US4224177A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Fixation of radioactive materials in a glass matrix
Assignee: Individual
•
Filing: 1978-03-09
•
Granted: 1980-09-23
•
Expires: 1998-03-09
Abstract
Abstract This invention relates to radioactive materials which are fixed, stored, entrapped, encapsulated, or otherwise rendered immobile in a glass matrix for extremely long periods of time. Radioactive material such as radioactive wastes are incorporated into a glass matrix by a process of "molecular stuffing" a porous glass either with a radioactive gas which is trapped in the porous glass by dissolution during sintering of the pores of the glass, or with a salt solution containing radioactive material such as CsNO 3 , Sr(NO 3 ), etc., or with a combination of both salt solution and radioactive gas, followed by drying and sintering of the pores of the glass whereby these radioactive materials upon chemical change to their oxides, excepting of course the noble gases which remain in molecular form, become a part of the integrated glass structure. The resulting glass article may have the radioactive material dispersed essentially homogeneously throughout the glass article, or there may be a layer free of such radioactive waste material over the entire surface of the glass article. In either case such glass articles demonstrate an extremely slow diffusion of the encapsulated radioactive material to the surrounding area.
Inventors
- 👤 Pedro B. Macedo
- 👤 Joseph H. Simmons
- 👤 Theodore A. Litovitz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:00
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/002; C03C23/00; C03C23/0095; C03C4/00; G; G21; G21F; G21F9/00; G21F9/28; G21F9/30; G21F9/301; G21F9/302; G21F9/305
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
91 words
A non-porous glass composition containing radioactive materials encapsulated and immobilized in the glass matrix, said composition bein characterized by: (a) containing and at least 75 mol percent SiO 2 , (b) having a radiation activity above one millicurie per cubic centimeter of said composition, (c) having high chemical durability to aqueous solution, and (d) containing immobilized oxides of said radioactive material chemically incoporated into the silica structure thereof whereby leakage of said oxides of the radioactive components to the environment at environmental temperature is prevented for extremely long periods of time.
Claim 2
Dependent Claim
91 words
A non-porous glass composition containing radioactive materials encapsulated and immobilized in the glass matrix, said composition bein characterized by: (a) containing and at least 75 mol percent SiO 2 , (b) having a radiation activity above one millicurie per cubic centimeter of said composition, (c) having high chemical durability to aqueous solution, and (d) containing immobilized oxides of said radioactive material chemically incoporated into the silica structure thereof whereby leakage of said oxides of the radioactive components to the environment at environmental temperature is prevented for extremely long periods of time.
Claim 3
Dependent Claim
21 words
The composition of claim 1 wherein at least 0.1 mol percent radioactive material is encapsulated and immobilized in the glass matrix.
Claim 4
Dependent Claim
42 words
The composition of claim 1 wherein said radioactive material comprises at least five oxides selected from the group consisting of carbon, rubidium, strontium, lanthanides, cobalt, cadmium, silver, zirconium, niobium, molybdenum, technetium, ruthenium, rhodium, palladium, tellurium, cesium, barium, francium, yttrium, radium, and actinides.
Claim 5
Dependent Claim
21 words
The composition of claim 1 characterized by a radiation activity of at least one curie per cubic centimeter of said composition.
Claim 6
Dependent Claim
18 words
The composition of claim 1 wherein said radioactive material further includes dissolved radioactive gases in the glass matrix.
Claim 7
Dependent Claim
51 words
A low-level radioactive, non-porous glass composition comprising: (a) at least 75 mol percent SiO 2 ; (b) high chemical durability to aqueous solution; and (c) the oxides of boron, cobalt and cesium chemically fixed and immobilized in the glass matrix, said oxides being derived from low-level radioactive contaminated boric acid wastes.
Claim 8
Dependent Claim
51 words
A low-level radioactive, non-porous glass composition comprising: (a) at least 75 mol percent SiO 2 ; (b) high chemical durability to aqueous solution; and (c) the oxides of boron, cobalt and cesium chemically fixed and immobilized in the glass matrix, said oxides being derived from low-level radioactive contaminated boric acid wastes.
Claim 9
Dependent Claim
93 words
A glass article characterized by (a) an outer glass clad or skin composition of at least 90 mol percent SiO 2 and substantially free of radioactive material, (b) an inner core composition of at least 75 mol percent SiO 2 and containing B 2 O 3 and the oxide of a radioactive element chemically immobilized in the glass article, (c) the concentration of said radioactive element being at least sufficient to provide radiation activity greater than one millicurie per cubic centimeter of said glass article; and (d) high chemical durability to aqueous solution.
Claim 10
Dependent Claim
93 words
A glass article characterized by (a) an outer glass clad or skin composition of at least 90 mol percent SiO 2 and substantially free of radioactive material, (b) an inner core composition of at least 75 mol percent SiO 2 and containing B 2 O 3 and the oxide of a radioactive element chemically immobilized in the glass article, (c) the concentration of said radioactive element being at least sufficient to provide radiation activity greater than one millicurie per cubic centimeter of said glass article; and (d) high chemical durability to aqueous solution.
Claim 11
Dependent Claim
12 words
The glass article of claim 7 wherein the radioactive element comprises cesium.
Claim 12
Independent Claim
110 words
A method of preventing the dissemination of radioactive material into the environment which comprises (a) impregnating the pores of a porous glass preform with radioactive material, said preform being characterized by an interconnected porous structure, and containing at least 75 mol percent SiO 2 , (b) heating said preform to decompose said radioactive material to its corresponding oxide and further heating to sintering temperature to collapse the porous structure thereof, and (c) cooling the resultant nonporous glass product which contains an amount of radioactive material encapsulated and immobilized in said glass product and sufficient to provide radiation activity greater than at least one millicurie per cubic centimeter of glass product.
Claim 13
Independent Claim
110 words
A method of preventing the dissemination of radioactive material into the environment which comprises (a) impregnating the pores of a porous glass preform with radioactive material, said preform being characterized by an interconnected porous structure, and containing at least 75 mol percent SiO 2 , (b) heating said preform to decompose said radioactive material to its corresponding oxide and further heating to sintering temperature to collapse the porous structure thereof, and (c) cooling the resultant nonporous glass product which contains an amount of radioactive material encapsulated and immobilized in said glass product and sufficient to provide radiation activity greater than at least one millicurie per cubic centimeter of glass product.
Claim 14
Dependent Claim
13 words
The method of claim 9 wherein said radioactive material comprises radioactive nuclear wastes.
Claim 15
Dependent Claim
35 words
The method of claim 9 wherein the preform, after the impregnation step, is treated to remove radioactive material from the surface thereof thereby producing an outer surface layer which is substantially free of radioactive material.
Claim 16
Dependent Claim
22 words
The method of claim 9 wherein before the collaspsing step, the porous glass preform as further impregnated with a radioactive gaseous isotope.
Claim 17
Dependent Claim
21 words
The method according to claim 9 further comprising incorporating the non-porous glass product into an instrument as a source of radioactivity.
Claim 18
Dependent Claim
13 words
The method according to claim 13 further comprising destroying microorganisms employing said instrument.
Claim 19
Dependent Claim
20 words
An instrument containing as a source of radiation the non-porous glass product of the method of defined in claim 9.
Claim 20
Independent Claim
143 words
A method of preventing the dissemination of radioactive material selected from the group of normally radioactive gases and volatilizable materials which yield radioactive gases which comprises (a) impregnating the pores of a porous glass preform with a dopant to increase the surface are thereof, said preform being characterized by an interconnected porous structure and a SiO 2 content of at least 75 mol percent, (b) removing said dopant from the surface of the preform to thus product a skin or outer clad which is substantially free of said dopant and an inner code region containing substantial quantities of dopant therein; (c) drying said preform; (d) impregnating the pores of the dried preform with the abovesaid radioactive material; (e) heating said preform to sintering temperature to collapse the porous structure of the preform thereby encapsulating and immobilizing the radioactive material in the glass matrix.
Claim 21
Independent Claim
143 words
A method of preventing the dissemination of radioactive material selected from the group of normally radioactive gases and volatilizable materials which yield radioactive gases which comprises (a) impregnating the pores of a porous glass preform with a dopant to increase the surface are thereof, said preform being characterized by an interconnected porous structure and a SiO 2 content of at least 75 mol percent, (b) removing said dopant from the surface of the preform to thus product a skin or outer clad which is substantially free of said dopant and an inner code region containing substantial quantities of dopant therein; (c) drying said preform; (d) impregnating the pores of the dried preform with the abovesaid radioactive material; (e) heating said preform to sintering temperature to collapse the porous structure of the preform thereby encapsulating and immobilizing the radioactive material in the glass matrix.
Claim 22
Dependent Claim
67 words
The method of claim 25 wherein the temperature of the heating step is controlled to first collapse the porous structure of the inner core region while remaining below the temperature at which the skin or outer clad of the preform sinters, removing radioactive gases from the environment of the preform, thereafter raising the temperature to sinter and collapse the porous structure of the skin or outer clad.
Claim 23
Independent Claim
175 words
A method for the storage of dangerous radioactive nuclear waste products in glass for extraordinarily long periods of time which comprises: (a) impregnating the interconnected pores of a porous glass preform with a liquid waste comprising radioactive nuclear waste products comprising radioactive material capable of decomposing to its oxide form at a temperature below the sintering temperature of said preform, (b) causing said radioactive material to precipitate within the pores of said preform, (c) drying said preform, (d) causing said radioactive material to be converted to the oxide form at a temperature below the sintering temperature of said preform, (e) heating said preform to sintering temperature to collapse the pores of said preform whereby the radioactive material in the form of its oxide is incorporated into the silica structure, and (f) obtaining a radioactive, non-porous glass product characterized by immobilized radioactive material in the form of its oxide incorporated into the silica structure thereof whereby leakage of said immobilized radioactive material to the environment at environmental temperatures is prevented for extraordinarily long periods of time.
Claim 24
Independent Claim
175 words
A method for the storage of dangerous radioactive nuclear waste products in glass for extraordinarily long periods of time which comprises: (a) impregnating the interconnected pores of a porous glass preform with a liquid waste comprising radioactive nuclear waste products comprising radioactive material capable of decomposing to its oxide form at a temperature below the sintering temperature of said preform, (b) causing said radioactive material to precipitate within the pores of said preform, (c) drying said preform, (d) causing said radioactive material to be converted to the oxide form at a temperature below the sintering temperature of said preform, (e) heating said preform to sintering temperature to collapse the pores of said preform whereby the radioactive material in the form of its oxide is incorporated into the silica structure, and (f) obtaining a radioactive, non-porous glass product characterized by immobilized radioactive material in the form of its oxide incorporated into the silica structure thereof whereby leakage of said immobilized radioactive material to the environment at environmental temperatures is prevented for extraordinarily long periods of time.
Claim 25
Dependent Claim
12 words
The method of claim 18 wherein said radioactive material comprises nitrate compounds.
Claim 26
Dependent Claim
93 words
A non-porous glass composition containing radioactive material encapsulated and immobilized in a glass matrix, derived from a porous silica glass, said composition being characterized by: (a) at least 75 mol percent SiO 2 , (b) a radiation activity above one millicurie per cubic centimeter of said composition, (c) high chemical durability to aqueous solution, and (d) an immobilized oxide of said radioactive material chemically incorporated into the silica structure thereof whereby leakage of said oxide of the radioactive component to the environment at environmental temperatures is prevented for extremely long periods of time.
Claim 27
Dependent Claim
93 words
A non-porous glass composition containing radioactive material encapsulated and immobilized in a glass matrix, derived from a porous silica glass, said composition being characterized by: (a) at least 75 mol percent SiO 2 , (b) a radiation activity above one millicurie per cubic centimeter of said composition, (c) high chemical durability to aqueous solution, and (d) an immobilized oxide of said radioactive material chemically incorporated into the silica structure thereof whereby leakage of said oxide of the radioactive component to the environment at environmental temperatures is prevented for extremely long periods of time.
Claim 28
Dependent Claim
23 words
A non-porous glass composition as claimed in claim 20 having a radiation activity of one curie per cubic centimeter of said glass composition.
Claim 29
Dependent Claim
91 words
A non-porous glass composition containing radioactive material, derived from nuclear waste, encapsulated and immobilized in the glass matrix, said composition being characterized by: (a) at least 75 mol percent SiO 2 , (b) a radiation activity above one millicurie per cubic centimeter of said composition, (c) high chemical durability to aqueous solution, and (d) an immobilized oxide of said radioactive material chemically incorporated into the silica structure thereof whereby leakage of said oxide of the radioactive component to the environment at environmental temperatures is prevented for extremely long periods of time.
Claim 30
Dependent Claim
91 words
A non-porous glass composition containing radioactive material, derived from nuclear waste, encapsulated and immobilized in the glass matrix, said composition being characterized by: (a) at least 75 mol percent SiO 2 , (b) a radiation activity above one millicurie per cubic centimeter of said composition, (c) high chemical durability to aqueous solution, and (d) an immobilized oxide of said radioactive material chemically incorporated into the silica structure thereof whereby leakage of said oxide of the radioactive component to the environment at environmental temperatures is prevented for extremely long periods of time.
References Cited (Backward Citations)
US2106744A
Cited
US2943059A
Cited
US3141852A
Cited
US3147225A
Cited
US3132033A
Cited
US3116131A
Cited
US3167504A
Cited
US3114716A
Cited
US3364148A
Cited
US3640888A
Cited
US3971717A
Cited
US4094809A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-23 | 1984-03-24 | 1984-09-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-23 | 1988-03-24 | 1988-09-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-23 | 1992-03-24 | 1992-09-23 | $7700.00 | Window Closed / Lapsed |