Method for making porous, crushable core having a porous integral outer barrier layer having a density gradient therein
Assignee: General Electric Co
•
Filing: 1979-01-25
•
Granted: 1980-09-09
•
Expires: 1999-01-25
Abstract
Abstract A method for simultaneously forming an integral porous outer barrier layer having a density gradient therein on selected external surfaces of a fired ceramic article and for increasing the porosity content and crushability characteristics thereof embodies the firing of a ceramic compact comprising a reactant fugitive filler material and a ceramic material in a controlled atmosphere.
Inventors
- 👤 Wayne D. Pasco
- 👤 Frederic J. Klug
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:25
CPC Classifications
C; C30; C30B; C30B21/00; C30B21/02; B; B22; B22C; B22C9/00; B22C9/02; B22C9/04; B22C9/10; B22D; B22D27/00; B22D27/04; B22D27/045
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
222 words
A method for simultaneously forming a porous integral barrier layer having a density gradient across its thickness on all external surfaces of a fired ceramic article and for increasing the porosity content and the crushability characteristics of the interior portion thereby including the process steps of (a) preparing a material composition consisting essentially of an organic binder, a reactant fugitive filler material and an alumina flour, the particle size of the alumina flour and the reactant fugitive filler material is less than about 300 microns, and the binder comprises less than 50 percent by volume; (b) working a portion of the material composition to produce a preform of a predetermined shape; (c) heating the preform to remove the organic binder from the preform while retaining substantially all of the reactant fugitive filler material therein and to obtain a desired green strength; (d) firing the preform in a controlled atmosphere to react the alumina and the reactant fugitive filler material to produce at least one or more suboxides of alumina to produce a ceramic article having a predetermined continuous porosity content, grain morphology, and crushability characteristics, and (e) oxidizing at least a portion of the suboxides of alumina to form a porous integral barrier layer of alumina at the surface of the ceramic article, the layer having a density gradient across its thickness.
Claim 2
Independent Claim
222 words
A method for simultaneously forming a porous integral barrier layer having a density gradient across its thickness on all external surfaces of a fired ceramic article and for increasing the porosity content and the crushability characteristics of the interior portion thereby including the process steps of (a) preparing a material composition consisting essentially of an organic binder, a reactant fugitive filler material and an alumina flour, the particle size of the alumina flour and the reactant fugitive filler material is less than about 300 microns, and the binder comprises less than 50 percent by volume; (b) working a portion of the material composition to produce a preform of a predetermined shape; (c) heating the preform to remove the organic binder from the preform while retaining substantially all of the reactant fugitive filler material therein and to obtain a desired green strength; (d) firing the preform in a controlled atmosphere to react the alumina and the reactant fugitive filler material to produce at least one or more suboxides of alumina to produce a ceramic article having a predetermined continuous porosity content, grain morphology, and crushability characteristics, and (e) oxidizing at least a portion of the suboxides of alumina to form a porous integral barrier layer of alumina at the surface of the ceramic article, the layer having a density gradient across its thickness.
Claim 3
Dependent Claim
169 words
The method of claim 1 wherein the preform of the material composition is heated in a controlled atmosphere at a rate of less than 100° C. per hour to a first temperature range of less than about 1100° C. to remove the organic binder, the preform is heated in a controlled atmosphere at a rate of at least 100° C. per hour through a first predetermined temperature range of from about 1650° C. to about 1900° C.; isothermally heating the preform within the second predetermined temperature range for a sufficient time to chemically react substantially all of the reactant filler material with alumina to form suboxides of alumina; vapor transporting the suboxides to the vicinity of the surface of the ceramic article; oxidizing the suboxides of alumina in the vicinity of the surface of the ceramic article to obtain the desired volume of continuous porosity therein, and forming the porous integral barrier layer of alumina having a density gradient across its thickness at the surface of the ceramic article.
Claim 4
Dependent Claim
49 words
The method of claim 2 wherein the preform is heated in the second predetermined temperature range in a controlled atmosphere having an oxygen partial pressure which is the equivalent of the oxygen partial pressure present in wet hydrogen gas having a dewpoint range of less than about -35° F.
Claim 5
Dependent Claim
17 words
The method of claim 3 wherein the controlled atmosphere in the second predetermined temperature range is hydrogen.
Claim 6
Dependent Claim
32 words
The method of claim 3 wherein the controlled atmosphere in the second predetermined temperature range is an inert gas which is one selected from the group consisting of argon, helium and neon.
Claim 7
Dependent Claim
19 words
The method of either claim 1, 2, 3, 4 or 5 wherein the reactant fugitive filler material is carbon.
Claim 8
Dependent Claim
32 words
The method of either claim 1, 2 or 3 wherein the reactant fugitive fill material is one selected from the group consisting of aluminum, aluminum carbide, aluminum oxycarbide, boron and boron carbide.
Claim 9
Dependent Claim
104 words
The method of claim 2 wherein heating the preform is at a rate of about 25° C. per hour up to about 400° C., heating the preform at a rate of from about 50° C. per hour to no greater than about 100° C. per hour from about 400° C. up to a temperature range of from 1100° C. to 1300° C., heating the preform at a rate of greater than 200° C. per hour up to a temperature of about 1650° C. or greater, and isothermally heating the preform for a predetermined period of time at the temperature of 1650° C. or greater.
Claim 10
Dependent Claim
77 words
The method of claim 8 wherein the compact is placed in a fine flour up to about 1100° C. to 1300° C., the flour is one which is selected from the group consisting of alumina, carbon, activated charcoal, high surface area carbon black and activated alumina, the flour having a pore size which is smaller than that of the compact after removal of the binder, and removing the compact from the packing flour and continuing the heating.
Claim 11
Dependent Claim
140 words
The method of either claim 1 or 2 including the steps of packing the compact in a fine flour which is one selected from the group consisting of alumina, activated alumina, carbon, activated charcoal, and high surface area carbon black, heating the packed compact at a rate of less than 25° C. per hour up to 200° C. to remove at least a portion of the binder material therefrom, removing the compact from the packing flour, heating the compact at a rate of less than 25° C. per hour up to 400° C. to remove the remainder of the binder material, heating the compact at a rate of greater than 200° C. per hour to at least 1650° C., and isothermally heating the compact at the last elevated temperature for a predetermined time period to obtain the desired physical properties.
Claim 12
Dependent Claim
26 words
The method of either claim 8 or 9, wherein the reactant fugitive filler material is carbon and the molar ratio of carbon to alumina is 0≦G/A≦1.25.
Claim 13
Dependent Claim
23 words
The method of claim 10 wherein the reactant fugitive filler material is carbon and the molar ratio of carbon to alumina is 0≦G/A≦1.25.
Claim 14
Dependent Claim
27 words
The method of claim 11 wherein the preferred particle size of the reactant fugitive filler material and the alumina material is from 1 micron to 50 microns.
Claim 15
Dependent Claim
27 words
The method of claim 12 wherein the preferred particle size of the reactant fugitive filler material and the alumina material is from 1 micron to 50 microns.
Claim 16
Dependent Claim
23 words
The method of claim 6 wherein the reactant fugitive filler material is carbon and the molar ratio of carbon to alumina is 0≦G/A≦1.25.
Claim 17
Dependent Claim
23 words
The method of claim 6 wherein the reactant fugitive filler material is carbon and the molar ratio of carbon to alumina is 0.1<G/A<0.4.
Claim 18
Dependent Claim
23 words
The method of claim 6 wherein the reactant fugitive filler material is carbon and the molar ratio of carbon to alumina is 0.2<G/A<0.3.
Claim 19
Dependent Claim
15 words
The method of claim 3 wherein the dewpoint range is less than about -80° F.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-09-09 | 1984-03-10 | 1984-09-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-09-09 | 1988-03-10 | 1988-09-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-09-09 | 1992-03-10 | 1992-09-09 | $7700.00 | Window Closed / Lapsed |