Conditioned colloidal silica post impregnant to prevent binder migration
Assignee: CARDBORUNDUM COMPANY
•
Filing: 1978-03-29
•
Granted: 1980-05-27
•
Expires: 1998-03-29
Abstract
Abstract The invention comprises the process for making an inorganic refractory insulation article by forming a fiber mat from a fiber slurry, impregnating the mat with a conditioned colloidal silica composition comprising colloidal silica, acid, aluminum chlorhydrate and water and drying the mat to form the article. The invention further comprises an inorganic refractory insulation article comprising randomly oriented refractory fibers retained by dried colloidal silica uniformly distributed throughout the article and from about 0.001 to about 1.5 weight percent of aluminum chlorhydrate which article is manufactured in accordance with the process.
Inventors
- 👤 Harris J. Korklan
- 👤 John K. Greany
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:20
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/24
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
65 words
A process for forming a refractory fiber article comprising placing a refractory fiber slurry into a mold and draining liquid therefrom; impregnating the resulting fiber article with a conditioned colloidal silica composition comprising colloidal silica, acid and a multivalent cation containing gelling compound; applying a differential pressure through said article, waiting for the conditioned colloidal silica composition to gel and drying the resulting fiber article.
Claim 2
Dependent Claim
65 words
A process for forming a refractory fiber article comprising placing a refractory fiber slurry into a mold and draining liquid therefrom; impregnating the resulting fiber article with a conditioned colloidal silica composition comprising colloidal silica, acid and a multivalent cation containing gelling compound; applying a differential pressure through said article, waiting for the conditioned colloidal silica composition to gel and drying the resulting fiber article.
Claim 3
Dependent Claim
41 words
The process of claim 1 wherein said fiber slurry is an aqueous slurry containing from about 0.5 to about 3 weight percent of refractory fiber, said article is an insulation board and the multivalent cation containing gelling compound is aluminum chlorhydrate.
Claim 4
Dependent Claim
20 words
The process of claim 2 wherein said fiber slurry contains from about 0.04 to about 0.2 weight percent colloidal silica.
Claim 5
Dependent Claim
20 words
The process of claim 3 wherein said fiber slurry contains from about 0.01 to about 0.1 weight percent colloidal clay.
Claim 6
Dependent Claim
11 words
The process of claim 4 wherein said colloidal clay is bentonite.
Claim 7
Dependent Claim
25 words
The process of claim 3 wherein said board is impregnated with from about 10 to about 80 volume percent of said conditioned colloidal silica composition.
Claim 8
Dependent Claim
60 words
The process of claim 3 wherein the conditioned colloidal silica is an aqueous composition containing from about 15 to about 20 weight percent SiO 2 , sufficient hydrochloric acid to obtain a pH of between about 4.8 and about 5.4; from about 0.5 to about 0.12 percent aluminum chlorhydrate by weight of conditioned colloidal silica and the balance being water.
Claim 9
Dependent Claim
30 words
The process of claim 1 wherein said fiber board is dried at a temperature of from about 150 to about 600° C. for from about 1 to about 12 hours.
Claim 10
Dependent Claim
46 words
An insulation article comprising randomly oriented refractory fibers retained by dried colloidal silica uniformly distributed throughout the article and from about 0.001 to about 1.5 weight percent of aluminum chlorhydrate wherein said article is a board which is formed according to the process of claim 1.
Claim 11
Dependent Claim
14 words
The article of claim 9 wherein said multivalent cation containing compound is aluminum chlorhydrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-05-27 | 1983-11-26 | 1984-05-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-05-27 | 1987-11-26 | 1988-05-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-05-27 | 1991-11-26 | 1992-05-27 | $7700.00 | Window Closed / Lapsed |