Porous carbon support materials useful in chromatography and their preparation

Assignee: Merck Patent GmbH
•
Filing: 1979-01-23
•
Granted: 1980-09-30
•
Expires: 1999-01-23
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A process for preparing porous carbon support materials comprises treating activated carbon or coke, having a particle size of about 5 to about 50 μm, a specific surface area of about 10 to 1,000 m 2 /g, a hardness of at least about 95% attrition resistance, with solvent or solvents, and then heat treating the activated carbon or coke at a temperature of about 2,400-3,000° C. under an inert, gas atmosphere; said solvent or solvents affecting the mineral and organic impurities in the activated carbon or coke such that after said subsequent heat treatment, substantially all of said impurities are removed. A hard, mechanically stable, porous carbon support material consisting essentially of highly purified activated carbon, highly purified coke or a mixture thereof, said support material having a carbon content of at least 99%, a specific surface area of about 1 to about 5 m 2 /g and a particle size of about 5 to about 50 μm, may be prepared in this way.

Inventors

  • 👤 Klaus Unger
  • 👤 Heinz Gotz

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-10-27 06:41
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/02; B01J20/20; C; C01; C01B; C01B32/00; C01B32/30; C01B32/354; C01B32/378

Claims Analysis

Total Claims: 7
Claim 1
Independent Claim 108 words
A process for preparing porous carbon support materials useful in chromatography, which comprises treating activated carbon or coke, having a particle size of about 5 to about 50 μm, a specific surface area of about 10 to about 1,000 m 2 /g, and a hardness of at least about 95% attrition resistance, with a solvent or solvents, and then heat treating the activated carbon or coke at a temperature of about 2,400°-3,000° C. under an inert, gas atmosphere; said solvent or solvents affecting the mineral and/or organic impurities in the activated carbon or coke, such that, after said subsequent heat treatment, substantially all of said impurities are removed.
Claim 2
Dependent Claim 108 words
A process for preparing porous carbon support materials useful in chromatography, which comprises treating activated carbon or coke, having a particle size of about 5 to about 50 μm, a specific surface area of about 10 to about 1,000 m 2 /g, and a hardness of at least about 95% attrition resistance, with a solvent or solvents, and then heat treating the activated carbon or coke at a temperature of about 2,400°-3,000° C. under an inert, gas atmosphere; said solvent or solvents affecting the mineral and/or organic impurities in the activated carbon or coke, such that, after said subsequent heat treatment, substantially all of said impurities are removed.
Claim 3
Dependent Claim 31 words
The process of claim 1, wherein the solvent treatment comprises extracting the activated carbon or coke with an aqueous acid or acids and then repeatedly evaporating after addition of hydrofluoric acid.
Claim 4
Dependent Claim 43 words
The process of claim 2, wherein the solvent treatment comprises extracting the activated carbon or coke 3-5 times with about 20% hydrochloric acid for a total of about 72 hours, and then evaporating to dryness about 3 times after addition of hydrofluoric acid.
Claim 5
Dependent Claim 64 words
A hard, mechanically stable, porous carbon support material useful in chromatography consisting essentially of highly purified activated carbon, highly purified coke, or a mixture thereof, said support material having a carbon content of at least 99%, a specific surface area of about 1 to about 5 m 2 /g a particle size of about 5 to about 50 μm and a graphitzed carbon surface.
Claim 6
Dependent Claim 64 words
A hard, mechanically stable, porous carbon support material useful in chromatography consisting essentially of highly purified activated carbon, highly purified coke, or a mixture thereof, said support material having a carbon content of at least 99%, a specific surface area of about 1 to about 5 m 2 /g a particle size of about 5 to about 50 μm and a graphitzed carbon surface.
Claim 7
Dependent Claim 40 words
The porous carbon support material of claim 1 having a carbon content of at least 99%, a specific surface area of about 1 to about 5 m 2 /g and a particle size of about 5 to about 50 μm.

References Cited (Backward Citations)

US2734800A Cited
US3869302A Cited
US4066699A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1983-09-30 1984-03-31 1984-09-30 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1987-09-30 1988-03-31 1988-09-30 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1991-09-30 1992-03-31 1992-09-30 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag