Method of manufacturing a gas sensor
Assignee: United States Department of the Interior
•
Filing: 1978-12-19
•
Granted: 1980-09-09
•
Expires: 1998-12-19
Abstract
Abstract A system for detecting carbon monoxide, even in the presence of methane, using a catalytic sensor material having a perovskite crystal structure and a composition A.sub.1-n B.sub.n CO.sub.3-m where A is a rare earth metal; B is an alkaline metal; C is a metal from the group consisting of cobalt, vanadium and maganese; O is oxygen; n is less than 0.1; and m is not greater than 0.5, which material is substantially free of oxides of A, B and C. The method of making the crystalline material involves firing appropriate amounts of mixed salts of A, B and C until substantially converted to the perovskite structure, and then leaching with a caustic to remove the undesired oxides.
Inventors
- 👤 John M. Parry
- 👤 Paul Raccah
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:43
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/02; G01N27/04; G01N27/12; Y; Y10; Y10S; Y10S502/00; Y10S502/525
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
118 words
A method of manufacturing a gas sensor comprising the steps of: heating a mixture of salts of A, B, and C at a temperature and for at least one period of time sufficient to convert most of said mixture into a material having a perovskite crystal structure of the type: A.sub.1-n B.sub.n CO.sub.3-m where A is a rare earth metal; B is an alkaline earth metal; C is a metal selected from the group consisting of cobalt, vanadium, and manganese; O is oxygen; n is less than 0.1; and m is not greater than 0.5; leaching substantially all oxides of said metals from said material; and coupling a mass of said material between a pair of electrical leads.
Claim 2
Independent Claim
118 words
A method of manufacturing a gas sensor comprising the steps of: heating a mixture of salts of A, B, and C at a temperature and for at least one period of time sufficient to convert most of said mixture into a material having a perovskite crystal structure of the type: A.sub.1-n B.sub.n CO.sub.3-m where A is a rare earth metal; B is an alkaline earth metal; C is a metal selected from the group consisting of cobalt, vanadium, and manganese; O is oxygen; n is less than 0.1; and m is not greater than 0.5; leaching substantially all oxides of said metals from said material; and coupling a mass of said material between a pair of electrical leads.
Claim 3
Dependent Claim
59 words
The method of claim 1 wherein said step of coupling comprises coating an electrically insulating substrate at two separate points with electrically conductive metal; forming a paste from said material in a binder and applying said paste to form a bridge between said points; and heating said bridge to form a dry mass of said material connecting said points.
Claim 4
Dependent Claim
27 words
The method of claim 2 wherein said step of coating comprises forming a first coat of chromium at said points; and overcoating said chromium coat with gold.
Claim 5
Dependent Claim
21 words
The method of claim 2 wherein said paste is formed of a mixture of a powder of said material with polytetrafluorethylene.
Claim 6
Dependent Claim
115 words
The method of claim 1 wherein said heating and leaching steps comprise: forming at least one pellet of a mixture of said salts; firing said pellets at a temperature and for a period of time sufficient to effect at least partial conversion of said mixture to said perovskite structure; at least one time grinding the fired pellets, forming new pellets from the ground pellets and refiring said new pellets at said temperature and for said period until most of said mixture is converted to said perovskite structure; leaching the converted mixture with a caustic bath to remove substantially all oxides of said metals from said mixture; and treating the leached mixture to neutralize said caustic.
Claim 7
Dependent Claim
13 words
The method of claim 5 wherein said temperature is about 920° C.-925° C.
Claim 8
Dependent Claim
13 words
The method of claim 5 wherein said caustic bath is a KOH solution.
Claim 9
Dependent Claim
15 words
The method of claim 5 wherein said leached mixture is treated with HNO 3 .
Claim 10
Dependent Claim
40 words
The method of claim 5 wherein the step of at least one time grinding, firing and refiring is performed in part prior to the step of leaching and in part thereafter prior to the step of treating the leached mixture.
Claim 11
Dependent Claim
36 words
The method of claim 5 including after the step of treating a further step of leaching in caustic, and treatment of the mixture after said further step to neutralize the caustic added by said further step.
Claim 12
Independent Claim
77 words
A method of manufacturing a carbon monoxide sensor comprising the steps of heating a mixture of salts of lanthanum, strontium and cobalt to convert most of the mixture into a material having a perovskite crystal of the type La.sub.1-n Sr.sub.n CoO.sub.3-m where n is about 0.07 and m is approximately 0; removing substantially all oxides of La, Sr and Co from said mixture; and coupling a mass of the oxide-free mixture between a pair of electrical leads.
Claim 13
Independent Claim
77 words
A method of manufacturing a carbon monoxide sensor comprising the steps of heating a mixture of salts of lanthanum, strontium and cobalt to convert most of the mixture into a material having a perovskite crystal of the type La.sub.1-n Sr.sub.n CoO.sub.3-m where n is about 0.07 and m is approximately 0; removing substantially all oxides of La, Sr and Co from said mixture; and coupling a mass of the oxide-free mixture between a pair of electrical leads.
References Cited (Backward Citations)
US3922204A
Cited
US3951603A
Cited
JPS49103699A
Cited
JPS5016695A
Cited
US3897367A
Cited
DE2533442A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-09 | 1984-03-10 | 1984-09-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-09 | 1988-03-10 | 1988-09-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-09 | 1992-03-10 | 1992-09-09 | $7700.00 | Window Closed / Lapsed |