US4211683A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the preparation of aqueous dispersions of polyurethanes
Assignee: Bayer AG
•
Filing: 1977-08-03
•
Granted: 1980-07-08
•
Expires: 1997-08-03
Abstract
Abstract The present invention relates to a process for the preparation of aqueous dispersions or solutions of polyurethanes which have urea end groups and contain non-ionic hydrophilic segments and which are capable of being cross-linked with the aid of cross-linking agents which are reactive with urea groups, characterized in that prepolymers which have isocyanurate end groups and which (i) have an average molecular weight of less than about 15,000 and (ii) contain from about 2 to 30%, by weight, of ethylene oxide units corresponding to the following formula: --CH.sub.2 --CH.sub.2 --O-- within a polyether chain (containing ethylene oxide units) are reacted at from about 10° to 70° C. with an aqueous solution of ammonia or with a primary amine, optionally dissolved in water, the aqueous solution of ammonia or the primary amine, optionally dissolved in water, being added to the prepolymer in the reaction vessel and the quantity of water used for dissolving the ammonia or primary amine being not more than about 10%, by weight, based on the total quantity of reaction mixture, and finally, after termination of the addition reaction between the free isocyanate groups of the prepolymer and the added ammonia or primary amine, the reaction product obtained is stirred with water at from about 10° to 70° C. to form an aqueous dispersion or solution having a concentration of from about 5 to 65%, by weight. The present invention also relates to the use of dispersions or solutions obtainable by the process according to the present invention for the production of cross-linked sheets by application of the dispersion to a substrate and drying, cross-linking of the sheet being ensured by the addition of a cross-linking agent capable of undergoing a cross-linking reaction with the urea groups either before, during or after application of the solution or dispersion to the substrate.
Inventors
- 👤 Wolfgang Wenzel
- 👤 Dieter Dieterich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:18
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/83; C08G18/84; C08G18/08; C08G18/10; C08G18/28; C08G18/40; C08G18/48; C08G18/4833
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
221 words
A process for the preparation of aqueous dispersions of polyurethanes which have urea end groups and which contain non-ionic hydrophilic segments and which may be cross-linked by means of cross-linking agents which are reactive with urea groups comprising reacting in a reaction vessel a prepolymer which has isocyanate end groups and which (i) has a stoichiometrically calculated average molecular weight of less than about 10,000; and (ii) contains from about 2 to 30%, by weight, of ethylene oxide units corresponding to the following formula; --CH.sub.2 --CH.sub.2 --O-- arranged within a polyether chain containing ethylene oxide units, at from about 10° to 70° C. with an aqueous solution of ammonia or with a monoprimary amine, optionally dissolved in water, the aqueous solution of ammonia or the monoprimary amine, optionally dissolved in water, being added to the prepolymer previously introduced into the reaction vessel, the quantity of water used for dissolving the ammonia or primary amine being at the most about 10%, by weight, based on the total quantity of the reaction mixture, and finally, after completion of the addition reaction between the free isocyanate groups of the prepolymer and the added ammonia or monoprimary amine, the desired reaction product is stirred with water at from about 10° to 70° C. to form a from about 5 to 65%, by weight, aqueous dispersion.
Claim 2
Dependent Claim
221 words
A process for the preparation of aqueous dispersions of polyurethanes which have urea end groups and which contain non-ionic hydrophilic segments and which may be cross-linked by means of cross-linking agents which are reactive with urea groups comprising reacting in a reaction vessel a prepolymer which has isocyanate end groups and which (i) has a stoichiometrically calculated average molecular weight of less than about 10,000; and (ii) contains from about 2 to 30%, by weight, of ethylene oxide units corresponding to the following formula; --CH.sub.2 --CH.sub.2 --O-- arranged within a polyether chain containing ethylene oxide units, at from about 10° to 70° C. with an aqueous solution of ammonia or with a monoprimary amine, optionally dissolved in water, the aqueous solution of ammonia or the monoprimary amine, optionally dissolved in water, being added to the prepolymer previously introduced into the reaction vessel, the quantity of water used for dissolving the ammonia or primary amine being at the most about 10%, by weight, based on the total quantity of the reaction mixture, and finally, after completion of the addition reaction between the free isocyanate groups of the prepolymer and the added ammonia or monoprimary amine, the desired reaction product is stirred with water at from about 10° to 70° C. to form a from about 5 to 65%, by weight, aqueous dispersion.
Claim 3
Dependent Claim
64 words
A process for the production of cross-linked sheets comprising applying the aqueous dispersions or solutions of polyurethanes obtained by the process of claim 1 to a substrate and drying, cross-linking of the resulting sheet being ensured by the addition of a cross-linking agent capable of undergoing a cross-linking reaction with urea groups before, during or after application of the aqueous dispersions to the substrate.
Claim 4
Dependent Claim
24 words
The process of claim 2 wherein the cross-linking agent is selected from the group consisting of formaldehyde or melamine resins which have methylol groups.
Claim 5
Dependent Claim
56 words
The process of claim 1 wherein the prepolymer which has isocyanate end groups (i) has an average molecular weight of less than about 10,000; (ii) contains from about 6 to 20% by weight of ethylene oxide units arranged within a polyether chain; and (iii) has an isocyanate content of from about 1.5 to 10% by weight.
Claim 6
Dependent Claim
29 words
The process of claim 1 wherein the prepolymer is produced by reacting a diisocyanate with a polyhydroxyl compound at an NCO/OH equivalent ratio of from about 1.1:1 to 2.5:1.
Claim 7
Dependent Claim
106 words
The process of claim 5 wherein the polyhydroxyl compound corresponds to a compound of the formula ##STR2## wherein R represents a divalent group such as is obtained by removal of the isocyanate groups from a diisocyanate having a molecular weight of from about 112 to 1000; X represents --O--or --NR"--; R' and R" which may be the same or different, each represents a monovalent hydrocarbon group having from 1 to 12 carbon atoms; R''' represents hydrogen or a monovalent hydrocarbon group having from 1 to 8 carbon atoms; n represents an integer of from 4 to 89; and R IV represents hydrogen or a methyl group.
Claim 8
Dependent Claim
71 words
The process of claim 1 wherein the prepolymer which has isocyanate end groups is reacted with the aqueous solution of ammonia or with the primary amine at a temperature of from about 15° to 50° C. and wherein the reactants are chosen so that the reaction mixture contains from about 0.9 to 1.2 molecules of ammonia or of amino groups of the primary amine per each isocyanate group of the prepolymer.
Claim 9
Dependent Claim
32 words
The process of claim 1 wherein the reaction product is stirred with water at from about 15° to 50° C. to form a from about 20 to 50% by weight aqueous dispersion.
Claim 10
Dependent Claim
182 words
A solvent free process for the preparation of aqueous dispersions of non-ionic polyurethanes containing urea end groups and non-ionic hydrophilic segments comprising (A) introducing a prepolymer having isocyanate end groups into a reaction vessel, said prepolymer (i) having a stoichiometrically calculated average molecular weight of less than about 10,000 and (ii) containing from about 2 to 30% by weight of ethylene oxide units corresponding to the formula --CH 2 --CH 2 --O-- arranged within a polyether chain, (B) adding an aqueous solution of ammonia or a monoprimary amine, optionally dissolved in water, to the reaction vessel to form a reaction mixture, said reaction mixture containing at most about 10% by weight of water and having about 0.9 to 1.2 molecules of ammonia or of amino groups of the primary amine for each isocyanate group; (C) reacting the reaction mixture at about 10° to 70° C. until the isocyanate addition reaction is complete; and (D) stirring the reaction product of (C) with water at from about 10° to 70° C. to form an about 5 to 65% by weight aqueous dispersion of polyurethane.
Claim 11
Dependent Claim
182 words
A solvent free process for the preparation of aqueous dispersions of non-ionic polyurethanes containing urea end groups and non-ionic hydrophilic segments comprising (A) introducing a prepolymer having isocyanate end groups into a reaction vessel, said prepolymer (i) having a stoichiometrically calculated average molecular weight of less than about 10,000 and (ii) containing from about 2 to 30% by weight of ethylene oxide units corresponding to the formula --CH 2 --CH 2 --O-- arranged within a polyether chain, (B) adding an aqueous solution of ammonia or a monoprimary amine, optionally dissolved in water, to the reaction vessel to form a reaction mixture, said reaction mixture containing at most about 10% by weight of water and having about 0.9 to 1.2 molecules of ammonia or of amino groups of the primary amine for each isocyanate group; (C) reacting the reaction mixture at about 10° to 70° C. until the isocyanate addition reaction is complete; and (D) stirring the reaction product of (C) with water at from about 10° to 70° C. to form an about 5 to 65% by weight aqueous dispersion of polyurethane.
References Cited (Backward Citations)
US3242230A
Cited
US3491067A
Cited
US3756992A
Cited
US3796678A
Cited
US3905929A
Cited
US3920598A
Cited
US4039517A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-07-08 | 1984-01-07 | 1984-07-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-07-08 | 1988-01-07 | 1988-07-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-07-08 | 1992-01-07 | 1992-07-08 | $7700.00 | Window Closed / Lapsed |