Heather yarn made by combining polyester and polyamide yarns
Assignee: DuPont Canada Inc
•
Filing: 1979-04-16
•
Granted: 1980-10-07
•
Expires: 1999-04-16
Abstract
Abstract A continuous process is disclosed for producing a heather yarn from a continuous filament polyester feed yarn having a residual draw ratio in the range of from 1.6 to 2.0 and a continuous filament polyamide feed yarn having a residual draw ratio in the range of from 106 to 120 percent of the residual draw ratio of the polyester feed yarn. The process involves the steps of: (1) combining the yarns; (2) false twist texturing and drawing the combined yarns in a draw-texturing zone comprising feed rolls, a heating means, a friction twisting element and draw rolls; (3) randomly entangling the combined and textured yarns together in a jet-intermingling zone formed by an air jet device; and (4) withdrawing the heather yarn so produced.
Inventors
- 👤 Bruce D. Mountney
- 👤 Ralph C. Wirsig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:18
CPC Classifications
D; D02; D02G; D02G3/00; D02G3/22; D02G3/34; D02G3/346; D02G1/00; D02G1/02; D02G1/0286; Y; Y10; Y10S; Y10S57/00; Y10S57/908
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
129 words
A continuous process for producing heather yarn comprising the steps of combining a continuous filament polyester feed yarn having a residual draw ratio in the range of from 1.6 to 2.0 with a continuous filament polyamide feed yarn having a residual draw ratio in the range of from 106 to 120 percent of the residual draw ratio of the polyester feed yarn, feeding the combined yarns to a draw-texturing zone, false twist texturing and drawing the combined yarns in the draw-texturing zone at a draw ratio equivalent to 95 to 105 percent of the residual draw ratio of the polyester feed yarn, feeding the combined yarns from the draw-texturing zone to a jet-intermingling zone, randomly entangling the combined yarns together in the jet-intermingling zone and withdrawing the heather yarn.
Claim 2
Dependent Claim
129 words
A continuous process for producing heather yarn comprising the steps of combining a continuous filament polyester feed yarn having a residual draw ratio in the range of from 1.6 to 2.0 with a continuous filament polyamide feed yarn having a residual draw ratio in the range of from 106 to 120 percent of the residual draw ratio of the polyester feed yarn, feeding the combined yarns to a draw-texturing zone, false twist texturing and drawing the combined yarns in the draw-texturing zone at a draw ratio equivalent to 95 to 105 percent of the residual draw ratio of the polyester feed yarn, feeding the combined yarns from the draw-texturing zone to a jet-intermingling zone, randomly entangling the combined yarns together in the jet-intermingling zone and withdrawing the heather yarn.
Claim 3
Dependent Claim
33 words
The process according to claim 1 in which the combined yarns are drawn in the draw-texturing zone at a draw ratio substantially equal to the residual draw ratio of the polyester feed yarn.
Claim 4
Dependent Claim
37 words
The process according to claim 2 including the step of feeding the combined yarns from the jet intermingling zone to a heating zone in order to heat set the combined yarns prior to withdrawing the heather yarn.
Claim 5
Dependent Claim
43 words
The process according to claim 3 in which the heather yarn is withdrawn from heating zone at a speed in the range of from 6 to 17 percent slower than the speed at which the combined yarns are fed to the jet-intermingling zone.
Claim 6
Dependent Claim
54 words
The process according to claim 1 in which the polyester feed yarn has a residual draw ratio in the range of from 1.7 to 1.9 and the polyamide feed yarn has a residual draw ratio in the range of from 110 to 117 percent of the residual draw ratio of the polyester feed yarn.
Claim 7
Dependent Claim
31 words
The process according to claim 5 in which the polyester feed yarn has a residual draw ratio of 1.65 and the polyamide feed yarn has a residual draw ratio of 1.86.
Claim 8
Dependent Claim
35 words
The process according to any one of claim 1, claim 3 and claim 6 in which the polyester feed yarn is made from poly(ethylene terephthalate) and the polyamide feed yarn is made from poly(hexamethylene adipamide).
Claim 9
Dependent Claim
59 words
The process according to claim 1, except that the residual draw ratio of the polyamide feed yarn is 104 to 118 percent of the residual draw ratio of the polyester feed yarn, and that the combined yarns are drawn at a draw ratio equivalent to at least 95 percent of the residual draw ratio of the polyester feed yarn.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-07 | 1984-04-07 | 1984-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-07 | 1988-04-07 | 1988-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-07 | 1992-04-07 | 1992-10-07 | $7700.00 | Window Closed / Lapsed |