Viscous dispersion for forming wet-laid, non-woven fabrics

Claim 2

In a process for forming a non-woven fabric by wet-laying fibers on paper making equipment, the fabric containing staple length, synthetic fibers having a length to diameter ratio of about 400 to 3000, the fabric having a microvariation in basis weight of not more that about 10% and a macrovariation in basis weight of not more than about 5%, and the fabric being essentially free of knits, bundles and strings, the improvement which comprises forming a stable, viscous, uniform, air, fiber and water dispersion by the steps of: providing the fibers in a high-shear agitated, air, fiber and water mixture, which contains a dispersant and throughout which the fibers are completely and uniformly distributed; and then, slowly adding, over a period of about 10 minutes or longer, a thixotropic thickener to the high-shear agitated mixture to form the viscous dispersion; the viscous dispersion containing about 1% to 50% by volume of entrained air and having a nascent viscosity of about 10 to 125 cps., when measured at a shear rate of 30.5 sec. -1 ; and individual fibers in the viscous dispersion being restrained from becoming entangled and from forming knits, bundles and strings.

Claim 3

The process of claim 1 wherein the high-shear agitated, air, fiber and water mixture is provided by adding the fibers to a high-shear agitated mixture of water and the dispersant.

Claim 4

The process of claim 2 wherein 2% to 3% by weight of a fiber furnish, containing predominantly fibers having a length to diameter ratio of 400 to 700, is added to the high-shear agitated mixture of water and dispersant.

Claim 5

The process of claim 3 wherein about 2.5% by weight of said fiber furnish is added to the high-shear agitated mixture of water and dispersant.

Claim 6

The process of claim 2 wherein 1% to 2% by weight of a fiber furnish, containing predominantly fibers having a length to diameter rate of 700 to 2000, is added to the high-shear agitated mixture of water and dispersant.

Claim 7

The process of claim 5 wherein about 1.5% by weight of said fiber furnish is added to the high-shear agitated mixture of water and dispersant.

Claim 8

The process of claim 6 wherein said fibers have a length to diameter ratio of about 1500.

Claim 9

The process of claim 2 wherein 0.25% to 1% by weight of a fiber furnish, containing predominantly fibers having a length to diameter ratio of 2000 to 3000, is added to the high-shear agitated mixture of water and dispersant.

Claim 10

The process of claim 8 wherein about 0.5% by weight of said fiber furnish is added to the high-shear agitated mixture of water and dispersant.

Claim 11

The process of claim 2 wherein 0.001% to 0.2% by weight of dispersant is utilized.

Claim 12

The process of claim 10 wherein 0.005% to 0.1% by weight of dispersant is utilized.

Claim 13

The process of claim 1 wherein said synthetic fibers are hydrophobic fibers.

Claim 14

The process of claim 2 wherein a non-foaming dispersant is utilized which is selected from the group consisting of polyacrylic acid dispersants and relatively low molecular weight, polyacrylate dispersants.

Claim 15

The process of claim 2 wherein a high-foam or low-foam generating dispersant is utilized which is selected from the group consisting of alkylaryl polyether alcohols and alkyl taurines.

Claim 16

The process of claim 1 wherein 1 to 10 parts by weight of a thickener are utilized per part by weight of dispersant in the high-shear agitated mixture of water and dispersant.

Claim 17

The process of claim 2 wherein 1% to 4% by volume of tiny air bubbles is entrained in the high-shear agitated mixture of water and dispersant.

Claim 18

The process of claim 1 wherein the thixotropic thickener is a relatively high molecular weight polyacrylamide.

Claim 19

The process of claim 1 wherein the thickener is added to the high-shear agitated mixture of water and dispersant over a period of about 10 to 20 minutes.

Claim 20

The process of claim 2 wherein the thickener is added to the high-shear agitated mixture of water and dispersant 5 to 15 minutes after the fibers are added to the high-shear agitated mixture of water and dispersant.

Claim 21

The process of claim 2 wherein about 1% to 10% by volume of tiny air bubbles is entrained in the viscous dispersion.

Claim 22

The process of claim 20 wherein the nascent viscosity of the viscous dispersion is about 10 to 50 cps., at a shear rate of 30.5 sec. 31 1.

Claim 23

The process of claim 21 wherein the nascent viscosity of the viscous dispersion is about 15 to 30 cps., at a shear rate of 30.5 sec. -1 .

Claim 24

The process of claim 1 wherein the viscous dispersion is diluted in an eductor, the viscous dispersion being fed to the annulus ring of the eductor.

Claim 25

The process of claim 23 wherein the viscous dispersion is pumped to the eductor utilizing a helical progressive cavitation pump.

Claim 26

The process of claim 1 wherein the viscous dispersion is diluted with a viscous, diluting medium having about the same nascent viscosity as the nascent viscosity of the viscous dispersion.

Claim 27

The process of claim 25 wherein the viscous dispersion and the viscous, diluting medium are agitated with a non-stapling agitator.

Claim 28

The process of claim 25 wherein the viscous dispersion is subsequently diluted in an eductor, the viscous dispersion being fed to the annulus ring of the eductor.

Claim 29

The process of claim 27 wherein the viscous dispersion is pumped to the eductor utilizing a helical progressive cavitation pump.

Claim 30

The process of claim 27 wherein the viscous dispersion is diluted in the eductor with a white water having a nascent viscosity of about 5 to 30 cps., at a shear rate of 30.5 sec. -1 , and which contains about 1% to 10% by volume of entrained air.

Claim 31

The process of claim 29 wherein the white water has a nascent viscosity of 10 to 15 cps., at a shear rate of 30.5 sec. -1 .

Claim 32

The process of claim 29 wherein the white water contains about 2% to 4% by volume of entrained air.

Claim 33

The process of claim 29 wherein the viscous dispersion is diluted with 2 to 12 volumes of the white water.

Claim 34

The process of claim 29 wherein the viscous dispersion is subsequently diluted with 1 to 20 volumes of the white water to produce a dilute dispersion having a fiber consistency of about 0.001% to 0.1% by weight, a nascent viscosity of about 5 to 30 cps., at a shear rate of 30.5 sec. -1 , and an air entrainment of about 1% to 10% by volume.

Claim 35

The process of claim 33 wherein the dilute dispersion has a fiber consistency of 0.001% to 0.010% by weight.

Claim 36

The process of claim 33 wherein the dilute dispersion has a nascent viscosity of 10 to 15 cps., at a shear rate of 30.5 sec. -1 .

Claim 37

The process of claim 33 wherein the dilute dispersion has an air entrainment of about 2% to 4% by volume.

Claim 38

The process of claim 1 wherein the high-shear agitated mixture is agitated vigorously enough to create tumbling surface conditions with little or no vortex and without creating any substantial amount of surface foam.

Claim 39

A process for forming a non-woven fabric by wet-laying, on paper making equipment, staple length, synthetic fibers having a length to diameter ratio of about 400 to 3000, the fabric having a microvariation in basis weight of not more than about 10% and a macrovariation in basis weight of not more than about 5%, and the fabric being essentially free of knits, bundles and strings, comprising the steps of: adding about 0.1% to 3.0% by weight of a fiber furnish containing said fibers to a high-shear agitated mixture of water and at least 0.0001% by weight of a dispersant, to separate the fibers and to completely and uniformly distribute the individual fibers throughout the resulting, high-shear agitated mixture containing about 1% to 4% by volume of entrained air; the high-shear agitated mixture being agitated vigorously enough to create tumbling surface conditions with little or no vortex and without creating any substantial amount of surface foam; then, slowly adding a thixotropic thickener, over a period of about 10 minutes or longer, to the high-shear agitated mixture to form the viscous dispersion; the viscous dispersion containing about 1% to 50% by volume of entrained air and having a nascent viscosity of about 10 to 125 cps., when measured at a shear rate of 30.5 sec. -1 ; and individual fibers in the viscous dispersion being restrained from becoming entangled and from forming knits, bundles and strings; diluting the viscous dispersion with a viscous, diluting medium, having about the same nascent viscosity as the viscous dispersion to form a once-diluted, viscous dispersion; and diluting the once-diluted, viscous dispersion in an eductor with a white water; the once-diluted, viscous dispersion being pumped to the annulus ring of the eductor utilizing a helical progressive cavitation pump; and the white water having a nascent viscosity of 5 to 30 cps., at a shear rate of 30.5 sec. -1 , and containing about 1% to 10% by volume of entrained air.

Claim 40

A process for forming a non-woven fabric by wet-laying, on paper making equipment, staple length, synthetic fibers having a length to diameter ratio of about 400 to 3000, the fabric having a microvariation in basis weight of not more than about 10% and a macrovariation in basis weight of not more than about 5%, and the fabric being essentially free of knits, bundles and strings, comprising the steps of: adding about 0.1% to 3.0% by weight of a fiber furnish containing said fibers to a high-shear agitated mixture of water and at least 0.0001% by weight of a dispersant, to separate the fibers and to completely and uniformly distribute the individual fibers throughout the resulting, high-shear agitated mixture containing about 1% to 4% by volume of entrained air; the high-shear agitated mixture being agitated vigorously enough to create tumbling surface conditions with little or no vortex and without creating any substantial amount of surface foam; then, slowly adding a thixotropic thickener, over a period of about 10 minutes or longer, to the high-shear agitated mixture to form the viscous dispersion; the viscous dispersion containing about 1% to 50% by volume of entrained air and having a nascent viscosity of about 10 to 125 cps., when measured at a shear rate of 30.5 sec. -1 ; and individual fibers in the viscous dispersion being restrained from becoming entangled and from forming knits, bundles and strings; diluting the viscous dispersion with a viscous, diluting medium, having about the same nascent viscosity as the viscous dispersion to form a once-diluted, viscous dispersion; and diluting the once-diluted, viscous dispersion in an eductor with a white water; the once-diluted, viscous dispersion being pumped to the annulus ring of the eductor utilizing a helical progressive cavitation pump; and the white water having a nascent viscosity of 5 to 30 cps., at a shear rate of 30.5 sec. -1 , and containing about 1% to 10% by volume of entrained air.

Claim 41

The process of claim 38 wherein about 0.001% to 0.2% by weight of dispersant is utilized; and the viscous dispersion contains 1% to 10% by volume of entrained air and has a nascent viscosity of 10 to 50 cps., at a shear rate of 30.5 sec. -1 .

Claim 42

The process of claim 39 wherein the thixotropic thickener is added to the high-shear agitated mixture of water and dispersant over a period of about 10 to 20 minutes.

Claim 43

The process of claim 39 wherein the viscous dispersion has a nascent viscosity of 15 to 30 cps. and the white water has a nascent viscosity of 10 to 15 cps., at a shear rate of 30.5 sec. -1 .

Claim 44

The process of claim 41 wherein the viscous dispersion and the white water contain 2% to 4% by volume of entrained air.

Claim 45

The process of claim 39 wherein the viscous dispersion is diluted with about 2 to 5 volumes of the viscous, diluting medium; the once-diluted viscous dispersion is diluted with about 2 to 12 volumes of the white water in the eductor to form a twice-diluted, viscous dispersion; and the twice-diluted, viscous dispersion is diluted with 1 to 20 volumes of the white water to form a dilute dispersion having a fiber consistency of about 0.001% to 0.10% by weight, a nascent viscosity of about 5 to 30 cps., at a shear rate of 30.5 sec. -1 , and an air entrainment of about 1% to 10% by volume.

Claim 46

The process of claim 43 wherein the dilute dispersion has a fiber consistency of about 0.001% to 0.010%, a nascent viscosity of about 10 to 15 cps., at a shear rate of 30.5 sec. -1 , and an air entrainment of 2% to 4% by volume.