Ceramic veneer
Assignee: Wilhelm Gailsche Tonwerke KGaA
•
Filing: 1978-12-15
•
Granted: 1980-06-10
•
Expires: 1998-12-15
Abstract
Abstract A ceramic veneer manufactured from a thin-fluid slip by drying and baking of the slip. The slip consists of at least two different layers which have either different shrinkage rates during baking and/or different co-efficients of thermal expansion in the baked condition. The shrinkage rates and the coefficients of thermal expansion of the individual layers are determined such that the veneer remains of a uniform thickness throughout the manufacturing process.
Inventors
- 👤 Joachim Otto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:17
CPC Classifications
B; B32; B32B; B32B18/00; C; C04; C04B; C04B33/00; C04B33/24; C04B2237/00; C04B2237/02; C04B2237/10; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; C04B2237/38; C04B2237/50; C04B2237/58; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
248 words
A continuous method for preparing a ceramic veneer of uniform thickness, which comprises the steps of: depositing a first thin layer of a first thin-fluid slip onto a moving surface; then applying a first glass fleece layer on top of said first slip layer and pressing said first glass fleece layer into said first slip layer so that said first slip layer is impregnated in said first glass fleece layer; then depositing a second thin layer of a second thin-fluid slip on top of said first glass fleece layer, said second thin-fluid slip having a different composition than said first thin-fluid slip and having a different shrinkage rate during baking, a different coefficient of thermal expansion after baking or both a different shrinkage rate and a different coefficient of thermal expansion; then applying a second glass fleece layer on top of said second slip layer and pressing said second glass fleece layer into said second slip layer so that said second slip layer is impregnated in said second glass fleece layer whereby to form an assembly of said layers; then heating said assembly to dry said slips whereby to form a dry assembly; then firing said dry assembly to form a unitary first ceramic veneer product of uniform thickness consisting essentially of two different layers and then cooling said ceramic veneer product, wherein the compositions of said slip layers are effective to cause said ceramic veneer product to remain flat and of uniform thickness during firing and cooling.
Claim 2
Dependent Claim
248 words
A continuous method for preparing a ceramic veneer of uniform thickness, which comprises the steps of: depositing a first thin layer of a first thin-fluid slip onto a moving surface; then applying a first glass fleece layer on top of said first slip layer and pressing said first glass fleece layer into said first slip layer so that said first slip layer is impregnated in said first glass fleece layer; then depositing a second thin layer of a second thin-fluid slip on top of said first glass fleece layer, said second thin-fluid slip having a different composition than said first thin-fluid slip and having a different shrinkage rate during baking, a different coefficient of thermal expansion after baking or both a different shrinkage rate and a different coefficient of thermal expansion; then applying a second glass fleece layer on top of said second slip layer and pressing said second glass fleece layer into said second slip layer so that said second slip layer is impregnated in said second glass fleece layer whereby to form an assembly of said layers; then heating said assembly to dry said slips whereby to form a dry assembly; then firing said dry assembly to form a unitary first ceramic veneer product of uniform thickness consisting essentially of two different layers and then cooling said ceramic veneer product, wherein the compositions of said slip layers are effective to cause said ceramic veneer product to remain flat and of uniform thickness during firing and cooling.
Claim 3
Dependent Claim
36 words
A method according to claim 1 including the step of applying glaze onto the upper surface of said assembly of said layers prior to said firing step whereby said ceramic veneer product has a glaze thereon.
Claim 4
Dependent Claim
65 words
A method according to claim 1 in which the solids of said first thin-fluid slip consist essentially of 40 wt. % of clay, 20 wt. % of hard burned fireclay and 40 wt. % of feldspar, and the solids of said second thin-fluid slip consist essentially of 30 wt. % of clay, 30 wt. % of hard burned fireclay and 40 wt. % of feldspar.
Claim 5
Dependent Claim
71 words
A method according to claim 1 in which the solids of said first thin-fluid slip consist essentially of 30 wt. % of clay, 15 wt. % of hard burned fireclay, 15 wt. % of glow fireclay and 40 wt. % of feldspar, and the solids of said second thin-fluid slip consist essentially of 30 wt. % of clay, 30 wt. % of hard burned fireclay and 40 wt. % of feldspar.
Claim 6
Dependent Claim
88 words
A method according to claim 1 in which the solids of said first thin-fluid slip consist essentially of 30 wt. % of clay, 15 wt. % of fireclay having a high coefficient of thermal expansion, 15 wt. % of glow fireclay having a high coefficient of thermal expansion and 40 wt. % of feldspar, and the solids of said second thin-fluid slip consist essentially of 30 wt. % of clay, 30 wt. % of fireclay having a low coefficient of thermal expansion and 40 wt. % of feldspar.
Claim 7
Dependent Claim
10 words
A ceramic veneer prepared by the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-06-10 | 1983-12-10 | 1984-06-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-06-10 | 1987-12-10 | 1988-06-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-06-10 | 1991-12-10 | 1992-06-10 | $7700.00 | Window Closed / Lapsed |