Abstract
Abstract A gas composition detector, particularly an oxygen concentration detector includes a metal oxide an electrical resistance or an electromotive force of which is changed by oxygen ions which are conducted in accordance with a difference between an oxygen concentration of gas being examined and an oxygen concentration of a reference gas. A surface of the metal oxide is coated with a conductive metal electrode, and a metal which is the same as or different than the conductive metal penetrates into the metal oxide at the interface of the metal oxide and the conductive metal, whereby the tear-off of the electrode is prevented.
Inventors
- 👤 Kazuo Tanaka
- 👤 Osamu Takenaka
- 👤 Masatosi Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 15:17
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4073; G01N27/4075
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
228 words
A method for manufacturing a gas composition detector comprising a metal oxide mixture, the electrical resistance or the electromotive force of which changes with the concentration of the gas composition of gas to be examined, said method comprising the steps of: pre-calcining said metal oxide mixture to form a preform detection element having a porous surface of sufficient porosity to permit a aqueous solution including a conductive metal component to penetrate said pre-calcined detection element; spraying said aqueous solution including said conductive metal component on said pre-calcined element; drying said pre-calcined detection element; firing said detection element to cause further sintering of said element whereby said porous surface is concentrated and some particles of said conductive metal component penetrate the concentrated porous surface of said detection element while other particles remain on said surface, to cause the penetrated particles and the other particles of said conductive metal component to be strongly deposited on the porous surface; and forming an electrode layer of the same metal as said conductive metal component on a surface of the fired detection element through said conductive metal component, the metal protrusions on the surface of the detection element from said strongly deposited conductive metal component serving as a base for the metal plating in said forming step to provide strong adhesion between the metal layers in the first and second metal deposition steps.
Claim 2
Independent Claim
228 words
A method for manufacturing a gas composition detector comprising a metal oxide mixture, the electrical resistance or the electromotive force of which changes with the concentration of the gas composition of gas to be examined, said method comprising the steps of: pre-calcining said metal oxide mixture to form a preform detection element having a porous surface of sufficient porosity to permit a aqueous solution including a conductive metal component to penetrate said pre-calcined detection element; spraying said aqueous solution including said conductive metal component on said pre-calcined element; drying said pre-calcined detection element; firing said detection element to cause further sintering of said element whereby said porous surface is concentrated and some particles of said conductive metal component penetrate the concentrated porous surface of said detection element while other particles remain on said surface, to cause the penetrated particles and the other particles of said conductive metal component to be strongly deposited on the porous surface; and forming an electrode layer of the same metal as said conductive metal component on a surface of the fired detection element through said conductive metal component, the metal protrusions on the surface of the detection element from said strongly deposited conductive metal component serving as a base for the metal plating in said forming step to provide strong adhesion between the metal layers in the first and second metal deposition steps.
Claim 3
Dependent Claim
46 words
A method for manufacturing a gas composition detector according to claim 1, wherein said calcining step includes calcining the detection element consisting of 85 mole % of zirconium oxide and 15 mole % of calcium oxide at 1300° C. to 1400° C. for about 10 hours.
Claim 4
Dependent Claim
59 words
A method for manufacturing a gas composition detector according to claim 2, wherein said spraying step of said aqueous solution includes spraying a solution of chloroplatinic acid at a concentration of 5 g/1 and a solution of sodium hydroborate at the concentration of 4 g/l simultaneously on a surface of the calcined detection element for 5 to 15 seconds.
Claim 5
Dependent Claim
33 words
A method for manufacturing a gas composition detector according to claim 3, wherein the ratio of the spray amount by weight of said chloroplatinic acid to that of said sodium borohydrate is 1.
Claim 6
Dependent Claim
31 words
A method for manufacturing a gas composition detector according to claim 3, wherein said drying step is carried out at 80° C. to 100° C. for about 0.5 to 1 hour.
Claim 7
Dependent Claim
29 words
A method for manufacturing a gas composition detector according to claim 5, wherein said firing step is carried out at 1600° C. to 1700° C. for about 2 hours.
References Cited (Backward Citations)
US2950996A
Cited
US3630768A
Cited
US3653946A
Cited
US3978006A
Cited
US3841987A
Cited
US3843400A
Cited
US3935089A
Cited
US3983266A
Cited
US4080276A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-30 | 1984-03-31 | 1984-09-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-30 | 1988-03-31 | 1988-09-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-30 | 1992-03-31 | 1992-09-30 | $7700.00 | Window Closed / Lapsed |