Unsaturated polyester resin composition for use in pressure molding
Assignee: Hitachi Ltd
•
Filing: 1977-02-10
•
Granted: 1980-07-08
•
Expires: 1997-02-10
Abstract
Abstract An unsaturated polyester resin composition for use in pressure molding, which comprises an unsaturated polyester resin and fillers consisting essentially of (a) calcium carbonate powder which passes a 325 mesh sieve, (b) an inorganic mineral particulate which passes a 12 mesh sieve and is retained on a 200 mesh sieve and (c) glass fibers having a length larger than 0.2 mm, wherein the ratio by weight of (a) to (b) is within a range of from 0.3 to 10, the ratio of (a)+(b) to the unsaturated polyester resin is within a range of from 1.5 to 7, and the ratio of (c) to the total weight of the resin, calcium carbonate, silica sand and glass fiber is within a range of from 0.01 to 0.25.
Inventors
- 👤 Akio Nishikawa
- 👤 Junichi Katagiri
- 👤 Noriyuki Kinjo
- 👤 Hitoshi Yokono
- 👤 Tamotsu Ikeda
- 👤 Tsuguo Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:20
CPC Classifications
C; C08; C08K; C08K13/00; C08K13/04; C08K3/00; C08K3/01; C08K3/013; C08K3/18; C08K3/24; C08K3/26; C08K7/00; C08K7/02; C08K7/04; C08K7/14
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
186 words
An unsaturated polyester resin composition for use in pressure molding, which comprises: (I) a liquid mixture comprising an unsaturated polyester resin of a polycondensate or condensate synthesized from an unsaturated or saturated polybasic acid or anhydrides thereof, and hydroxyl compounds, or precursors thereof, an ethylenically unsaturated compound monomer in an amount of 20 to 50% by weight, based on the mixture, and a curing catalyst in an amount effective for the polymerization reaction between the polyester resin and the compound monomer, said mixture having a viscosity of 50 to 50,000 centipoises at 25° C., and (II) a filler consisting essentially of, (a) a calcium carbonate powder, (b) a silica sand having a particle size larger than said powder and smaller than 1500 μm and (c) a chopped glass fiber wherein the ratio by weight of (a) to (b) is within a range of from 0.3 to 10, the ratio of (a) and (b) to (I) is within a range of from 2.5 to 6, and the ratio of (c) to the total weight of (I) and (II) is within a range of from 0.01 to 0.25.
Claim 2
Dependent Claim
186 words
An unsaturated polyester resin composition for use in pressure molding, which comprises: (I) a liquid mixture comprising an unsaturated polyester resin of a polycondensate or condensate synthesized from an unsaturated or saturated polybasic acid or anhydrides thereof, and hydroxyl compounds, or precursors thereof, an ethylenically unsaturated compound monomer in an amount of 20 to 50% by weight, based on the mixture, and a curing catalyst in an amount effective for the polymerization reaction between the polyester resin and the compound monomer, said mixture having a viscosity of 50 to 50,000 centipoises at 25° C., and (II) a filler consisting essentially of, (a) a calcium carbonate powder, (b) a silica sand having a particle size larger than said powder and smaller than 1500 μm and (c) a chopped glass fiber wherein the ratio by weight of (a) to (b) is within a range of from 0.3 to 10, the ratio of (a) and (b) to (I) is within a range of from 2.5 to 6, and the ratio of (c) to the total weight of (I) and (II) is within a range of from 0.01 to 0.25.
Claim 3
Dependent Claim
22 words
An unsaturated polyester resin composition according to claim 1, wherein said calcium carbonate powder has a particle size less than 80 μm.
Claim 4
Dependent Claim
22 words
An unsaturated polyester resin composition of claim 2, wherein said silica sand has a particle size of from 100 to 1,500 μm.
Claim 5
Dependent Claim
67 words
An unsaturated polyester resin composition according to claim 1, wherein said hydroxyl compound, or precursors thereof, is selected from the group consisting of ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, trimethylene glycol, tetramethylene glycol, hexamethylene glycol, 2,2-diethylpropane diol-1,3, neopentyl glycol, bromoneopentyl glycol, bisphenol dioxyethyl ether, hydrogenated bisphenol A, 2,2-di(4-hydroxy propoxy phenyl) propane, ethyleneoxide, propylene oxide, 3,3,3-trichloropropylene oxide, phenylglycidyl ether, and arylglycidyl ether.
Claim 6
Dependent Claim
55 words
An unsaturated polyester resin composition according to claim 4, wherein said unsaturated or saturated polybasic acid, or anhydride thereof, is selected from the group consisting of maelic acid, maelic anhydride, fumaric acid, chloromaleic acid, dichloromaleic acid, methacoic acid, itacoic acid, adipic acid, sebacinic acid, phthalic acid, phthalic anhydride, isophthalic acid, pyrometritic acid, and Het acid.
Claim 7
Dependent Claim
27 words
An unsaturated polyester resin composition according to claim 3, wherein said chopped glass fiber has a length of from 0.2 to 8 mm. in the kneaded composition.
Claim 8
Dependent Claim
44 words
An unsaturated polyester resin composition according to claim 6, wherein the filler has: (a) a calcium carbonate powder which passes a 325 mesh sieve, and (b) a silica sand powder which passes a 12 mesh sieve and is retained on a 200 mesh sieve.
Claim 9
Dependent Claim
27 words
An unsaturated polyester resin composition according to claim 7, wherein the silica sand powder passes a 12 mesh sieve and is retained on a 100 mesh sieve.
Claim 10
Dependent Claim
23 words
An unsaturated polyester resin composition according to claim 6, wherein the particle size of said calcium carbonate powder is less than 44 μm.
Claim 11
Dependent Claim
25 words
An unsaturated polyester resin composition according to claim 6, wherein the ratio of (a) to (b) is within a range of from 0.3 to 4.
Claim 12
Dependent Claim
31 words
An unsaturated polyester resin composition according to claim 6, wherein the ratio of (c) to the total weight of [I] and [II] is within a range of from 0.1 to 0.2.
Claim 13
Dependent Claim
37 words
An unsaturated polyester resin composition according to claim 6, wherein the composition further contains a diallylphthalate prepolymer in an amount of 1 to 10% by weight based on the total weight of [I] and the diallylphthate prepolymer.
Claim 14
Dependent Claim
177 words
An unsaturated polyester resin composition comprising: (I) a liquid mixture comprising an unsaturated polyester resin of a polycondensate or a condensate synthesized from an unsaturated or saturated polybasic acid, or anhydrides thereof, and hydroxyl compounds, or precursors thereof, an ethylenically unsaturated compound reactable with said unsaturated polyester resin, and a curing catalyst for the reaction therebetween, said mixture having a viscosity of 50 to 50,000 centipoises at 25° C.; and (II) a filler consisting essentially of, (a) a calcium carbonate powder which passes a 325 mesh sieve, (b) an inorganic mineral particulate which passes a 12 mesh sieve and is retained on a 150 mesh sieve, and (c) a chopped glass fiber having a length of from 0.2 to 8 mm, wherein the ratio of weight of (a) to (b) is within a range of 0.3 to 4, the ratio of (a) and (b) to (I) is within a range of from 2.5 to 6, and the ratio of (c) to the total weight of (I) and (II) is within a range of from 0.1 to 0.2.
Claim 15
Dependent Claim
177 words
An unsaturated polyester resin composition comprising: (I) a liquid mixture comprising an unsaturated polyester resin of a polycondensate or a condensate synthesized from an unsaturated or saturated polybasic acid, or anhydrides thereof, and hydroxyl compounds, or precursors thereof, an ethylenically unsaturated compound reactable with said unsaturated polyester resin, and a curing catalyst for the reaction therebetween, said mixture having a viscosity of 50 to 50,000 centipoises at 25° C.; and (II) a filler consisting essentially of, (a) a calcium carbonate powder which passes a 325 mesh sieve, (b) an inorganic mineral particulate which passes a 12 mesh sieve and is retained on a 150 mesh sieve, and (c) a chopped glass fiber having a length of from 0.2 to 8 mm, wherein the ratio of weight of (a) to (b) is within a range of 0.3 to 4, the ratio of (a) and (b) to (I) is within a range of from 2.5 to 6, and the ratio of (c) to the total weight of (I) and (II) is within a range of from 0.1 to 0.2.
Claim 16
Dependent Claim
37 words
An unsaturated polyester resin composition according to claim 13, wherein the composition further contains a diallylphthalate prepolymer in an amount of 1 to 10% by weight based on the total weight of [I] and the diallylphthalate prepolymer.
Claim 17
Dependent Claim
18 words
An unsaturated polyester resin composition according to claim 13, wherein the mineral particulate is a powder of limestone.
Claim 18
Dependent Claim
16 words
An unsaturated polyester resin composition as in claim 13, wherein the mineral particulate is silica sand.
Claim 19
Dependent Claim
161 words
An unsaturated polyester resin composition comprising: (I) a liquid mixture comprising an unsaturated polyester resin synthesized from methacrylate and a bisphenol A type epoxy compound, styrene monomer in an amount of 30 to 45% by weight based on the total weight of the resin and styrene, and a curing catalyst; and (II) a filler consisting essentially of, (a) a calcium carbonate powder which passes a 325 mesh sieve, (b) a silica sand powder which passes a 12 mesh sieve and is retained on a 100 mesh sieve, and (c) a chopper glass fiber having a length of from 1 to 6 mm in the kneaded composition, wherein the ratio by weight of (a) to (b) is within a range of from 0.3 to 10, the ratio of (a)+(b) to (I) is within a range of from 1.5 to 7, and the ratio of (c) to the total weight of (I) and (II) is within a range of from 0.1 to 0.2.
Claim 20
Dependent Claim
161 words
An unsaturated polyester resin composition comprising: (I) a liquid mixture comprising an unsaturated polyester resin synthesized from methacrylate and a bisphenol A type epoxy compound, styrene monomer in an amount of 30 to 45% by weight based on the total weight of the resin and styrene, and a curing catalyst; and (II) a filler consisting essentially of, (a) a calcium carbonate powder which passes a 325 mesh sieve, (b) a silica sand powder which passes a 12 mesh sieve and is retained on a 100 mesh sieve, and (c) a chopper glass fiber having a length of from 1 to 6 mm in the kneaded composition, wherein the ratio by weight of (a) to (b) is within a range of from 0.3 to 10, the ratio of (a)+(b) to (I) is within a range of from 1.5 to 7, and the ratio of (c) to the total weight of (I) and (II) is within a range of from 0.1 to 0.2.
Claim 21
Dependent Claim
37 words
An unsaturated polyester resin composition according to claim 17, wherein the composition further contains a diallylphthalate prepolymer in an amount of 1 to 10% by weight based on the total weight of [I] and the diallylphthalate prepolymer.
Claim 22
Dependent Claim
114 words
An unsaturated polyester resin composition for use in injection molding, which comprises: (I) a liquid mixture comprising an unsaturated polyester resin of a vinylester of a bisphenol A epoxy resin, about 30% by weight of styrene, and a curing catalyst, (II) a filler consisting essentially of, (a) a calcium carbonate powder which passes a 325 mesh sieve, (b) a silica sand powder which passes a 12 mesh sieve and is retained on a 100 mesh sieve, and (c) a glass fiber having a length of 1 to 5 mm, and (III) a diallylphthalate prepolymer, wherein (a)/(b) by weight is about 1, (a)+(b)/(I) is about 4, (c)/(I)+(II) is about 0.1, and (III)/(I)+(III) is about 0.05.
Claim 23
Dependent Claim
114 words
An unsaturated polyester resin composition for use in injection molding, which comprises: (I) a liquid mixture comprising an unsaturated polyester resin of a vinylester of a bisphenol A epoxy resin, about 30% by weight of styrene, and a curing catalyst, (II) a filler consisting essentially of, (a) a calcium carbonate powder which passes a 325 mesh sieve, (b) a silica sand powder which passes a 12 mesh sieve and is retained on a 100 mesh sieve, and (c) a glass fiber having a length of 1 to 5 mm, and (III) a diallylphthalate prepolymer, wherein (a)/(b) by weight is about 1, (a)+(b)/(I) is about 4, (c)/(I)+(II) is about 0.1, and (III)/(I)+(III) is about 0.05.
References Cited (Backward Citations)
FR1317975A
Cited
US3326845A
Cited
FR1413988A
Cited
US3658750A
Cited
US3936414A
Cited
FR2132474B1
Cited
US3763080A
Cited
US3926902A
Cited
US3991006A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-07-08 | 1984-01-07 | 1984-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-07-08 | 1988-01-07 | 1988-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-07-08 | 1992-01-07 | 1992-07-08 | $7700.00 | Window Closed / Lapsed |