Imitation-leather material and method of preparing such material

Claim 2

In a method of preparing an imitation leather sheet material, which method comprises: (a) coating a thin, wet foam layer of a foam latex composition onto a flexible sheet material, the latex composition comprising a film-forming, elastomeric, cross-linkable, carboxylated polymer and a cross-linking agent for the carboxylated polymer; (b) placing a fibrous base steet material onto the top surface of the wet foam latex layer to provide a wet laminate product; and (c) heating the wet laminate product to dry and cure the foam layer and to provide a dry laminate product, the improvement which comprises: (i) providing a heat-coagulable, polymeric acidic latex composition as the wet foam layer and wherein the latex composition includes an acid or an acid salt to reduce the pH to less than 5.0, and (ii) shock-heating the wet foam layer of the wet laminate product by rapidly heating the wet foam layer in a single heating oven operation and in a single temperature step to a temperature of not greater than 450° F. and greater than about 250° F. to heat-coagulate rapidly the acidic polymer to a fine, dense, open-cell foam structure and to remove water rapidly from the coagulated foam layer without blistering of the foam layer to form a dry foam layer and to cross-link the coagulated dried polymer, all during such single temperature step and in such single oven.

Claim 3

The method of claim 1 wherein the polymer has a gel temperature of from about 125° F. or less.

Claim 4

The method of claim 1 wherein the latex composition has a pH of from about 2.0 to 5.0.

Claim 5

The method of claim 1 wherein the latex composition includes a paratoluene sulfonic acid or acid salt to reduce the pH to a pH of from about 2.0 to 3.5.

Claim 6

The method of claim 1 wherein the latex composition includes a heat-sensitizing coagulant which comprises a polysiloxane compound.

Claim 7

The method of claim 1 wherein the polymer comprises a carboxylated, acrylonitrile-butadiene elastomeric polymer and the curing agent is a methylated amino resin.

Claim 8

The method of claim 1 wherein the latex composition includes from about 5% to 30% by weight of the composition of a vinyl-halide polymer.

Claim 9

The method of claim 1 wherein the heat-coagulated dry foam layer and the dry laminate product has a dry foam density of greater than about 50 pounds per cubic foot.

Claim 10

The method of claim 1 wherein the fibrous base sheet comprises a nap fabric sheet and the nap fabric side of the sheet is placed in contact with the wet foam layer, and wherein the flexible sheet material comprises a thin, elastomeric urethane resin or a vinyl-halide resin on a release paper, and which method includes the step of stripping the release paper from the resin layer to provide an imitation-leather sheet laminate material.

Claim 11

The method of claim 1 wherein the dry heat-coagulated foam layer has a thickness of from about 5 to 50 mils.

Claim 12

The method of claim 1 wherein the flexible sheet material comprises a release paper, and which includes the step of stripping the release paper from the dry foam layer of the dry laminate product to provide an imitation-leather sheet material which comprises the dry heat-coagulated polymer as a dry layer bonded to the fibrous base sheet material.

Claim 13

The method of claim 1 wherein the latex composition has a pH of less than 5.0 and includes a small amount of a paratoluene sulfonic acid, and shock-heating of the wet laminate product is carried out at a temperature of from 275° F. to 350° F.

Claim 14

The product produced by the method of claim 1.

Claim 15

The product produced by the method of claim 1 wherein the flexible sheet material is stripped from the dry laminate product to provide an imitation-leather sheet material.

Claim 16

In a method of preparing an imitation leather laminate sheet material, which method comprises: coating a thin, wet foam layer of from about 5 to 100 mils of a foamed carboxylated acrylonitrile-butadiene latex composition onto a thin, top skin layer of a urethane resin or vinyl-chloride resin on a release paper, the latex composition containing a methylated amino resin cross-linking agent for the carboxylated polymer and a foaming agent to permit mechanical frothing of the latex composition, placing a napped fabric sheet material onto the top surface of the wet foam layer, the napped surface down and in contact with the wet foam layer to provide a wet laminate product, and heating the wet laminate product to dry and cure the foam layer, and, thereafter, removing the release sheet from the urethane resin or vinyl-chloride resin layer to provide an imitation-leather substitute material, the improvement which comprises: (a) providing a heat-coagulable, polymeric, acrylonitrile-butadiene, carboxylated polymer composition which has a pH of less than 5.0 and which contains paratoluene sulfonic acid, to provide a heat-coagulated polymer having a gel temperature of about 125° F. or less; and (b) shock-heating the wet foam layer of the wet laminate product by rapidly heating the wet foam layer in a single heating oven operation and in a single temperature step to a temperature of from about 275° F. to 350° F. to heat-coagulate rapidly the carboxylated acrylonitrile-butadiene polymer into a fine, dense, open-cell foam structure, the foam having a dry density of about 50 pounds per cubic foot or greater to remove water rapidly from the coagulated foam layer without blistering of the foam layer to form a dry foam layer and to cross-link the coagulated dried polymer, all during such single temperature step and in such single oven.

Claim 17

In a method of preparing an imitation leather laminate sheet material, which method comprises: coating a thin, wet foam layer of from about 5 to 100 mils of a foamed carboxylated acrylonitrile-butadiene latex composition onto a thin, top skin layer of a urethane resin or vinyl-chloride resin on a release paper, the latex composition containing a methylated amino resin cross-linking agent for the carboxylated polymer and a foaming agent to permit mechanical frothing of the latex composition, placing a napped fabric sheet material onto the top surface of the wet foam layer, the napped surface down and in contact with the wet foam layer to provide a wet laminate product, and heating the wet laminate product to dry and cure the foam layer, and, thereafter, removing the release sheet from the urethane resin or vinyl-chloride resin layer to provide an imitation-leather substitute material, the improvement which comprises: (a) providing a heat-coagulable, polymeric, acrylonitrile-butadiene, carboxylated polymer composition which has a pH of less than 5.0 and which contains paratoluene sulfonic acid, to provide a heat-coagulated polymer having a gel temperature of about 125° F. or less; and (b) shock-heating the wet foam layer of the wet laminate product by rapidly heating the wet foam layer in a single heating oven operation and in a single temperature step to a temperature of from about 275° F. to 350° F. to heat-coagulate rapidly the carboxylated acrylonitrile-butadiene polymer into a fine, dense, open-cell foam structure, the foam having a dry density of about 50 pounds per cubic foot or greater to remove water rapidly from the coagulated foam layer without blistering of the foam layer to form a dry foam layer and to cross-link the coagulated dried polymer, all during such single temperature step and in such single oven.

Claim 20

The method of claim 16 wherein the paper-release sheet has an embossed design thereon, whereby, on stripping the paper-release sheet from the dry, coagulated foam layer, the foam layer having an embossed design thereon.

Claim 21

The laminate product produced by the method of claim 16.

Claim 22

The laminate product produced by the method of claim 15.