Modified polycarbonates and a process for their preparation

Claim 2

A process for the modification of a thermoplastic aromatic polycarbonate prepared from (a) between about 0 and 95 mol % of diphenols of the general formula (I) ##STR5## (b) between about 5 and 100 mol % of diphenols of the general formula (II) ##STR6## (c) between about 1 and 5 mol % of monophenols of the general formula (III) ##STR7## the mol percentages being relative to the sum of the mols of diphenols I and II, wherein X denotes a single bond or a C 1 to C 8 alkylene, C 2 to C 8 alkylidene, C 5 to C 15 cycloalkylene, C 5 to C 15 cycloalkylidene, O, S, SO, SO 2 or ##STR8## R denotes a halogen atom or a primary alkyl, secondary alkyl or alkenyl radical, m 1 ,m 2 --0 or 1, n 1 and n 2 are 0, 1, 2, 3 or 4, and the sum of n 1 and n 2 must be at least 1 in each case, n is 1, 2, 3, 4 or 5 and D denotes a hydrogen or halogen atom or an alkyl or β,γ-unsaturated alkyl radical comprising irradiating the polycarbonates with UV light, after adding between about 1% and 5% by weight, relative to the weight of polycarbonate, of a photoinitiator.

Claim 3

The process according to claim 1, wherein between about 1% and 3% by weight of the photoinitiator is added to the polycarbonate.

Claim 4

The process according to claim 1, wherein between about 0.05% and 5% by weight, relative to the weight of polycarbonate, of a flameproofing agent is added prior to the irradiation.

Claim 5

The process according to claim 3, wherein between about 0.1% and 2% by weight of the flameproofing agent is added prior to irradiation.

Claim 6

The process according to claim 1, wherein R is a C 1 to C 18 primary alkyl radical, a C 3 to C 18 secondary alkyl radical or C 2 -C 18 alkenyl radical, m 1 and m 2 are 1, n 1 and n 2 are 1 or 2 and D is a hydrogen, chlorine or bromine atom or a C 1 to C 18 alkyl or C 3 to C 18 β,γ-unsaturated alkyl radical.

Claim 7

The process according to claim 5, wherein n 1 and n 2 are 2.

Claim 8

The process of claim 1, wherein the photoinitiator is added via solution and the polycarbonate is isolated as a film.

Claim 9

The process of claim 1, wherein the photoinitiator is added via compounding between about 280° and 330° C.

Claim 10

The process of claim 1, wherein the photoinitiator-containing polycarbonate is molded into sheets or other injection molded parts prior to irradiation.

Claim 11

A process for cross-linking thermoplastic aromatic polycarbonates prepared from (a) between about 0 and 95 mol % of diphenols of the general formula (I) ##STR9## (b) between about 5 and 100 mol % of diphenols of the general formula (II) ##STR10## (c) between about 1 and 5 mol % of the monophenols of the general formula (III) ##STR11## the mol percentages being relative to the sum of the mols of diphenols I and II, wherein X denotes a single bond or a C 1 to C 8 alkylene, C 2 to C 8 alkylidene, C 5 to C 15 cycloalkylene, C 5 to C 15 cycloalkylidene, O, S, SO, SO 2 or ##STR12## R denotes a halogen atom or a primary alkyl, secondary alkyl or alkenyl radical, m 1 ,m 2 --0 or 1, n 1 and n 2 are 0, 1, 2, 3, or 4, and the sum of n 1 and n 2 must be at least 1 in each case, n is 1, 2, 3, 4 or 5 and D denotes a hydrogen or halogen atom or an alkyl or β,γ-unsaturated alkyl radical comprising (a) molding the polycarbonate into sheets or other injection molded parts; (b) dipping or spraying said polycarbonate sheets or molded parts in or with solvent mixtures of photoinitiators characterized in that the solvents are inert toward said polycarbonate, (c) drying the polycarbonate sheet or molded parts, and (d) irradiating with UV light.

Claim 12

A process for cross-linking thermoplastic aromatic polycarbonates prepared from (a) between about 0 and 95 mol % of diphenols of the general formula (I) ##STR9## (b) between about 5 and 100 mol % of diphenols of the general formula (II) ##STR10## (c) between about 1 and 5 mol % of the monophenols of the general formula (III) ##STR11## the mol percentages being relative to the sum of the mols of diphenols I and II, wherein X denotes a single bond or a C 1 to C 8 alkylene, C 2 to C 8 alkylidene, C 5 to C 15 cycloalkylene, C 5 to C 15 cycloalkylidene, O, S, SO, SO 2 or ##STR12## R denotes a halogen atom or a primary alkyl, secondary alkyl or alkenyl radical, m 1 ,m 2 --0 or 1, n 1 and n 2 are 0, 1, 2, 3, or 4, and the sum of n 1 and n 2 must be at least 1 in each case, n is 1, 2, 3, 4 or 5 and D denotes a hydrogen or halogen atom or an alkyl or β,γ-unsaturated alkyl radical comprising (a) molding the polycarbonate into sheets or other injection molded parts; (b) dipping or spraying said polycarbonate sheets or molded parts in or with solvent mixtures of photoinitiators characterized in that the solvents are inert toward said polycarbonate, (c) drying the polycarbonate sheet or molded parts, and (d) irradiating with UV light.

Claim 13

Modified polycarbonates produced by the process of claim 1 and 10.

Claim 14

A process for the modification of a thermoplastic aromatic polycarbonate prepared from (a) between about 0 and 95 mol % of diphenols of the general formula (I) ##STR13## (b) between about 5 and 100 mol % of diphenols of the general formula (II) ##STR14## (c) between about 1 and 5 mol % of monophenols of the general formula (III) ##STR15## the mol percentages being relative to the sum of the mols of diphenols I and II, wherein X denotes a single bond or a C 1 to C 8 alkylene, C 2 to C 8 alkylidene, C 5 to C 15 cycloalkylene, C 5 to C 15 cycloalkylidene, O, S, SO, SO 2 or ##STR16## R denotes a primary alkyl, secondary alkyl or alkenyl radical, m 1 ,m 2 --0 or 1, n 1 and n 2 are 0, 1, 2, 3 or 4, and the sum of n 1 and n 2 must be at least 1 in each case, n is 1, 2, 3, 4 or 5 and D denotes a hydrogen or an alkyl or β,γ-unsaturated alkyl radical comprising irradiating the polycarbonates with UV light, after adding between about 1% and 5% by weight, relative to the weight of polycarbonate, of a photoinitiator.

Claim 15

A process for the modification of a thermoplastic aromatic polycarbonate prepared from (a) between about 0 and 95 mol % of diphenols of the general formula (I) ##STR13## (b) between about 5 and 100 mol % of diphenols of the general formula (II) ##STR14## (c) between about 1 and 5 mol % of monophenols of the general formula (III) ##STR15## the mol percentages being relative to the sum of the mols of diphenols I and II, wherein X denotes a single bond or a C 1 to C 8 alkylene, C 2 to C 8 alkylidene, C 5 to C 15 cycloalkylene, C 5 to C 15 cycloalkylidene, O, S, SO, SO 2 or ##STR16## R denotes a primary alkyl, secondary alkyl or alkenyl radical, m 1 ,m 2 --0 or 1, n 1 and n 2 are 0, 1, 2, 3 or 4, and the sum of n 1 and n 2 must be at least 1 in each case, n is 1, 2, 3, 4 or 5 and D denotes a hydrogen or an alkyl or β,γ-unsaturated alkyl radical comprising irradiating the polycarbonates with UV light, after adding between about 1% and 5% by weight, relative to the weight of polycarbonate, of a photoinitiator.