Method for the chemical decontamination of nuclear reactor components
Assignee: Kraftwerk Union AG
•
Filing: 1978-10-26
•
Granted: 1980-10-07
•
Expires: 1998-10-26
Abstract
Abstract Chemical decontamination of equipment contaminated with radioactive material, such as components and systems, particularly water-cooled nuclear reactors, by pretreating with alkaline permanganate, rinsing with demineralized water, treating with a citrate-oxalate solution, rinsing with demineralized water, and post-treating with an acidified hydrogen peroxide solution containing suspended inert particles. Solutions desirably contain no sulfur. The decontamination solution with a pH of about 3.5 and other preferred operating conditions are recited.
Inventors
- 👤 Horst-Otto Bertholdt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 05:38
CPC Classifications
G; G21; G21F; G21F9/00; G21F9/28; G21F9/001; G21F9/002; G21F9/004
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
174 words
Method for the chemical decontamination of radioactively contaminated equipment constructed of a metal selected from the group consisting of chrome-nickel steel, nickel alloys or chrome alloy steel, which comprises subjecting the contaminated equipment to three stages of treatment with an intermediate rinsing with demineralized water between stages as follows: (a) pretreating the contaminated equipment with an aqueous alkaline permanganate solution at a temperature of 85° C. to 125° C. for about 2 hours (b) rinsing the equipment after treatment with the alkaline permanganate with demineralized water (c) treating the rinsed equipment with an aqueous decontamination solution with a pH-value adjusted to about 3.5, containing a citrate and oxalate and an inhibitor, at a temperature of 85° C. to 125° C. for about 2 to 20 hours (d) rinsing the equipment after treatment with the citrate-oxalate with demineralized water, and (e) post-treating the rinsed equipment with an aqueous solution of an organic acid and hydrogen peroxide containing suspended inert particles at a temperature of 20° C. to 80° C. for about 2 to 8 hours.
Claim 2
Dependent Claim
174 words
Method for the chemical decontamination of radioactively contaminated equipment constructed of a metal selected from the group consisting of chrome-nickel steel, nickel alloys or chrome alloy steel, which comprises subjecting the contaminated equipment to three stages of treatment with an intermediate rinsing with demineralized water between stages as follows: (a) pretreating the contaminated equipment with an aqueous alkaline permanganate solution at a temperature of 85° C. to 125° C. for about 2 hours (b) rinsing the equipment after treatment with the alkaline permanganate with demineralized water (c) treating the rinsed equipment with an aqueous decontamination solution with a pH-value adjusted to about 3.5, containing a citrate and oxalate and an inhibitor, at a temperature of 85° C. to 125° C. for about 2 to 20 hours (d) rinsing the equipment after treatment with the citrate-oxalate with demineralized water, and (e) post-treating the rinsed equipment with an aqueous solution of an organic acid and hydrogen peroxide containing suspended inert particles at a temperature of 20° C. to 80° C. for about 2 to 8 hours.
Claim 3
Dependent Claim
31 words
Method according to claim 1, wherein the alkaline permanganate solution has the following composition in the proportions: 10to 50 g sodium hydroxide 5 to 30 g potassium permanganate 1000 ml water.
Claim 4
Dependent Claim
18 words
Method according to claim 1, wherein permanganate solution is alkalized by means of hydroxides of the alkali metals.
Claim 5
Dependent Claim
53 words
Method according to claim 1, wherein the decontamination solution contains the following substances per 1000 ml water: 25 to 50 g citric acid 20 to 40 g oxalic acid 2 to 4 g ethylenediamine tetraacetic acid ≧5 g Fe-III formate as well as ammonia for adjusting the pH-value of the solution to 3.5.
Claim 6
Dependent Claim
19 words
Method according to claim 4, wherein the oxalic acid/citric acid/ethylenediamine tetraacetic acid ratio in the decontamination solution is 10:12.5:1.
Claim 7
Dependent Claim
17 words
Method according to claim 1, wherein all said solutions used are free of sulfur or sulfur-containing compounds.
Claim 8
Dependent Claim
23 words
Method according to claim 1, wherein the inhibitor of the decontamination solution is a two- or three-valent metal salt of an organic acid.
Claim 9
Dependent Claim
16 words
Method according to claim 1, wherein the pH-value is held constant at 3.5±0.5 during the decontamination.
Claim 10
Dependent Claim
37 words
Method according to claim 1, wherein the suspension solution contains the following substances per 1000 ml water: ≧1.0 g citric acid ≧0.5 g hydrogen peroxide 0.1 to 0.5 g perfluoro-carbonic acid 0.1 to 5 g cellulose fibers.
Claim 11
Dependent Claim
39 words
Method according to claim 1, wherein the inert material in the suspension solution are fibers of organic or inorganic substances with the following dimensions: Length: 0.5 to 15 mm Diameter: 0.05 to 1 mm Density: ≧1 g/cm 3 .
Claim 12
Dependent Claim
23 words
Method according to claim 1, wherein in the suspension solution, fabric cuttings with a size of 0.2 to 4 cm 2 are used.
Claim 13
Dependent Claim
14 words
Method according to claim 1, wherein in the suspension, rubber sponge balls are used.
Claim 14
Dependent Claim
48 words
Method according to claim 1, wherein the acid in the suspension solution is selected from the group consisting of an organic acid containing a carboxyl group, an organic acid containing dicarboxyl groups and an organic acid containing at least one hydroxy group and at least one carboxyl group.
Claim 15
Dependent Claim
16 words
Method according to claim 1, wherein the organic acid in the suspension solution is citric acid.
Claim 16
Dependent Claim
26 words
Method according to claim 1, including the addition of an organic wetting agent to the suspension solution to reduce the surface tension of the suspension solution.
References Cited (Backward Citations)
US2801824A
Cited
US3080262A
Cited
US3013909A
Cited
US3272650A
Cited
US3275562A
Cited
US3496017A
Cited
US3873362A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-07 | 1984-04-07 | 1984-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-07 | 1988-04-07 | 1988-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-07 | 1992-04-07 | 1992-10-07 | $7700.00 | Window Closed / Lapsed |