Glass conveying roll and a method of forming it
Assignee: Pilkington North America Inc
•
Filing: 1979-01-04
•
Granted: 1980-08-05
•
Expires: 1999-01-04
Abstract
Abstract A roll for conveying flat glass at elevated temperatures over extended periods of time without material damage to the supported surface of the glass, and a procedure for preparing such rolls. The roll is built up of thin asbestos discs compressed endwise upon a mandrel. The asbestos is impregnated with a solution of potassium sulfate and then thoroughly dried before the roll is put into use. The potassium sulfate crystals provide lubricity to the roll surface and bind the asbestos fibers together so as to improve the durability of the roll while minimizing damage to the heated glass.
Inventors
- 👤 Norman K. Gladieux
- 👤 Carey M. Allen
- 👤 Thomas J. Koralewski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:35
CPC Classifications
C; C03; C03B; C03B35/00; C03B35/14; C03B35/16; C03B35/18; C03B35/189; C03B35/181; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
72 words
In a method of treating a roll including an outer asbestos material-supporting portion for conveying glass at elevated temperatures, the steps of preparing an aqueous solution of potassium sulfate, immersing said outer asbestos portion in said solution for a period of time sufficient to allow said solution to penetrate said asbestos, removing said outer asbestos portion from said solution, and drying said outer asbestos portion whereby potassium sulfate crystallizes within the asbestos.
Claim 2
Dependent Claim
72 words
In a method of treating a roll including an outer asbestos material-supporting portion for conveying glass at elevated temperatures, the steps of preparing an aqueous solution of potassium sulfate, immersing said outer asbestos portion in said solution for a period of time sufficient to allow said solution to penetrate said asbestos, removing said outer asbestos portion from said solution, and drying said outer asbestos portion whereby potassium sulfate crystallizes within the asbestos.
Claim 3
Dependent Claim
57 words
A method of treating a roll for conveying glass as claimed in claim 1, wherein said drying is accomplished by first allowing said outer asbestos portion to air dry in the ambient atmosphere to evaporate the surface mositure, and thereafter subjecting it to heat to gradually increase its temperature until substantially all of the moisture is removed.
Claim 4
Dependent Claim
36 words
A method of treating a roll for conveying glass as claimed in claim 1 or claim 2, wherein said aqueous solution is a saturated solution of potassium sulfate agitated to maintain the uniformity of the solution.
Claim 5
Dependent Claim
35 words
A method of treating a roll for conveying glass as claimed in claim 1 or claim 2, wherein said solution is maintained at a temperature of about 160° F. while said asbestos is immersed therein.
Claim 6
Dependent Claim
59 words
A method of treating a roll for conveying glass as claimed in claim 1, including the steps of positioning said roll over said solution with its longitudinal axis parallel to the surface of, and its lower portion immersed in, said solution, and rotating said roll about its longitudinal axis to progressively immerse the periphery of said outer asbestos portion.
Claim 7
Dependent Claim
55 words
A method of treating a roll for conveying glass as claimed in claim 2, wherein the temperature to which said outer asbestos portion is exposed in applying said heat is at least partially increased in increments, with the temperature remaining at each increment point for a time sufficient to permit gradual escape of entrapped moisture.
Claim 8
Dependent Claim
37 words
A method of treating a roll for conveying glass as claimed in claim 6, wherein the temperature is increased in 100° F. increments from 100° F. through 600° F., and thereafter is increased to about 1000° F.
Claim 9
Dependent Claim
40 words
A method of treating a roll for conveying glass as claimed in claim 7, including the step of directly inserting the prepared roll in an operating glass producing facility while said outer asbestos material-supporting portion remains in the heated state.
Claim 10
Dependent Claim
146 words
A method of treating a roll for conveying glass as claimed in claim 2, wherein said aqueous solution is a saturated solution of potassium sulfate maintained at a temperature of about 160° F. and agitated to maintain the uniformity of the solution while said asbestos is immersed therein, including the steps of positioning said roll over said solution with its longitudinal axis parallel to the surface of, and its lower portion immersed in, said solution, rotating the roll about its longitudinal axis to progressively immerse the periphery of said outer asbestos portion, and wherein the temperature to which said outer asbestos portion is exposed in applying said heat is increased in 100° F. increments from 100° F. through 600° F., with the temperature remaining at each increment point for a time sufficient to permit gradual escape of entrapped moisture, and thereafter increased to about 1000° F.
Claim 11
Dependent Claim
30 words
In a roll for conveying glass at elevated temperatures including an asbestos portion upon which the glass is carried, the improvement wherein said asbestos is impregnated with crystallized potassium sulfate.
Claim 12
Dependent Claim
30 words
In a roll for conveying glass at elevated temperatures including an asbestos portion upon which the glass is carried, the improvement wherein said asbestos is impregnated with crystallized potassium sulfate.
Claim 13
Dependent Claim
29 words
A roll for conveying glass at elevated temperatures as claimed in claim 10, wherein said asbestos portion comprises a plurality of asbestos discs axially compressed upon a central mandrel.
Claim 14
Dependent Claim
45 words
A roll for conveying glass at elevated temperatures as claimed in claim 11, wherein said potassium sulfate substantially permeates said discs from their exterior surface to said mandrel, the potassium sulfate crystals providing lubricity to the glass conveying surface and binding the asbestos fibers together.
References Cited (Backward Citations)
US1825509A
Cited
US2232765A
Cited
US2385653A
Cited
US3736179A
Cited
US3853525A
Cited
US3877919A
Cited
US4057410A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-08-05 | 1984-02-04 | 1984-08-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-08-05 | 1988-02-04 | 1988-08-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-08-05 | 1992-02-04 | 1992-08-05 | $7700.00 | Window Closed / Lapsed |