Mass polymerization process

Assignee: Allnex Austria GmbH
•
Filing: 1978-11-06
•
Granted: 1980-09-02
•
Expires: 1998-11-06
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A process for the preparation of polymers by free-radical, bulk polymerization comprising charging a reaction vessel with from about 5 to 15 percent by weight of an alpha, beta-unsaturated monomer which does not, under the conditions of the reaction, undergo free-radical polymerization, e.g., an alkyl ester of fumaric or maleic acid; thereafter adding to the reaction vessel from about 95 to 85 percent by weight of an acrylic monomer which, under the conditions of the reaction, undergoes free-radical polymerization in bulk form, blended with a free-radical initiator and controlling said addition in order that the acrylic monomer is present in said reaction kettle in an amount of less than about 20 percent, and preferably less than about 5 percent, during the course of the reaction. The process proceeds without excessive exothermy, permitting the complete polymerization in a synthetic resin reactor.

Inventors

  • 👤 Laszlo Tulacs
  • 👤 Hans Hiden

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-09 16:15
CPC Classifications
C; C08; C08F; C08F220/00; C08F220/02; C08F220/10; C08F220/12; C08F220/16; C08F220/18; C08F220/1808

Claims Analysis

Total Claims: 7
Claim 1
Independent Claim 158 words
A process for the bulk polymerization of acrylic monomers by free-radical polymerization comprising the steps of (1) charging to a reaction vessel from about 5 to 15 percent by weight of an alpha,beta-unsaturated monomer which does not, under the conditions of the reaction, tend to the formation of homopolymers through free-radical polymerization and which is selected from the group consisting of fumaric acid and maleic acid alkyl esters having from 4 to 12 carbon atoms in the ester chain, and mixtures thereof; (2) after step (1), adding to the reaction vessel about 95 to 85 percent by weight of an acrylic monomer which, under the conditions of the reaction, undergo free-radical polymerization blended with a free-radical initiator; and (3) controlling addition step (2) in order that the acrylic component in the reaction kettle is present in the form of unreacted momomers in an amount of less than about 20 percent by weight during the course of the reaction.
Claim 2
Dependent Claim 158 words
A process for the bulk polymerization of acrylic monomers by free-radical polymerization comprising the steps of (1) charging to a reaction vessel from about 5 to 15 percent by weight of an alpha,beta-unsaturated monomer which does not, under the conditions of the reaction, tend to the formation of homopolymers through free-radical polymerization and which is selected from the group consisting of fumaric acid and maleic acid alkyl esters having from 4 to 12 carbon atoms in the ester chain, and mixtures thereof; (2) after step (1), adding to the reaction vessel about 95 to 85 percent by weight of an acrylic monomer which, under the conditions of the reaction, undergo free-radical polymerization blended with a free-radical initiator; and (3) controlling addition step (2) in order that the acrylic component in the reaction kettle is present in the form of unreacted momomers in an amount of less than about 20 percent by weight during the course of the reaction.
Claim 3
Dependent Claim 24 words
The process of claim 1 wherein the reaction temperature during the addition of the acrylic monomer is maintained between about 80° and 140° C.
Claim 4
Dependent Claim 24 words
The process of claim 1 wherein the acrylic monomer is an acrylate having from 4 to 12 carbon atoms in the alkyl ester chain.
Claim 5
Dependent Claim 28 words
The process of claim 1 wherein the acrylic monomer is a monomer wherein the homopolymer of the monomer has a glass transition temperature of -40° C. or below.
Claim 6
Dependent Claim 18 words
The process of claim 4 wherein the acrylic monomer is the butyl or octyl ester of (meth)acrylic acid.
Claim 7
Dependent Claim 23 words
The process of claim 1 wherein the polymerization conversion of the acrylic monomer component is monitored by continued determinations of the refractive index.

References Cited (Backward Citations)

US2298039A Cited
US2544692A Cited
US2642414A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1983-09-02 1984-03-03 1984-09-02 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1987-09-02 1988-03-03 1988-09-02 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 1991-09-02 1992-03-03 1992-09-02 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag