US4217192A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Decontamination of metals using chemical etching
Assignee: United States Department of Energy
•
Filing: 1979-06-11
•
Granted: 1980-08-12
•
Expires: 1999-06-11
Abstract
Abstract The invention relates to chemical etching process for reclaiming contaminated equipment wherein a reduction-oxidation system is included in a solution of nitric acid to contact the metal to be decontaminated and effect reduction of the reduction-oxidation system, and includes disposing a pair of electrodes in the reduced solution to permit passage of an electrical current between said electrodes and effect oxidation of the reduction-oxidation system to thereby regenerate the solution and provide decontaminated equipment that is essentially radioactive contamination-free.
Inventors
- 👤 Ronald E. Lerch
- 👤 Jerry A. Partridge
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:18
CPC Classifications
C; C23; C23G; C23G1/00; C23G1/02; C23G1/08; C23G1/085; G; G21; G21F; G21F9/00; G21F9/28; G21F9/30
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
122 words
A process for reclaiming radiation contaminated equipment by removing radioactive contaminants from metal surfaces of said equipment comprising preparing a solution of nitric acid containing a reduction-oxidation system, wherein said reduction-oxidation system may be reduced and subsequently reoxidized by electrolysis, heating said solution, contacting the metal to be decontaminated with said solution, said contacting effecting a chemical reaction reducing said reduction-oxidation system to the reduced state, disposing a pair of electrodes in said solution, passing an electrical current between said electrodes thereby regenerating the oxidized state and thereby regenerating said solution, said contact of said metal with said solution effectively removing said radioactive contaminants from said metal surfaces, and subsequently removing said metal from said solution as an essentially radioactive contaminant-free metal.
Claim 2
Dependent Claim
21 words
The process of claim 1 wherein said reduction-oxidation system is selected from the group consisting of cerium(IV)-cerium(III), chromium(VI)-chromium(III), silver(II)-silver(I), and cobalt(III)-cobalt(II).
Claim 3
Dependent Claim
46 words
The process of claim 1 wherein said reduction-oxidation system comprises cerium(IV)-cerium(III), said contacting of said metal to be decontaminated with said solution effects a chemical reduction of said cerium(IV) to cerium(III), and said passage of said electrical current between said electrodes oxidizes said cerium(III) to cerium(IV).
Claim 4
Dependent Claim
23 words
The process of claim 3 wherein said electrolytic regeneration of cerium (IV) is accomplished by passing about 0.5 amperes current between said electrodes.
Claim 5
Dependent Claim
28 words
The process of claim 3 wherein said metal contact with said solution accomplishes a dissolution rate of said metal of about 29 milligrams per square centimeter per hour.
Claim 6
Dependent Claim
40 words
The process of claim 3 wherein said nitric acid is at a molar concentration of from about 1 molar to about 8 molar and said cerium(IV) is at a concentration range of from about 0.01 molar to about 0.30 molar.
Claim 7
Dependent Claim
40 words
The process of claim 6 wherein said nitric acid has a concentration of about 7 molar and said cerium(IV) has a concentration of about 0.25 molar to achieve a dissolution rate of about 29 milligrams per square centimeter per hour.
Claim 8
Dependent Claim
37 words
The process of claim 6 wherein said nitric acid has a concentration of 7 molar, said heating is at about 90° C. and said cerium(IV) has a concentration of about 0.25 molar in the (IV) oxidation state.
Claim 9
Dependent Claim
18 words
The process of claim 1 wherein said heating is to from about 20° C. to about 100° C.
Claim 10
Dependent Claim
13 words
The process of claim 9 wherein said heating is at about 90° C.
References Cited (Backward Citations)
US3437521A
Cited
US3682796A
Cited
US3496017A
Cited
US3615817A
Cited
US3640805A
Cited
US3821091A
Cited
US3840646A
Cited
US4006067A
Cited
US3873362A
Cited
US4162206A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-12 | 1984-02-11 | 1984-08-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-12 | 1988-02-11 | 1988-08-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-12 | 1992-02-11 | 1992-08-12 | $7700.00 | Window Closed / Lapsed |