone to form spherical ferrite particles with at least 80% of said spherical particles being of a size between 30 and 250 microns.
Claim 3
Dependent Claim
26 words
A process as in claim 1 in which the solids content of said suspension is 10-70% by weight based on the total weight of the suspension.
Claim 4
Dependent Claim
20 words
A process as in claim 1 in which said suspension is sprayed under applied pressure of 2-50 kg/cm 2 .
Claim 5
Dependent Claim
10 words
A process as in claim 3, wherein M is barium.
Claim 6
Dependent Claim
21 words
A process as in claim 1 in which said reaction is carried out in a whirling upward flow of hot air.
Claim 7
Dependent Claim
21 words
A process as in claim 1, wherein said impalpable powder is in the form of the oxides of said metal elements.
Claim 8
Dependent Claim
15 words
A process as in claim 6, wherein M is a mixture of nickel and zinc.
Claim 9
Dependent Claim
15 words
A process as in claim 1, wherein M is a mixture of nickel and zinc.
Claim 10
Dependent Claim
15 words
A process as in claim 1, wherein M is a mixture of copper and zinc.
Claim 11
Dependent Claim
15 words
A process as in claim 1, wherein M is a mixture of magnesium and zinc.
Claim 12
Dependent Claim
10 words
A process as in claim 1, wherein M is strontium.
Claim 13
Dependent Claim
13 words
A process as in claim 1, wherein said temperature is about 1200° C.
Claim 14
Dependent Claim
20 words
A process as in claim 1, wherein said reaction is carried out in a whirling upward flow of hot air.
Claim 15
Dependent Claim
18 words
A process as in claim 13, wherein said hot air is at a temperature of about 1200° C.
Claim 16
Dependent Claim
23 words
A process as in claim 1, wherein said high temperature zone is at a temperature of from about 1200° to about 1250° C.
Claim 17
Dependent Claim
97 words
The process of claim 1 wherein said impalpable powder is a pre-formed ferrite powder selected from the group consisting of (i) spinel type or hexagonal type pre-formed ferrite powders prepared by solid phase reactions at a temperature of from 800° to 1500° C.; (ii) fine grained spinel-type ferrite powder prepared by the following neutralization method M.sup.2+ +2 Fe.sup.3+ +ROH→MO.Fe.sub.2 O.sub.3 wherein M is selected from the group consisting of Na, K and NH 4 ; and (iii) fine grained simple or complex spinel-type ferrite powders prepared by the following oxidation method M.sup.2+ +2 Fe.sup.3+ +ROH+O.sub.2 ↑→MO.Fe.sub.2 O.sub.3.
Claim 18
Dependent Claim
79 words
The process of claim 1 wherein said impalpable powder is a ferrite-forming powder selected from the group consisting of (i) oxide or carbonates of ferric iron and at least one metal selected from the group consisting of Mn, Ni, Zn, Co, Mg, Cu, Li, Ba, and Sr; and (ii) hydroxides or carbonates or a mixture thereof of ferric iron and at least one metal selected from the group consisting of Ba 2+ and Sr 2+ which have been co-precipitated.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-07 | 1984-04-07 | 1984-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-07 | 1988-04-07 | 1988-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-07 | 1992-04-07 | 1992-10-07 | $7700.00 | Window Closed / Lapsed |