Method of producing a dielectric with perowskite structure and containing a copper oxide
Assignee: US Philips Corp
•
Filing: 1978-08-16
•
Granted: 1980-09-16
•
Expires: 1998-08-16
Abstract
Abstract Method for producing a dielectric having perowskite structure comprising stoichiometric alkaline earth titanates, alkaline earth zirconates, alkaline earth stannates and mixed crystals thereof, wherein an admixture of eutectic-forming compounds which are capable of forming CuO.MeO x when sintered in an oxygen atmosphere, which cannot in practice be built into the perowskite lattice, are added to the stoichiometric perowskite structure and wherein the mixture of compounds is sintered at a partial oxygen pressure of 0.2 to 1 Bar in the temperature range from 1000°-1250° C., MeO x in the above-mentioned formula being the oxide of at least one element of group III, V, VI or VII of the Periodic System of Elements (P.S.E.).
Inventors
- 👤 Detlev Hennings
- 👤 Herbert Schreinemacher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:52
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; H; H01; H01B; H01B3/00; H01B3/02; H01B3/12
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
130 words
A method of producing a dielectric material comprising perowskite-forming compounds consisting essentially of one or more of the group of stoichiometric alkaline earth titanates, alkaline earth zirconates, alkaline earth stannates and mixed crystals thereof, said method comprising the steps of: admixing, with said perowskite-forming compounds, a quantity of eutectic-forming compounds which cannot be incorporated into the perowskite lattice to any substantial extent and which are capable of forming CuO.MeO x when sintered in an oxygen atmosphere, where MeO x is at least one oxide of an element from group III, V, VI or VII of the periodic system of element; and sintering said admixture, at a partial oxygen pressure of 0.2-1 Bar, in the temperature range of from 1000°-1250° C., said eutectic-forming compounds being present in sintering temperature lowering amounts.
Claim 2
Independent Claim
130 words
A method of producing a dielectric material comprising perowskite-forming compounds consisting essentially of one or more of the group of stoichiometric alkaline earth titanates, alkaline earth zirconates, alkaline earth stannates and mixed crystals thereof, said method comprising the steps of: admixing, with said perowskite-forming compounds, a quantity of eutectic-forming compounds which cannot be incorporated into the perowskite lattice to any substantial extent and which are capable of forming CuO.MeO x when sintered in an oxygen atmosphere, where MeO x is at least one oxide of an element from group III, V, VI or VII of the periodic system of element; and sintering said admixture, at a partial oxygen pressure of 0.2-1 Bar, in the temperature range of from 1000°-1250° C., said eutectic-forming compounds being present in sintering temperature lowering amounts.
Claim 3
Dependent Claim
25 words
A method as claimed in claim 1, wherein the CuO-forming compounds and the MeO x -forming compounds are added in a molar ratio of 1:1.
Claim 4
Dependent Claim
36 words
A method as claimed in claim 1, further comprising the step of calcining the perowskite-forming compounds at a temperature of approximately 1150° C., prior to the step of admixing said perowskite-forming compounds with the eutectic-forming compounds.
Claim 5
Dependent Claim
37 words
A method as claimed in claim 1, 2, or 3, wherein MeO x is at least one oxide of an element from the group consisting essentially of boron, aluminum, gallium, thallium, vanadium, bismuth, antimony, chromium and manganese.
References Cited (Backward Citations)
US3473958A
Cited
US3441517A
Cited
US3490887A
Cited
US3851228A
Cited
US3977887A
Cited
US4143207A
Cited
DE2659016A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-16 | 1984-03-17 | 1984-09-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-16 | 1988-03-17 | 1988-09-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-16 | 1992-03-17 | 1992-09-16 | $7700.00 | Window Closed / Lapsed |