US4207381A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Bimetal and method for manufacturing the same
Assignee: Toshiba Corp
•
Filing: 1978-02-22
•
Granted: 1980-06-10
•
Expires: 1998-02-22
Abstract
Abstract A bimetal is disclosed having a high, rapid deflection over a specified temperature range, including a high expansion metal alloy component having a high thermal expansion coefficient that changes rapidly at 50×10 -6 /° C. or greater at a temperature of between about 100° C. and 250° C. and containing from 15-30% by weight of manganese, the balance of iron. The second component has a substantially constant thermal expansion coefficient regardless of the temperature change, and is preferably a stainless steel. These bimetals are used in circuit breakers, thermal protectors and the like.
Inventors
- 👤 Tatsuyoshi Aisaka
- 👤 Mitsuo Kawai
- 👤 Fumio Mori
- 👤 Shinzo Sugai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:46
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/01; B32B15/011; G; G12; G12B; G12B1/00; G12B1/02; H; H01; H01H; H01H37/00; H01H37/02; H01H37/32; H01H37/52; H01H2037/526; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/125; Y10T428/12507; Y10T428/12521
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
90 words
A bimetal comprising: (1) a high expansion component of a metal alloy whose thermal expansion coefficient rapidly changes from 21.5×10 -6 /°C. less to 50×10 -6 /°C. or more starting at a temperature of between 100° C. and 250° C., which consists of 15 to 30% by weight of manganese and substantially iron as the remainder, and which is substantially free from work strains and (2) a low expansion component of a metal alloy whose thermal expansion coefficient is substantially constant regardless of temperature change, said bimetal exhibiting a hysteresis.
Claim 2
Dependent Claim
90 words
A bimetal comprising: (1) a high expansion component of a metal alloy whose thermal expansion coefficient rapidly changes from 21.5×10 -6 /°C. less to 50×10 -6 /°C. or more starting at a temperature of between 100° C. and 250° C., which consists of 15 to 30% by weight of manganese and substantially iron as the remainder, and which is substantially free from work strains and (2) a low expansion component of a metal alloy whose thermal expansion coefficient is substantially constant regardless of temperature change, said bimetal exhibiting a hysteresis.
Claim 3
Dependent Claim
64 words
The bimetal according to claim 1, wherein the first alloy component is formed of a 15 to 25% by weight of manganese, and a member selected from the group consisting of 2 to 15% by weight of chromium, 2 to 15% by weight of cobalt and 2 to 20% by weight of a mixture of chromium and cobalt, and substantially iron as the remainder.
Claim 4
Dependent Claim
41 words
The bimetal according to claim 2, wherein the said first alloy component is formed of 15 to 25% by weight of manganese and 2% and 15% by weight of a mixture of chromium and cobalt and substantially iron as the remainder.
Claim 5
Dependent Claim
47 words
The bimetal according to claim 1, wherein the second alloy component has the same thermal expansion coefficient as that which is indicated by the first alloy component at a lower temperature than that at which the thermal expansion coefficient of said first alloy component is rapidly increased.
Claim 6
Dependent Claim
17 words
The bimetal according to claim 4, wherein the second alloy component is formed of austenitic stainless steel.
Claim 7
Dependent Claim
144 words
A bimetal exhibiting a rapid deflection over a specified temperature range and having a high thermal expression coefficient, including: (1) a high expansion metal alloy component having a thermal expansion coefficient that changes rapidly in the range of about 21.5×19 -6 /°C. to about 50×10 -6 /°C. at a temperature of between about 100° C. and 250° C., said alloy consisting essentially of from 15 to 30% by weight of manganeses, and a member selected from the group consisting of 2 to 15% by weight of chromium, 2 to 15% by weight of cobalt and 2 to 20% by weight of a mixture of chromium and cobalt, the balance being iron, the high expansion component being substantially devoid of machine strain; and (2) a low expansion metal alloy component having a thermal expansion coefficient substantially constant notwithstanding temperature change, said bimetal exhibiting a hysteresis.
Claim 8
Dependent Claim
144 words
A bimetal exhibiting a rapid deflection over a specified temperature range and having a high thermal expression coefficient, including: (1) a high expansion metal alloy component having a thermal expansion coefficient that changes rapidly in the range of about 21.5×19 -6 /°C. to about 50×10 -6 /°C. at a temperature of between about 100° C. and 250° C., said alloy consisting essentially of from 15 to 30% by weight of manganeses, and a member selected from the group consisting of 2 to 15% by weight of chromium, 2 to 15% by weight of cobalt and 2 to 20% by weight of a mixture of chromium and cobalt, the balance being iron, the high expansion component being substantially devoid of machine strain; and (2) a low expansion metal alloy component having a thermal expansion coefficient substantially constant notwithstanding temperature change, said bimetal exhibiting a hysteresis.
Claim 9
Dependent Claim
15 words
The bimetal according to claim 6 wherein said low expansion component is austenitic stainless steel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-06-10 | 1983-12-10 | 1984-06-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-06-10 | 1987-12-10 | 1988-06-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-06-10 | 1991-12-10 | 1992-06-10 | $7700.00 | Window Closed / Lapsed |