US4210619A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Cement bonded agglomerate containing boron
Assignee: HICKMAN WILLIAMS AND COMPANY COLUMBIA PLAZA SUITE 1110 PO BOX 538 CINCINNATI OH 45201 A CORP OF DE
•
Filing: 1978-08-18
•
Granted: 1980-07-01
•
Expires: 1998-08-18
Abstract
Abstract A cement bonded agglomerate containing boron wherein the setting time of the flowable mixture is essentially unchanged is prepared by dissolving a boron compound or compounds, such as boric acid or borax, in water. Next, adding a sufficient amount of a water soluble calcium compound, such as hydrated lime, to chemically react with substantially all of the dissolved boron, the reaction forming an insoluble calcium borate compound which forms a slurry with the water. This slurry is then mixed with material to be agglomerated and cement and poured into a mold. The mold can either produce individual shaped pieces ready for use or a slab which can be broken into the proper size pieces.
Inventors
- 👤 George D. Haley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 03:03
CPC Classifications
C; C04; C04B; C04B22/00; C04B22/0013
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
124 words
A method for producing cement bonded agglomerates containing boron wherein the setting time of the agglomerated mixture is essentially unchanged which comprises the steps of: (a) dissolving at least one water soluble boron compound selected from the group consisting of borax, colemanite, rasorite, boric oxide, or boric acid in water; (b) adding a sufficient amount of at least one water soluble calcium compound selected from the group consisting of oxides and hydroxides of calcium to chemically react with substantially all of the dissolved boron compound to form a slurry; (c) mixing the slurry with ferroalloy materials to be agglomerated and cement to form a flowable concrete mixture; (d) next pouring the resulting mixture into a suitable mold; and (e) allowing the mixture to set.
Claim 2
Independent Claim
124 words
A method for producing cement bonded agglomerates containing boron wherein the setting time of the agglomerated mixture is essentially unchanged which comprises the steps of: (a) dissolving at least one water soluble boron compound selected from the group consisting of borax, colemanite, rasorite, boric oxide, or boric acid in water; (b) adding a sufficient amount of at least one water soluble calcium compound selected from the group consisting of oxides and hydroxides of calcium to chemically react with substantially all of the dissolved boron compound to form a slurry; (c) mixing the slurry with ferroalloy materials to be agglomerated and cement to form a flowable concrete mixture; (d) next pouring the resulting mixture into a suitable mold; and (e) allowing the mixture to set.
Claim 3
Dependent Claim
18 words
The method as recited in claim 1 wherein the slurry comprises by weight: Boric Acid--11% Water--56% Hydrated Lime--33%
Claim 4
Dependent Claim
35 words
The method as recited in claim 2 wherein the mold produces a hardened slab after setting, said slab then being passed through a flake breaker to produce sized pieces for use as an alloying material.
Claim 5
Dependent Claim
18 words
The method as recited in claim 2 wherein the mold produces hardened, shaped forms of a desired size.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-07-01 | 1983-12-31 | 1984-07-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-07-01 | 1987-12-31 | 1988-07-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-07-01 | 1991-12-31 | 1992-07-01 | $7700.00 | Window Closed / Lapsed |