US4221829A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preparing a granular thermosetting novolak resin molding composition
Assignee: Euteco SpA
•
Filing: 1979-01-18
•
Granted: 1980-09-09
•
Expires: 1999-01-18
Abstract
Abstract A granular thermosetting novolak resin composition free from a tendency to release dust during handling and transformable into molded articles free from surface defects, is obtained by forming the composition into granules of from 2 to 9 mm in size, mixing said granules with 0.7-2.5 wt. % of a liquid mixture of acetone and polymers of alkyl esters of acrylic and methacrylic acids, and drying the thus impregnated granules.
Inventors
- 👤 Silvio Vargiu
- 👤 Pierluigi Manzoni
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 04:38
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08J3/124; C08L; C08L61/00; C08L61/04; C08L61/06; C08J2361/00; C08J2361/04; C08J2361/06; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2998
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
157 words
A method for preparing a granular thermosetting molding composition including a novolak phenolic resin with modified surface characteristics, which comprises forming said molding composition into granules of from 2 to 9 mm in size and mixing said granules with an amount of from 0.7 to 2.5 wt.%, based on the weight of the granules, of a mixture of acetone and one or more polymers of alkyl esters of acrylic and methacrylic acids having from 1 to 5 carbon atoms in the alkyl radical, said polymers being present in the mixture in an amount of from 1 to 20% by weight, at a temperature such as to maintain said mixture in liquid form and for a period such as to insure absorption of said mixture by said granules, and drying said granules to substantially remove said acetone, whereby the surface of said granules is modified to render the granules free from a tendency to release dust during handling.
Claim 2
Independent Claim
157 words
A method for preparing a granular thermosetting molding composition including a novolak phenolic resin with modified surface characteristics, which comprises forming said molding composition into granules of from 2 to 9 mm in size and mixing said granules with an amount of from 0.7 to 2.5 wt.%, based on the weight of the granules, of a mixture of acetone and one or more polymers of alkyl esters of acrylic and methacrylic acids having from 1 to 5 carbon atoms in the alkyl radical, said polymers being present in the mixture in an amount of from 1 to 20% by weight, at a temperature such as to maintain said mixture in liquid form and for a period such as to insure absorption of said mixture by said granules, and drying said granules to substantially remove said acetone, whereby the surface of said granules is modified to render the granules free from a tendency to release dust during handling.
Claim 3
Dependent Claim
65 words
The method of claim 1, wherein said novolak phenolic resin is included in an amount from 15 to 50 wt.% based on the weight of the molding composition and wherein the molding composition further includes from 3 to 10 wt.% of hexamine, from 0.5 to 2 wt.% of alkaline earth metal oxide, and one or more inert fillers, based on the weight of the composition.
Claim 4
Dependent Claim
14 words
The method of claim 1, wherein said mixture contains about 5 wt.% of polymers.
Claim 5
Dependent Claim
27 words
The method of claim 1, wherein said mixture is used in an amount of the order of 1.5 wt.% with respect to the weight of the granules.
Claim 6
Dependent Claim
17 words
The method of claim 1, wherein said mixing is carried out at 20°-30° C. for 5-30 minutes.
Claim 7
Dependent Claim
19 words
The method of claim 1, wherein said drying is carried out at a temperature of at least 40° C.
Claim 8
Dependent Claim
20 words
The method of claim 1, wherein said drying is carried out at a temperature of from 40° to 70° C.
Claim 9
Dependent Claim
30 words
The method of claim 7, wherein said drying is carried out by flowing through the granules a stream of hot gas for a period of from 1 to 10 minutes.
References Cited (Backward Citations)
US3971863A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-09 | 1984-03-10 | 1984-09-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-09 | 1988-03-10 | 1988-09-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-09 | 1992-03-10 | 1992-09-09 | $7700.00 | Window Closed / Lapsed |