Abstract This invention is a method for forming a protective, strippable, elastomeric film on a highly reflective surface. The method is especially well suited for protecting diamond-machined metallic mirrors, which are susceptible not only to abrasion and mechanical damage but also to contamination and corrosion by various fluids. In a typical use of the invention, a diamond-machined copper mirror surface is coated uniformly with a solution comprising a completely polymerized and completely cured thermoplastic urethane elastomer dissolved in tetrahydrofuran. The applied coating is evaporated to dryness, forming a tough, adherent, impermeable, and transparent film which encapsulates dust and other particulates on the surface. The film may be left in place for many months. When desired, the film may be stripped intact, removing the entrapped particulates and leaving no residue on the mirror surface.
A method for forming on a diamond-machined metallic surface having a given reflectivity a dry, impermeable, transparent elastomeric film which can be formed on said surface and stripped intact therefrom without substantially altering said reflectivity, said method comprising: applying to said surface as a coating a liquid composition comprising (a) 5 to 11% by weight of a completely polymerized and completely cured thermoplastic urethane elastomer characterized by an elongation of at least 400%; (b) 72 to 95% by weight tetrahydrofuran; and (c) 0 to 17% by weight of an alcohol selected from the group consisting of methyl, ethyl, and isopropyl alcohols, and evaporating said coating or dryness.
Claim 2
Independent Claim
107 words
A method for forming on a diamond-machined metallic surface having a given reflectivity a dry, impermeable, transparent elastomeric film which can be formed on said surface and stripped intact therefrom without substantially altering said reflectivity, said method comprising: applying to said surface as a coating a liquid composition comprising (a) 5 to 11% by weight of a completely polymerized and completely cured thermoplastic urethane elastomer characterized by an elongation of at least 400%; (b) 72 to 95% by weight tetrahydrofuran; and (c) 0 to 17% by weight of an alcohol selected from the group consisting of methyl, ethyl, and isopropyl alcohols, and evaporating said coating or dryness.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein said elastomer is characterized by a tear strength in the range of from 450 to 750 lbs/linear-inch.
Claim 4
Dependent Claim
14 words
The method of claim 1 wherein said evaporating step is conducted at ambient temperature.
Claim 5
Dependent Claim
14 words
The method of claim 1 wherein said coating is prepared with substantially anhydrous elastomer.
Claim 6
Dependent Claim
11 words
The method of claim 1 wherein said alcohol is isopropyl alcohol.