Polyacrylate rubber-modified vinylidene chloride copolymer compositions

Claim 2

A blend composition comprising (A) a vinylidene chloride copolymer and (B) a vinylidene chloride copolymer-polyacrylate rubber latex prepared by emulsion polymerization of an aqueous mixture containing (1) vinylidene chloride comonomer, (2) a monoethylenically unsaturated comonomer and (3) a cross-linked polyacrylate rubber obtained from an acrylate monomer of the formula: ##STR4## wherein R is an alkyl hydrocarbon radical containing at least 3 carbon atoms and R' is hydrogen or a methyl radical, and wherein the vinylidene chloride copolymer contains from 70 to 97 percent by weight of vinylidene chloride with the remainder composed of one or more other monoethylenically unsaturated comonomers.

Claim 3

The blend composition of claim 1 wherein R is an alkyl hydrocarbon radical having from 3 to 20 carbon atoms.

Claim 4

A blend composition of claim 1 wherein the proportions of Components A and B are such that the amount of polyacrylate rubber in the blend is within the range of about 1 to about 40 weight percent.

Claim 5

A blend composition of claim 1 wherein the polyacrylate rubber is polybutylacrylate and the comonomer is n-butylacrylate.

Claim 6

The latex composition of claim 1 wherein the polyacrylate rubber has an average particle size within the range of from about 1,000 A to 10,000 A.

Claim 7

A powder prepared from the blend composition of claim 1.

Claim 8

A vinylidene chloride copolymer-polyacrylate rubber latex composition prepared by emulsion polymerization of an aqueous mixture containing vinylidene chloride monomer, a monoethylenically unsaturated comonomer and a cross-linked polyacrylate rubber obtained from a acrylate monomer of the formula: ##STR5## wherein R is an alkyl hydrocarbon radical having at least 3 carbon atoms, and R' is hydrogen or methyl radical.

Claim 9

A vinylidene chloride copolymer-polyacrylate rubber latex composition prepared by emulsion polymerization of an aqueous mixture containing vinylidene chloride monomer, a monoethylenically unsaturated comonomer and a cross-linked polyacrylate rubber obtained from a acrylate monomer of the formula: ##STR5## wherein R is an alkyl hydrocarbon radical having at least 3 carbon atoms, and R' is hydrogen or methyl radical.

Claim 10

The latex composition of claim 7 wherein trimethylolpropane triacrylate is the crosslinker used in making the polyacrylate rubber.

Claim 11

A process for producing a vinylidene chloride copolymer latex blend which comprises: (a) emulsion polymerizing an aqueous mixture containing sufficient vinylidene chloride and a monoethylenically unsaturated comonomer to produce from about 55 percent to about 95 percent of the total vinylidene chloride copolymer latex desired, wherein said vinylidene chloride copolymer contains from 70 to 97 percent by weight of vinylidene chloride, (b) adding to the resultant polymer latex the remainder of the vinylidene chloride and monoethylenically unsaturated comonomer, and from about 1 to about 40 weight percent based on the total weight of the blend composition of a cross-linked polyacrylate rubber obtained from an acrylate monomer of the formula: ##STR6## wherein R is an alkyl hydrocarbon radical having at least 3 carbon atoms and R' is hydrogen or a methyl radical, and (c) emulsion polymerizing the resultant mixture.

Claim 12

A process for producing a vinylidene chloride copolymer latex blend which comprises: (a) emulsion polymerizing an aqueous mixture containing sufficient vinylidene chloride and a monoethylenically unsaturated comonomer to produce from about 55 percent to about 95 percent of the total vinylidene chloride copolymer latex desired, wherein said vinylidene chloride copolymer contains from 70 to 97 percent by weight of vinylidene chloride, (b) adding to the resultant polymer latex the remainder of the vinylidene chloride and monoethylenically unsaturated comonomer, and from about 1 to about 40 weight percent based on the total weight of the blend composition of a cross-linked polyacrylate rubber obtained from an acrylate monomer of the formula: ##STR6## wherein R is an alkyl hydrocarbon radical having at least 3 carbon atoms and R' is hydrogen or a methyl radical, and (c) emulsion polymerizing the resultant mixture.

Claim 13

The latex blend produced by the method of claim 9.

Claim 14

The method of claim 9 including the additional steps of coagulating and drying the latex to produce a powder.

Claim 15

The powder produced by the method of claim 11.