Crevice-corrosion resistant aluminum radiator triclad composite

Claim 2

A triclad composite metal article having improved resistance to crevice corrosion in aqueous environments comprising an aluminum core, an aluminum brazing alloy metallurgically bonded to said core and a sacrificial aluminum cladding bonded to the other side of said core, said sacrificial alloy cladding consisting essentially of from 0 to 0.1% magnesium, 0.8 to 1.2% manganese, 0 to 0.1% chromium, 0 to 0.05% silicon, 0 to 0.05% copper, 0.1 to 0.4% zinc, 0 to 0.1% titanium, 0 to 0.1% iron, balance essentially aluminum.

Claim 3

A triclad composite metal article according to claim 1 wherein said cladding consists essentially of from 0 to 0.05% magnesium, 0.9 to 1.1% manganese, 0 to 0.05% chromium, 0 to 0.03% silicon, 0 to 0.01% copper, 0.15 to 0.25% zinc, 0.005 to 0.03% titanium and 0 to 0.08% iron.

Claim 4

A process for providing heat transfer with resistance to crevice corrosion in an aqueous environment which comprises: A. providing a metal header plate comprising an aluminum core, an aluminum brazing alloy metallurgically bonded to one side of said core and a sacrificial aluminum alloy cladding metallurgically bonded to the other side of said core, said sacrificial alloy cladding consisting essentially of from 0 to 0.1% magnesium, 0.8 to 1.2% manganese, 0 to 0.1% chromium, 0 to 0.05% silicon, 0 to 0.05% copper, 0.1 to 0.4% zinc, 0 to 0.1% titanium, 0 to 0.1% iron, balance essentially aluminum; B. affixing metal tubes to the brazing alloy side of said metal header plate; C. passing an aqueous liquid over said sacrificial alloy cladding and through said tubing; and D. contacting the external surface of said tubing with a secondary heat exchange surface.

Claim 5

A process for providing heat transfer with resistance to crevice corrosion in an aqueous environment which comprises: A. providing a metal header plate comprising an aluminum core, an aluminum brazing alloy metallurgically bonded to one side of said core and a sacrificial aluminum alloy cladding metallurgically bonded to the other side of said core, said sacrificial alloy cladding consisting essentially of from 0 to 0.1% magnesium, 0.8 to 1.2% manganese, 0 to 0.1% chromium, 0 to 0.05% silicon, 0 to 0.05% copper, 0.1 to 0.4% zinc, 0 to 0.1% titanium, 0 to 0.1% iron, balance essentially aluminum; B. affixing metal tubes to the brazing alloy side of said metal header plate; C. passing an aqueous liquid over said sacrificial alloy cladding and through said tubing; and D. contacting the external surface of said tubing with a secondary heat exchange surface.

Claim 6

A process according to claim 3 wherein said cladding consists essentially of from 0 to 0.05% magnesium, 0.9 to 1.1% manganese, 0 to 0.05% chromium, 0 to 0.03% silicon, 0 to 0.01% copper, 0.15 to 0.25% zinc, 0.005 to 0.03% titanium and 0 to 0.08% iron.

Claim 7

A process according to claim 3 wherein said second heat exchange surface is corrugated fin stock bonded to said tubing.

Claim 8

A process according to claim 3 including E. providing said sacrificial alloy cladding with a groove; F. positioning an O-ring gasket seal in said groove; and G. securing a plastic tank to said header plate so as to form a header assembly wherein said gasket provides a leak-free joint wherein crevice corrosion in the area of said gasket is reduced.

Claim 9

A process according to claim 6 wherein said cladding consists essentially of from 0 to 0.05% magnesium, 0.9 to 1.1% manganese, 0 to 0.05% chromium, 0 to 0.03% silicon, 0 to 0.01% copper, 0.15 to 0.25% zinc, 0.005 to 0.03% titanium and 0 to 0.08% iron.

Claim 10

An aluminum heat exchange assembly having improved resistance to crevice corrosion in aqueous environments comprising: A. at least one header plate; B. at least one tube connected to said header plate; and C. a second heat exchange surface connected to said tube wherein said header plate comprises an aluminum triclad composite having a core, a brazing alloy metallurgically bonded to one side of said core and an aluminum alloy sacrificial cladding metallurgically bonded to the other side of said core, said alloy cladding consisting essentially of from 0 to 0.1% magnesium, 0.8 to 1.2% manganese, 0 to 0.1% chromium, 0 to 0.05% silicon, 0 to 0.05% copper, 0.1 to 0.4% zinc, 0 to 0.1% titanium, 0 to 0.1% iron, balance essentially aluminum.

Claim 11

An aluminum heat exchange assembly having improved resistance to crevice corrosion in aqueous environments comprising: A. at least one header plate; B. at least one tube connected to said header plate; and C. a second heat exchange surface connected to said tube wherein said header plate comprises an aluminum triclad composite having a core, a brazing alloy metallurgically bonded to one side of said core and an aluminum alloy sacrificial cladding metallurgically bonded to the other side of said core, said alloy cladding consisting essentially of from 0 to 0.1% magnesium, 0.8 to 1.2% manganese, 0 to 0.1% chromium, 0 to 0.05% silicon, 0 to 0.05% copper, 0.1 to 0.4% zinc, 0 to 0.1% titanium, 0 to 0.1% iron, balance essentially aluminum.

Claim 12

An assembly according to claim 8 wherein said cladding consists essentially of from 0 to 0.05% magnesium, 0.9 to 1.1% manganese, 0 to 0.05% chromium, 0 to 0.03% silicon, 0 to 0.01% copper, 0.15 to 0.25% zinc, 0.005 to 0.03% titanium and 0 to 0.08% iron.

Claim 13

An assembly according to claim 8 further including a plastic tank secured to said header plate and sealing means provided between said tank and said sacrificial alloy of said header plate so as to provide a leak-free joint.

Claim 14

An assembly according to claim 10 wherein said cladding consists essentially of from 0 to 0.05% magnesium, 0.9 to 1.1% manganese, 0 to 0.05% chromium, 0 to 0.03% silicon, 0 to 0.01% copper, 0.15 to 0.25% zinc, 0.005 to 0.03% titanium and 0 to 0.08% iron.